Surface nanoprecipitation induced by severe plastic deformation in the Fe49.3Co23Ni23C0.85Mn1Si2.85 biphasic multicomponent alloy

Precipitation strengthening plays a vital role in enhancing the mechanical properties of metallic materials, typically achieved through heat treatment. However, deformation-induced precipitation (DIP) in multicomponent alloys (MAs) without the assistance of annealing is rarely reported, owing to their inherent high entropy and sluggish diffusion effects. This work reveals the significant formation of nanoscale and microscale precipitates in the dual-phase Fe 49.3 Co 23 Ni 23 C 0.85 Mn 1 Si 2.85 MA triggered by surface severe plastic deformation (SSPD) through industrial shot blasting. The SSPD process leads to the formation of ultrafine gradient structures comprising nanocrystalline and submicron-crystalline zones. Submicron SiO 2 precipitates emerge at the interfaces of both these zones, while various Mn 5 Si 3 and Si nanoparticles precipitate within the nanocrystalline zone. This phenomenon can be ascribed to the high density of generated substructures, the accelerated diffusion of atoms, and the reduction in solid solubility limits in the SPD-driven non-equilibrium state.