Activation parameters from nanoindentation repeated creep experiments: Spherical indenter vs cylindrical flat punch
Source abstract
Abstract
This study explores a repeated creep indentation approach to investigate the underlying deformation mechanisms in metals by extracting key deformation activation parameters. Using a thermally stable in-situ nanoindenter, repeated indentation creep tests were performed on nanocrystalline (nc) nickel (Ni), and the results were systematically compared with corresponding micropillar compression experiments. To explore the influence of tip geometry and material response, two distinct non-self-similar indenter geometries, spherical and cylindrical flat punch indenters, were used. The spherical indenter exhibited a linear decay in stress relaxation with increasing depth, while the flat punch showed minimal stress relaxation (∼10 MPa) on nc Ni. This behavior is reflected in the extracted activation parameters: for the spherical indenter, the activation volume increased linearly with representative indentation strain from 4.25 to 13.7 b 3 , whereas for the flat punch, it remained stable at 11.8 ± 1.5 b 3 . Due to obtaining consistent activation parameters with the cylindrical flat punch, it was further used to perform repeated indentation creep tests on single-crystal chromium (sx Cr) and single-crystal nickel (sx Ni). These tests demonstrated the reliability of the cylindrical flat punch geometry in capturing activation parameters across different material systems.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Microstructure and mechanical properties · Nanofabrication and Lithography Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (65)
Show source-provided references
1. Failure of metals II: fatigue10.1016/j.actamat.2015.05.050 ↗
2. Design for creep: a critical examination of some methods10.1016/j.engfailanal.2012.08.022 ↗
3. Indentation creep revisited10.1557/jmr.2011.213 ↗
4. On the measurement of power law creep parameters from instrumented indentation10.1007/s11837-017-2535-z ↗
5. An efficient way of extracting creep properties from short-time spherical indentation tests10.1557/jmr.2015.322 ↗
6. Nanoindentation creep of single-crystal tungsten and gallium arsenide10.1080/01418619708214217 ↗
7. Experimental and numerical study of the method to determine the creep parameters from the indentation creep testing10.1016/j.msea.2006.11.098 ↗
8. Local mechanical properties of the (β0+ω0) composite in multiphase titanium aluminides studied with nanoindentation at room and high temperatures10.1016/j.msea.2016.04.026 ↗
9. A robust method for mechanical characterization of heterogeneous materials by nanoindentation grid analysis10.1016/j.matdes.2020.108908 ↗
10. A critical appraisal of the extraction of creep parameters from nanoindentation data obtained at room temperature10.1016/j.actamat.2006.07.020 ↗
11. New flat-punch indentation creep testing approach for characterizing the local creep properties at high temperatures10.1016/j.matdes.2019.108090 ↗
12. A procedure for extracting primary and secondary creep parameters from nanoindentation data10.1016/j.mechmat.2013.05.014 ↗
13. A direct comparison of high temperature nanoindentation creep and uniaxial creep measurements for commercial purity aluminum10.1016/j.actamat.2016.03.032 ↗
14. An improved long-term nanoindentation creep testing approach for studying the local deformation processes in nanocrystalline metals at room and elevated temperatures10.1557/jmr.2013.39 ↗
15. Indentation creep vs. indentation relaxation: a matter of strain rate definition?10.1016/j.msea.2020.139246 ↗
16. Nanoindentation strain-rate jump tests for determining the local strain-rate sensitivity in nanocrystalline Ni and ultrafine-grained Al10.1557/jmr.2011.156 ↗
17. A new nanoindentation creep technique using constant contact pressure10.1557/jmr.2019.188 ↗
18. Nanoindentation creep testing: advantages and limitations of the constant contact pressure method10.1557/s43578-021-00445-6 ↗
19. Influence of solid solution strengthening on the local mechanical properties of single crystal and ultrafine-grained binary Cu–Al X solid solutions10.1557/jmr.2017.320 ↗
20. Characterization of thermally activated dislocation mechanisms using transient tests10.1016/S0921-5093(01)01124-8 ↗
21. Room temperature stress relaxation in nanocrystalline Ni measured by micropillar compression and miniature tension10.1557/jmr.2016.101 ↗
22. Displacement-controlled nanoindentation stress relaxation tests for reliable determination of activation volumes10.1016/j.matdes.2025.115067 ↗
23. The contribution of dislocation density and velocity to the strain rate and size effect using transient indentation methods and activation volume analysis10.1007/s11661-018-4817-7 ↗
24. An analytical model for the flat punch indentation size effect10.1016/j.ijsolstr.2019.05.004 ↗
25. A methodology for obtaining primary and secondary creep characteristics from indentation experiments, using a recess10.1016/j.ijmecsci.2020.105577 ↗
26. Essential refinements of spherical nanoindentation protocols for the reliable determination of mechanical flow curves10.1016/j.matdes.2018.03.003 ↗
27. Instrumented indentation apparatus having indenter punch with flat end surface and instrumented indentation method using the same, ([n.d.]).
