Superior oxidation behaviors of stable nano-grain-sized coating layers produced via sequential two-step pack cementation coatings by B and Si of TiTaNbMoZr high-entropy alloys
Source abstract
Abstract
In this study, Si-pack cementation coating and sequential B-Si-pack cementation coating were applied to TiTaNbMoZr alloy to investigate the resulting microstructural changes and oxidation resistance. The as-cast alloy underwent severe oxidation at 1300 °C, and the Si-pack cementation-coated alloy also exhibited crack formation due to the oxidation of Zr-rich XSi 2 to ZrO 2 within the XSi 2 layer, resulting in compromised coating integrity. In contrast, the B-Si-pack cementation-coated alloy formed a surface layer composed of XB 2 , XSi 2 , and X 5 SiB 2 , which remained structurally stable during oxidation and consequently exhibited enhanced oxidation resistance. The as-cast alloy and the Si-pack cementation-coated alloy exhibited substantial mass gains of 62.8 mg cm -2 and 55.6 mg cm -2 , respectively, after oxidation at 1300 °C for 10 h. Conversely, the B-Si-pack cementation-coated alloy demonstrated markedly lower mass gain, recording only 4.7 mg cm -2 under identical conditions. Even after 20 h of oxidation, the mass gain remained low at 9.85 mg cm -2 . Furthermore, once the initial protective oxide layer formed, the parabolic rate constant was determined to be as low as 1.47 mg cm -2 h -1/2 . These results confirm the potential of high-entropy alloys (HEAs) for use in high-temperature environments and emphasize the critical role of selecting suitable coating strategies tailored to the alloy composition.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (60)
Show source-provided references
1. A. Behera. Failure analysis and materials development of gas turbine blades10.1016/j.matpr.2020.02.859 ↗
2. A critical review on gas turbine cooling performance and failure analysis of turbine blades10.1016/j.ijft.2023.100329 ↗
3. Common failures in gas turbine blades10.1016/j.engfailanal.2004.07.004 ↗
4. Effect of chemical composition on particle morphology of topologically close-packed precipitates in a Ni-based single crystal superalloy
5. Alloys-by-design: application to nickel-based single crystal superalloys10.1016/j.actamat.2009.08.018 ↗
6. High temperature creep property of a novel porous double layer cooling structure for gas turbine blades10.1016/j.engfracmech.2023.109440 ↗
7. Impact of thermal radiation on turbine blades with film cooling structures10.1016/j.applthermaleng.2022.119832 ↗
8. Renew, increasing the efficiency of vertical-axis turbines through improved blade support structures10.1016/j.renene.2021.01.092 ↗
9. Effects of upgraded cooling system and new blade materials on a real gas turbine performance10.1016/j.egypro.2016.11.154 ↗
10. A review on high-Temperature Applicability: a milestone for high entropy alloys
11. Effects of boron content on microstructure and mechanical properties of AlFeCoNiBx high entropy alloy prepared by vacuum arc melting10.1016/j.vacuum.2019.03.019 ↗
12. Multicomponent intermetallic nanoparticles and superb mechanical behaviors of complex alloys10.1126/science.aas8815 ↗
13. The corrosion behaviour of CoCrFeNi-x (x = Cu, Al, Sn) high entropy alloy systems in chloride solution10.1016/j.corsci.2020.108740 ↗
14. Microstructure and corrosion behavior of the Ti-V-Cr-Nb high-entropy alloys in 3.5 wt% NaCl solution10.1016/j.corsci.2023.111149 ↗
15. High temperature wear behavior of refractory high entropy alloys based on 4-5-6 elemental palette10.1016/j.jallcom.2020.156004 ↗
16. Effect of Ti on the wear behavior of AlCoCrFeNi high-entropy alloy during unidirectional and bi-directional sliding wear processes10.1016/j.wear.2021.203650 ↗
17. High temperature oxidation behaviour of non-equimolar AlCoCrFeNi high entropy alloys10.1016/j.vacuum.2020.109969 ↗
18. Influence of Al content on high temperature oxidation behavior of AlxCoCrFeNiTi0.5 high entropy alloys10.1016/j.vacuum.2019.01.053 ↗
19. High-entropy alloys10.1038/s41578-019-0121-4 ↗
20. Microstructure and wear behavior of AlCrTiNbMo high-entropy alloy coating prepared by electron beam cladding on Ti600 substrate
21. A critical review of high entropy alloys and related concepts10.1016/j.actamat.2016.08.081 ↗
22. Refractory high-entropy alloys10.1016/j.intermet.2010.05.014 ↗
23. Mechanical properties of Nb25Mo25Ta25W25 and V20Nb20Mo20Ta20W20 refractory high entropy alloys10.1016/j.intermet.2011.01.004 ↗
24. Microstructure and elevated temperature properties of a refractory TaNbHfZrTi alloy10.1007/s10853-012-6260-2 ↗
25. A refractory Hf25Nb25Ti25Zr25 high-entropy alloy with excellent structural stability and tensile properties10.1016/j.matlet.2014.05.134 ↗
26. Enhanced mechanical properties of HfMoTaTiZr and HfMoNbTaTiZr refractory high-entropy alloys10.1016/j.intermet.2015.03.013 ↗
