Synergistic role of Bi, Ni, and Pd alloying in SAC305 for enhanced IMC suppression and superior thermo-mechanical performance
Source abstract
Abstract
ABSTRACT In this study, the effect of dopants on solder joint reliability was investigated by examining the mechanical behavior of solder joints with respect to solder composition; standard Sn-3.0Ag-0.5Cu (SAC305) solder and SAC alloy with bismuth (Bi), nickel (Ni), and palladium (Pd) (SAC-BNP). To analyze the creep behavior, bulk type solders specimens are fabricated, and creep tests are conducted under three temperatures (25, 75, 125 °C) and three stress levels (5, 10, 15 MPa). The intermetallic compounds (IMCs) growth and shear strength on the PCB of both solder types are studied during thermal aging. Also, the thermo-mechanical fatigue reliability is tested and compared by thermal shock tests ranging from 0°C to 125°C with ball grid array (BGA) assemblies. The results show that SAC-BNP exhibit superior creep resistance, suppression of IMC growth, and about 40% higher shear strength compared to SAC305. In thermal cycling, SAC-BNP demonstrate approximately 65.8% longer fatigue life, withstanding 2306 cycles before failure, compared to 1390 cycles for SAC305. These findings suggest that incorporating Bi, Ni, and Pd into SAC alloys significantly improves the reliability of solder joints under thermal and mechanical stress conditions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electronic Packaging and Soldering Technologies · 3D IC and TSV technologies · Copper Interconnects and Reliability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (34)
Show source-provided references
1. Characterizing the mechanical properties of actual SAC105, SAC305, and SAC405 solder joints by digital image correlation10.1007/s11664-011-1534-z ↗
2. The great SAC debate: comparing the reliability of SAC305 and SAC405 solders in a variety of applications
3. Wetting of Ni-based amorphous and crystalline alloys by Sn and Sn-based solders10.1016/j.microrel.2020.113722 ↗
4. A study on wettability and formation of intermetallic phase between Co–Cr–Mo alloy and Sn-Solder used as a potential under bump metallization for flip-chip packages10.1016/j.intermet.2020.106875 ↗
5. Comparative study on the hourglass-like joint of electroplated Sn-base solder reinforced by adding Ag3Sn nanoparticles and Ag micro-alloying elements10.1016/j.mtla.2019.100558 ↗
6. Analysis of microstructure and mechanical properties of bismuth-doped SAC305 lead-free solder alloy at high temperature10.3390/met11071077 ↗
7. Effect of bismuth addition on the corrosion dynamics of Sn–3Ag–0.5 Cu solder alloy in Hydrochloric Acid Solution10.46460/ijiea.911862 ↗
8. Pb-free solder: SAC105 vs SAC305 drop-test reliability data comparison
9. Influence of bismuth on microstructure, thermal properties, mechanical performance, and interfacial behavior of SAC305-xBi/Cu solder joints10.1016/S1003-6326(21)65585-1 ↗
10. Maalekian · 2015
11. Effects of bismuth additions on mechanical property and microstructure of SAC-Bi solder joint under current stressing10.1016/j.microrel.2021.114041 ↗
12. Alloying effect of Ni, Co, and Sb in SAC solder for improved drop performance of chip scale packages with Cu OSP pad finish
13. Effect of Ni, Bi concentration on the microstructure and shear behavior of low-Ag SAC–Bi–Ni/Cu solder joints10.1007/s10854-014-1921-3 ↗
14. Shear fatigue analysis of SAC-Bi solder joint exposed to varying stress cycling conditions10.1109/TCPMT.2023.3240367 ↗
15. Microstructures, mechanical properties and reliability induced from size effect in Sn-based solder joints10.1016/j.jmrt.2025.02.169 ↗
16. An overview of surface finishes and their role in printed circuit board solderability and solder joint performance10.1108/03056129910244518 ↗
17. The effect of PCB surface finish on lead‐free solder joints10.1108/09540910510579203 ↗
18. Packaging reliability effect of ENIG and ENEPIG surface finishes in board level thermal test under long-term aging and cycling10.3390/ma10050451 ↗
19. Comparative study of ENIG and ENEPIG as surface finishes for a Sn-Ag-Cu solder joint10.1007/s11664-011-1686-x ↗
20. Comparative study between the Sn–Ag–Cu/ENIG and Sn–Ag–Cu/ENEPIG solder joints under extreme temperature thermal shock10.1007/s10854-021-05395-7 ↗
21. Investigation of isothermal aged Sn-3Ag-0.5 Cu/Sn58Bi-Co hybrid solder joints on ENIG and ENEPIG substrate with various mechanical performances
22. Influence of Sn grain size and orientation on the thermomechanical response and reliability of Pb-free solder joints10.1109/TCAPT.2008.916835 ↗
23. The mechanics of the solder ball shear test and the effect of shear rate10.1016/j.msea.2005.10.064 ↗
24. Reflow sensitivity classification for nonhermetic solid state surface mount devices
25. Thermal cycling test method for fatigue life caracterization of surface mount attachments
26. Guidelines for accelerated testing of surface mount solder attachments
27. The effect of cooling rate on grain orientation and misorientation microstructure of SAC105 solder joints before and after impact drop tests10.1007/s11664-014-3176-4 ↗
28. Preparation of SAC305 solder specimens that mimic the microstructures of a micro solder ball
29. Thermal aging study of encapsulated power devices under autonomous driving condition and its effect on board level reliability
30. Effect of shear speed on the ball shear strength of Sn–3Ag–0.5 Cu solder ball joints10.5104/jiepeng.1.9 ↗
31. The role of Pd in Sn-Ag-Cu solder interconnect mechanical shock performance10.1007/s11664-012-2340-y ↗
32. Vasquez, A.A., et al., Comparative study for solder joint performance under shock for ENIG and ENEPIG surface plated tester PCBs.
33. The doped Pd on the crystal calculation and intermetallic property of low-temperature soldered ENEPIG substrates10.1016/j.jmrt.2023.11.126 ↗
34. Cost-benefit analysis of ENIG vs. HASL vs. OSP for class 3 PCBs