28. A new long-term indentation relaxation method to measure creep properties at the micro-scale with application to fused silica and PMMA10.1016/j.mechmat.2019.103095 ↗
29. Indentation power-law creep of high-purity indium10.1007/s11661-999-0051-7 ↗
30. Indentation size effects in crystalline materials: a law for strain gradient plasticity10.1016/S0022-5096(97)00086-0 ↗
31. Sargent · 1992
32. Review of indentation size effect in crystalline materials: progress, challenges and opportunities10.1016/j.jmrt.2024.06.071 ↗
33. The correlation of indentation experiments10.1016/0022-5096(70)90029-3 ↗
34. On the constraint factor associated with the indentation of work-hardening materials with a spherical ball10.1007/BF02665003 ↗
35. 2007
36. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments10.1557/JMR.1992.1564 ↗
37. Analogy between creep cycles and stress relaxation series for activation volume measurement10.1016/0921-5093(94)09630-F ↗
38. J. Bonneville, B. Viguier, P. Sptitig, Repeated load transients for measuring the effective activation volume, (n.d.).
39. Comparison of in Situ micromechanical strain-rate sensitivity measurement techniques10.1007/s11837-015-1447-z ↗
40. Deformation and adiabatic heating of single crystalline and nanocrystalline Ni micropillars at high strain rates10.1016/j.eml.2025.102336 ↗
41. W.C. Oliver, G.M. Pharr, Measurement of hardness and elastic modulus by instrumented indentation: advances in understanding and refinements to methodology, (n.d.).
42. Experimental determination of the effective indenter shape and ε -factor for nanoindentation by continuously measuring the unloading stiffness10.1557/jmr.2011.245 ↗
43. 2008
44. Evaluation of micro-pillar compression tests for accurate determination of elastic-plastic constitutive relations10.1115/1.4006767 ↗
45. Elastic–plastic spherical indentation: deformation regimes, evolution of plasticity, and hardening effect10.1016/j.mechmat.2013.01.003 ↗
46. Finite element analysis of cylindrical indentation for determining plastic properties of materials in small volumes10.1088/0022-3727/41/11/115415 ↗
47. Temperature-dependent strain rate sensitivity and activation volume of nanocrystalline Ni10.1016/j.actamat.2006.02.013 ↗
48. Grain size dependence of the plastic deformation kinetics in Cu10.1016/S0921-5093(02)00238-1 ↗
49. On the grain size softening in nanocrystalline materials10.1016/S1359-6462(00)00320-1 ↗
50. Novel high temperature vacuum nanoindentation system with active surface referencing and non-contact heating for measurements up to 800 °C10.1063/1.5029873 ↗
51. Extraction of plasticity parameters from a single test using a spherical indenter and FEM modelling10.1016/j.mechmat.2016.11.014 ↗
52. Activation volume and density of Mobile dislocations in plastically deforming nanocrystalline Ni10.1063/1.1946899 ↗
53. The effect of grain size on strain rate sensitivity and activation volume – from nano to ufg nickel10.3139/146.101464 ↗
54. Strain rate effects in the ultrafine grain and nanocrystalline regimes—influence on some constitutive responses10.1007/s10853-006-0700-9 ↗
55. Dominating deformation mechanisms in ultrafine-grained chromium across length scales and temperatures10.1016/j.actamat.2017.08.043 ↗
56. Temperature-dependent nanoindentation and activation volume in high-purity body-centered cubic chromium10.1016/j.msea.2022.143629 ↗
57. Thermally activated dislocation plasticity in body-centered cubic chromium studied by high-temperature nanoindentation10.1016/j.actamat.2017.08.026 ↗
58. Ultra-strength materials10.1016/j.pmatsci.2010.04.001 ↗
59. Comparison of nanoindentation results obtained with Berkovich and cube-corner indenters10.1080/14786430600746424 ↗
60. Thermally activated deformation processes in body-centered cubic Cr – how microstructure influences strain-rate sensitivity10.1016/j.scriptamat.2015.05.001 ↗
61. Overview of the grain size effects on the mechanical and deformation behaviour of electrodeposited nanocrystalline nickel − from nanoindentation to high pressure torsion
62. Microstructure-dependent deformation behaviour of bcc-metals – indentation size effect and strain rate sensitivity10.1080/14786435.2014.982741 ↗
63. Indentation size effect in polycrystalline F.C.C. metals10.1016/S1359-6454(02)00175-1 ↗
64. In situ measurements of a homogeneous to heterogeneous transition in the plastic response of ion-irradiated ⟨1 1 1⟩ Ni microspecimens10.1016/j.actamat.2015.01.007 ↗
65. Micro‐indentation fracture from flat‐ended cylindrical indenter10.1111/j.1460-2695.2011.01611.x ↗