Crystallization kinetics of amorphous Ga–Sb–Te films: Part II. Isothermal studies by a time-resolved optical transmission method

Isothermal crystallization kinetics of amorphous Ga–Sb–Te films was studied by means of a time-resolved optical transmission method. Thin films with compositions along the pseudo-binary tie-lines Sb₇Te₃–GaSb and Sb₂Te₃–GaSb in the ternary phase diagram were prepared by the co-sputtering method. Crystallization of GaSbTe films reveals a two-stage process: an initial surface nucleation and coarsening (Stage 1) followed by the one-dimensional grain growth (Stage 2). The kinetic exponent (n) value in Stage 1 shows strong dependence on film compositions, while that of Stage 2 is less dependent. The activation energy in Stage 1 increases with increasing GaSb content and reaches the maximum values at compositions close to GaSb, but a decreasing trend was observed in Stage 2. Kinetics parameters between isothermal crystallization of thin films and non-isothermal crystallization of powder samples analyzed by differential scanning colorimetry [J. Mater. Res. 19, 2929 (2004)] are compared. The kinetic parameters in Stage 1 show much correspondence with those of non-isothermal cases in comparable kinetic exponents but with lower activation energies. The discrepancies between nonisothermal and isothermal kinetics are attributed to the sample morphology and the constraint effects.