High-cycle fatigue behavior of T91 steel in air and high oxygen concentration lead-bismuth eutectic at 450 °C
Source abstract
Abstract
T91 steel is a promising structural material for lead-cooled fast reactors. However, its high-cycle fatigue (HCF) failure mechanisms in liquid lead–bismuth eutectic (LBE) remain poorly understood. This study investigates the HCF behavior of T91 at 450 °C in both air and high oxygen concentration LBE. The results reveal a strong dependence on the service environment. Notably, when the stress amplitude is below 320 MPa, the fatigue life in LBE is longer than that in air. In the high-stress regime, the surface oxide film undergoes rupture, delamination, and spallation, which promote crack nucleation and accelerate fatigue failure. In contrast, in the low-stress regime, the dense oxide film remains intact and exerts both barrier and constraint effects, thereby retarding crack initiation. As a result, T91 exhibits a fatigue life advantage in this regime. These findings highlight the protective role of the oxide scale under low-stress conditions and provide important data for evaluating the long-term service performance of T91 in LBE environments.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Nuclear reactor physics and engineering · Nuclear Materials and Properties · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (51)
Show source-provided references
1. Materials challenges in nuclear energy10.1016/j.actamat.2012.11.004 ↗
2. Structural materials challenges for advanced reactor systems10.1016/j.jnucmat.2008.11.026 ↗
3. Structural materials for Gen-IV nuclear reactors: challenges and opportunities10.1016/j.jnucmat.2008.08.044 ↗
4. Opportunities for the LWR ATF materials development program to contribute to the LBE-cooled ADS materials qualification program10.1016/j.jnucmat.2016.10.012 ↗
5. Mechanical properties of 9Cr martensitic steels and ODS-FeCr alloys after neutron irradiation at 325°C up to 42dpa10.1016/j.jnucmat.2007.03.166 ↗
6. Review of the studies on fundamental issues in LBE corrosion10.1016/j.jnucmat.2007.06.019 ↗
7. A review of steel corrosion by liquid lead and lead–bismuth10.1016/j.corsci.2009.03.013 ↗
8. An overview of corrosion issues for the design and operation of high-temperature lead-and lead-bismuth-cooled reactor systems10.13182/NT04-A3540 ↗
9. Review of liquid metal corrosion issues for potential containment materials for liquid lead and lead–bismuth eutectic spallation targets as a neutron source10.1016/S0029-5493(99)00303-9 ↗
10. Influence of liquid lead and lead–bismuth eutectic on tensile, fatigue and creep properties of ferritic/martensitic and austenitic steels for transmutation systems10.1016/j.jnucmat.2011.04.047 ↗
11. Liquid metal embrittlement10.1007/BF01028323 ↗
12. Corrosion scales on various steels after exposure to liquid lead–bismuth eutectic10.1016/j.jnucmat.2013.09.034 ↗
13. Corrosion behaviour of stainless steels in flowing LBE at low and high oxygen concentration10.1016/j.jnucmat.2004.07.011 ↗
14. Steel T91 subjected to static stress in lead-bismuth eutectic at 450–550 °C and low oxygen concentration10.1016/j.jnucmat.2018.09.056 ↗
15. Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 °C10.1016/j.corsci.2021.109324 ↗
16. Liquid lead–bismuth eutectic embrittlement effect on the tensile properties of T91 steel at 350° C10.1002/maco.202112530 ↗
17. Temperature dependence of liquid metal embrittlement susceptibility of a modified 9Cr–1Mo steel under low cycle fatigue in lead–bismuth eutectic at 160–450 °C10.1016/j.jnucmat.2015.06.021 ↗
18. Investigation of liquid LBE embrittlement effects on irradiated ferritic/martensitic steels by slow-strain-rate tensile tests10.1016/j.jnucmat.2011.11.036 ↗
19. Study on liquid metal embrittlement susceptibility of T91 exposed to liquid lead-bismuth eutectic10.3390/met15020206 ↗
20. A review of recent advances in the understanding of liquid metal embrittlement10.5006/2904 ↗
21. Stability of fatigue cracks at 350 °C in air and in liquid metal in T91 martensitic steel10.1016/j.ijfatigue.2019.105265 ↗
22. The role of oxide films in preventing liquid metal embrittlement of T91 steel exposed to liquid lead-bismuth eutectic10.1016/j.jnucmat.2018.07.018 ↗
