Selective Modification of the Tribological Properties of Aluminum Through Temperature and Dose Control in Oxygen Plasma Source Ion Implantation

M. Bolduc, B. Terreault, A. Reguer, E. Shaffer, R.G. St-Jacques

Journal of Materials Research· Volume 18· Issue 12
Publisher page

Abstract

Improvements in the tribological properties of pure aluminum and “aeronautical” alloy AA7075-T651 were obtained by oxygen-ion implantation [(0.7 to 5) × 1017 O/cm2, 30 keV] using our pulsed electron cyclotron resonance plasma source. This oxygen plasma source ion implantation process produced oxide nanoprecipitates that enhanced the hardness up to three times in the surface layer and caused reductions in the scratch depths and the friction coefficients by similar factors. A spectrum of tribological properties was obtained depending on temperature and ion dose. Temperature measurement and control were obtained through an integrated thermocouple and by changing the duty-cycle of the microwave source. The oxygen content and the depth-resolved chemical composition were measured and optimized using x-ray photoelectron spectroscopy (XPS) combined with Ar-ion etching. The tribological properties were investigated by (i) depth-sensing nanoindentation for hardness and Young's modulus, (ii) scratching and scratch-depth measurement via atomic force microscopy (AFM), and (iii) friction force measurements using AFM. Low-temperature (≤160°C) implantations with optimal O-ion doses produced, in both pure and alloyed Al, an approximately 50-nm-thick, smooth, and extremely fine-grained metal–alumina nanocomposite. The resulting surface was hard and stiff but nonbrittle and displayed high scratch resistance and low friction. High-temperature (~430°C) implantation had different effects on pure Al and AA7075. On pure Al, it produced a very hard but brittle Al2O3 layer for which yield points (displacement excursions) were observed at critical load values in the nanoindentation force–displacement curves. On AA7075, XPS chemical profiling revealed an effect of extreme Mg surface segregation and complete Al surface depletion; MgO crystallites formed a rather rough but surprisingly thick layer (>100 nm). The resulting AA7075 surface showed a hardness increase that was substantial but slightly smaller than that obtained at low temperature.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Metal and Thin Film Mechanics · Aluminum Alloys Composites Properties · Advanced ceramic materials synthesis

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (42)

Show source-provided references
1. 10.1063/1.37162010.1063/1.371620 ↗
2. Corcoran · 1997 · 436 · 159
3. 1961 · 1 · 917
4. 19. Biersack J.P. and Ziegler J.F. , STRIM-2000 .
5. 10.1063/1.33905510.1063/1.339055 ↗
6. 16. Bolduc M. , Terreault B. , and Shaffer E. , presented at PBII2003 (submitted to Surf. Coat. Technol., 2003).
7. 10.1016/0025-5416(87)90205-910.1016/0025-5416(87)90205-9 ↗
8. Bolduc · Nucl. Instrum. Methods B · 2001 · 175 · 452
9. 10.1016/0168-583X(95)00814-410.1016/0168-583X(95)00814-4 ↗
10. 10.1016/0168-583X(90)90640-G10.1016/0168-583X(90)90640-G ↗
11. 10.1016/S0924-4247(02)00393-X10.1016/S0924-4247(02)00393-X ↗
12. 10.1098/rspa.1970.013310.1098/rspa.1970.0133 ↗
13. 10.1063/1.154443210.1063/1.1544432 ↗
14. 10.1017/CBO978113917173110.1017/CBO9781139171731 ↗
15. 10.1103/PhysRevB.13.436410.1103/PhysRevB.13.4364 ↗
16. 10.1557/JMR.1998.005510.1557/JMR.1998.0055 ↗
17. 10.1116/1.58171710.1116/1.581717 ↗
18. 1998
19. 10.1016/S0257-8972(02)00122-610.1016/S0257-8972(02)00122-6 ↗
20. Orowan · 1948 · 451
21. 10.1002/(SICI)1096-9918(199709)25:10<809::AID-SIA304>3.0.CO;2-M10.1002/(SICI)1096-9918(199709)25:10<809::AID-SIA304>3.0.CO;2-M ↗
22. 10.1016/S1359-6454(99)00270-010.1016/S1359-6454(99)00270-0 ↗
23. 10.1016/0022-3115(78)90429-410.1016/0022-3115(78)90429-4 ↗
24. Saied · J. Phys.: Condens. Matter · 1993 · 5 · A165
25. Brandes · 1983
26. 10.1098/rspa.1956.011310.1098/rspa.1956.0113 ↗
27. 10.1557/JMR.2001.020710.1557/JMR.2001.0207 ↗
28. 10.1557/JMR.1992.156410.1557/JMR.1992.1564 ↗
29. Tabor · 1951
30. 10.1016/0956-7151(94)00351-H10.1016/0956-7151(94)00351-H ↗
31. 10.1115/1.292724010.1115/1.2927240 ↗
32. 10.1007/BF0267041810.1007/BF02670418 ↗
33. 10.1016/0168-583X(88)90182-610.1016/0168-583X(88)90182-6 ↗
34. 10.1557/JMR.2001.036210.1557/JMR.2001.0362 ↗
35. 10.1016/S1359-6454(98)00024-X10.1016/S1359-6454(98)00024-X ↗
36. 10.1557/JMR.1992.045010.1557/JMR.1992.0450 ↗
37. 10.1016/S1359-6454(98)00301-210.1016/S1359-6454(98)00301-2 ↗
38. Weiss · Phys. Status Solidi A · 1992 · 129 · 16710.1002/pssa.2211290115 ↗
39. 10.1002/(SICI)1527-2648(200005)2:5<247::AID-ADEM247>3.0.CO;2-U10.1002/(SICI)1527-2648(200005)2:5<247::AID-ADEM247>3.0.CO;2-U ↗
40. 10.1016/S0257-8972(02)00903-910.1016/S0257-8972(02)00903-9 ↗
41. 10.1016/S0257-8972(00)01149-X10.1016/S0257-8972(00)01149-X ↗
42. 10.1179/mst.1997.13.10.85910.1179/mst.1997.13.10.859 ↗