27. Elastic and plastic properties of as-cast equimolar TiHfZrTaNb high-entropy alloy10.1016/j.msea.2015.12.017 ↗
28. Study on high-temperature oxidation of TiZrHfNbTaV high-entropy alloy10.1016/j.matlet.2024.135907 ↗
29. Effect of Ni-Coated-Al2O3 addition on slurry erosion behavior of AlCoCrFeNi high-entropy alloy coatings prepared by laser cladding spray
30. Sliding wear behavior of high entropy alloy coatings deposited through cold spraying and flame spraying: a comparative assessment
31. Effect of tungsten and vanadium additions on the dry abrasive wear and solid particle erosion of flame-sprayed AlCoCrFeMo high entropy alloy coatings10.1016/j.ijrmhm.2023.106245 ↗
32. A novel Zr-Y modified silicide coating on Nb-Si based alloys as protection against oxidation and hot corrosion10.1016/j.corsci.2020.108948 ↗
33. Effect of high Fe content on the microstructure, mechanical and corrosion properties of AlCoCrFeNi high-entropy alloy coatings prepared by gas tungsten arc cladding10.1016/j.surfcoat.2021.127242 ↗
34. Thermal stability and degradation properties of aluminide coated and uncoated Ti-6Al-4V alloys exposed to high temperature flame10.1007/s12540-022-01359-6 ↗
35. Oxidation behaviour of a MoSiBTiC alloy coated by a (Si+B) co-deposition pack cementation method10.1016/j.corsci.2023.110990 ↗
36. Microstructures and high temperature oxidation behaviors of AlMo0.5NbTa0.5TiZr high entropy alloys coated by silicon pack cementation10.1016/j.corsci.2023.111203 ↗
37. R. Su, J. R. Becker, L. Liu, H. Zhang, X. Hu, J. H. Perepezko, Phase stability during high-temperature oxidation. JOM 20203;75(11):4636–4643. https://doi.org/10.1007/s11837-023-06080-2.10.1007/s11837-023-06080-2 ↗
38. Formation mechanism and oxidation performance for a novel Mo(Si,Al)2 coating prepared using a modified pack cementation strategy10.1016/j.surfcoat.2024.131574 ↗
39. Structural stability and thermal expansion of TiTaNbMoZr refractory high entropy alloy10.1016/j.jallcom.2021.162154 ↗
40. TiZrNbTaMo high-entropy alloy designed for orthopedic implants: As-cast microstructure and mechanical properties10.1016/j.msec.2016.12.057 ↗
41. Effect of Mo on the high temperature oxidation behavior of Al19Fe20-xCo20-xNi41Mo2x high entropy alloys10.1016/j.intermet.2023.107845 ↗
42. Hasegawa · 2014
43. Growth kinetics and isothermal oxidation behavior of a Si pack cementation coated Mo-Si-B alloy10.1016/j.apsusc.2019.06.020 ↗
44. Oxidation behavior of pack-cemented Mo-W-Si-B coatings at 1200 and 1650 ◦C10.1016/j.surfcoat.2022.129158 ↗
45. Observation of yttrium oxide segregation in a ZrO2-SiO2 glass-ceramic at nanometer dimensions10.1111/jace.17142 ↗
46. Chemical regulation in the bonding reconstruction stage of amorphous Zr-Si oxidation and the resultant phase selection10.1016/j.matdes.2023.112291 ↗
47. Examination of thin films in the ZrO2-SiO2 system by transmission electron microscopy and x-ray diffraction techniques
48. Thermodynamic properties of zirconium-oxygen solid solution and its deoxidation in calcium chloride molten salt10.1016/j.jallcom.2019.151964 ↗
49. Paul, J. Kishor, S. Majumdar, V. Kain. Studies on growth mechanism of intermediate layer of (Mo,W)5Si3 and interdiffusion in the (Mo,W)-(Mo,W)Si2 system prepared by pack cementation coating.
50. Aluminide and silicide diffusion coatings by pack cementation for nb-ti-al alloy10.1016/j.surfcoat.2020.125675 ↗
51. Formation of silicide layers on a Ti-46Al-8Ta alloy in pack cementation and diffusion couple experiments
52. Formation and oxidation behavior of refractory high-entropy silicide (NbMoTaW)Si2 coating10.1016/j.corsci.2022.110134 ↗
53. Co-deposition of Si and B to form oxidation-resistant coatings on an Nb–Ti–Si based ultrahigh temperature alloy by pack cementation technique10.1016/j.corsci.2015.01.013 ↗
54. Oxidation behaviour of a Ge-modified silicide coating on an Nb-Si based alloy in the moderate temperature range
55. Effect of Al content on microstructure and oxidation behavior of Si-Al co-deposition coatings on MoSiBTiC alloy10.1016/j.corsci.2024.112668 ↗
56. Microstructure and oxidation behaviour of MoSi2 coating combined MoB diffusion barrier layer on Mo substrate at 1300 ◦C10.1016/j.ceramint.2020.12.162 ↗
57. Oxidation and thermal stress analysis of silicide-coated Nb30Mo30Ti20Co20 high entropy alloys under high-temperature flame
58. The Formation and oxidation resistance of boron-modified and germanium-doped Silicide diffusion coatings for titanium and molybdenum10.4028/www.scientific.net/MSF.251-254.723 ↗
59. A crucial review on recent updates of oxidation behavior in high entropy alloys10.1007/s42452-021-04374-1 ↗
60. Y and Al modified silicide coatings on an nb–ti–si based ultrahigh temperature alloy prepared by pack cementation process10.1016/j.surfcoat.2011.07.056 ↗