23. Low cycle fatigue behavior of a modified 9Cr–1Mo ferritic–martensitic steel in lead–bismuth eutectic at 350°C – effects of oxygen concentration in the liquid metal and strain rate10.1016/j.corsci.2015.02.022 ↗
24. Liquid metal embrittlement of the T91 steel in lead bismuth eutectic: the role of loading rate and of the oxygen content in the liquid metal10.1016/j.msea.2014.04.082 ↗
25. Investigating liquid-metal embrittlement of T91 steel by fracture toughness tests10.1016/j.jnucmat.2015.12.019 ↗
26. Temperature effect in the maximum propagation rate of a liquid metal filled crack: the T91 martensitic steel/Lead–Bismuth Eutectic system10.1016/j.corsci.2009.06.049 ↗
27. Low-cyclic fatigue behavior of modified 9Cr–1Mo steel at elevated temperature10.1016/j.msea.2014.02.076 ↗
28. Low-cycle fatigue life prediction of modified 9Cr-1Mo ferritic-martensitic steel in liquid lead–bismuth eutectic environments using a physically-based model10.1016/j.engfracmech.2025.111434 ↗
29. New insight into fatigue life of modified 9Cr-1Mo steel in liquid lead–bismuth environment and life prediction considering environmental factors10.1016/j.nucengdes.2024.113648 ↗
30. Enhanced cyclic stress response and low-cycle fatigue life of modified 9Cr-1Mo steel by wire-arc additive manufacturing and post-heat treatment10.1016/j.ijfatigue.2024.108333 ↗
31. Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150–550 °C10.1016/j.ijfatigue.2022.107344 ↗
32. Low cycle fatigue behavior of T91 ferritic-martensitic steel hollow specimen in oxygen saturated lead–bismuth eutectic at 200 ∼ 450 °C10.1016/j.nucengdes.2025.114185 ↗
33. Study of lead–bismuth eutectic on material performance degradation and life assessment for modified 9Cr-1Mo steel under low cycle fatigue at high temperatures10.1016/j.ijfatigue.2023.107828 ↗
34. Cyclic slip irreversibilities and the evolution of fatigue damage10.1007/s11663-009-9240-4 ↗
35. Corrosion behavior of T91 steel in liquid lead-bismuth eutectic at 550 °C: effects of exposure time and dissolved oxygen concentration10.1016/j.corsci.2022.110405 ↗
36. Effect of long-term thermal aging on lead-bismuth eutectic corrosion behavior of 9Cr ferritic/martensitic steel10.1016/j.jmst.2024.05.049 ↗
37. Insights into the fatigue damage mechanism of T91 steel in liquid lead-bismuth eutectic at 150–550 °C10.1016/j.corsci.2024.112007 ↗
38. Tensile and very high cycle fatigue behaviors of a compressor blade titanium alloy at room and high temperatures10.1016/j.msea.2021.141049 ↗
39. Fast prediction of the flow induced vibration of wire-wrapped fuel rod in a lead-bismuth reactor based on improved DMD and LSTM network10.1016/j.net.2025.103780 ↗
40. Numerical modeling of flow induced vibration of nuclear fuel rods10.1016/j.nucengdes.2017.05.013 ↗
41. Study of flow-induced vibrations of spiral tube bundles under nonlinear support in lead-bismuth eutectic environment based on large eddy simulation10.1016/j.nucengdes.2025.114094 ↗
42. Effect of strain rate on low cycle fatigue behavior of T91 steel hollow specimen filled with liquid lead–bismuth eutectic at 350 °C10.1016/j.engfailanal.2025.110311 ↗
43. Strain-rate dependent fatigue behavior of T91 steel at 550 °C of liquid lead-bismuth eutectic10.1016/j.corsci.2024.112433 ↗
44. Stress corrosion cracking behavior of T91 steel in low oxygen concentration liquid lead-bismuth eutectic at 450°C10.1016/j.corsci.2025.112927 ↗
45. Local mechanical properties of corrosion layers formed on T91 and SS316L steels after exposure to static liquid LBE at 500 °C for 1000 h obtained by nano-indentation10.1016/j.net.2024.03.005 ↗
46. Liquid lead-bismuth eutectic enhanced intrusion/extrusion formation and early crack initiation in T91 steel under low-cycle fatigue10.1016/j.corsci.2025.113286 ↗
47. Behaviour of pre-stressed T91 and ODS steels exposed to liquid lead-bismuth eutectic10.1016/j.corsci.2017.12.005 ↗
48. Enhanced toughness and ductility of T91 steel after exposure to liquid LBE saturated by oxygen at 350–500 °C10.1016/j.jmrt.2024.04.230 ↗
49. Influence of oxide scale on the wettability of LBE on T91 steel10.1016/j.fusengdes.2017.03.089 ↗
50. Fatigue-induced oxidation assisting microcrack nucleation in Mg-RE alloy under ultrasonic fatigue10.1016/j.scriptamat.2023.115643 ↗
51. Fatigue crack tip corrosion processes and oxide induced closure10.1016/j.msea.2022.144383 ↗