Time-dependent deformation behavior of freestanding and SiN_x-supported gold thin films investigated by bulge tests

A novel strain-rate jump method was developed for the plane-strain bulge test and used to investigate the time-dependent deformation behavior of gold thin films in the thickness range 100–400 nm. The experimental method is based on an abrupt variation of the pressurization rate. The evaluated strain-rate sensitivity was found to be five times higher for films in freestanding condition (m= 0.094) than for films tested on a SiNxsubstrate (m= 0.020). Bulge creep tests confirmed this increased time-dependence. The observation of the surface of the freestanding films after the creep tests provided evidence of apparent grain boundary sliding taking place next to intragranular plastic deformation. The out-of-plane deformation was presumably favored by the columnar microstructure of the samples, with grains extending between both free surfaces. In the case of SiNx-supported films, grain boundary sliding was prevented by the good adhesion of gold to the SiNxsubstrate.