Fabrication and compressive strength of macrochannelled tetragonal zirconia polycrystals with calcium phosphate coating layer

Macrochannelled tetragonal zirconia polycrystals (TZP) coated with a calcium phosphate layer were fabricated using a coextrusion process to produce strong and bioactive porous bioceramics. The initial feedrod, composed of three materials [TZP (shell), calcium phosphate (intermediate layer), and carbon black (core)], was coextruded through a 750-μm orifice at 120 °C, producing a continuous and flexible filament. Each sheet, which was composed of a unidirectional array of filaments, was stacked and then warm-pressed at 140 °C with 10 MPa. After binder burnout, the green billet was sintered between 1350 and 1600 °C for 1 h in air, leaving uniform macrochannels clad on the inside with bioactive calcium phosphate on a strong TZP body. The compressive strength of the specimen was much higher than that of calcium phosphate with a similar structure.