Magnetic field–dependent microstructure evolution and magnetic property of Fe–6.5 Si–0.05 B alloy during solidification

Chunmei Liu, Yunbo Zhong, Zhe Shen, Licheng Dong, Tianxiang Zheng, Weili Ren, Zuosheng Lei, Zhongming Ren

Journal of Materials Research· Volume 34· Issue 24
Publisher page

Abstract

Fe–6.5 Si–0.05 B alloy was used in the study to investigate the texture evolution and magnetic property of the ferromagnetic crystal under an axial high magnetic field during bulk solidification. Optical microscopy (OM) and X-ray diffraction (XRD) were applied to analyze the microstructures and texture evolution of the alloy solidified under different magnetic field intensities. The result shows that with an increase in the magnetic field intensity from 0 to 2 T, the texture gradually changes from random orientation to {100} 〈120〉, eventually becoming a mixture of cube and Goss texture. The alloys treated at 1 and 2 T showed magnetic anisotropic behavior, while the alloy treated at 0 T showed magnetic isotropic behavior. The change in magnetic property comes from the evolution of α-Fe crystal orientation. Furthermore, a method for controlling the crystallization process and crystallographic orientation by adjusting the magnetic field intensity was proposed.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Magnetic Properties and Applications · Microstructure and Mechanical Properties of Steels · Metallic Glasses and Amorphous Alloys

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (36)

Show source-provided references
1. 10.1016/j.matchemphys.2018.12.07010.1016/j.matchemphys.2018.12.070 ↗
2. 10.1016/j.matlet.2011.02.02010.1016/j.matlet.2011.02.020 ↗
3. 10.1016/j.stam.2003.07.00110.1016/j.stam.2003.07.001 ↗
4. 10.1063/1.302674210.1063/1.3026742 ↗
5. 10.1016/j.msea.2013.01.07010.1016/j.msea.2013.01.070 ↗
6. 10.1016/j.jmmm.2019.02.08910.1016/j.jmmm.2019.02.089 ↗
7. 10.1016/j.msea.2018.07.01310.1016/j.msea.2018.07.013 ↗
8. 10.1016/j.msea.2010.11.02310.1016/j.msea.2010.11.023 ↗
9. 10.1007/s11661-008-9525-210.1007/s11661-008-9525-2 ↗
10. 10.1063/1.34998510.1063/1.349985 ↗
11. 10.1063/1.34237310.1063/1.342373 ↗
12. 10.1016/0304-8853(96)00128-X10.1016/0304-8853(96)00128-X ↗
13. 10.1557/jmr.2009.030310.1557/jmr.2009.0303 ↗
14. 10.1016/j.jallcom.2018.08.29310.1016/j.jallcom.2018.08.293 ↗
15. High-strength low-iron-loss silicon steels fabricated by cold rolling
16. Evolution of magnetic properties and microstructure of high-silicon steel during hot dipping and diffusion annealing10.1109/TMAG.2002.802414 ↗
17. 10.1016/j.jmmm.2004.04.09810.1016/j.jmmm.2004.04.098 ↗
18. 10.1016/j.jmmm.2015.10.12710.1016/j.jmmm.2015.10.127 ↗
19. 10.1016/0304-8853(90)90554-410.1016/0304-8853(90)90554-4 ↗
20. 10.1016/j.jcrysgro.2007.12.04510.1016/j.jcrysgro.2007.12.045 ↗
21. 10.1016/j.jmmm.2014.01.00210.1016/j.jmmm.2014.01.002 ↗
22. 10.1038/349770a010.1038/349770a0 ↗
23. 10.1016/j.matlet.2014.10.12510.1016/j.matlet.2014.10.125 ↗
24. Effect of a transverse weak magnetic field on the texture evolution and magnetic property of Fe–1.0 wt% Si alloy during bulk solidification
25. 10.1016/j.intermet.2012.12.00510.1016/j.intermet.2012.12.005 ↗
26. 10.1063/1.170866410.1063/1.1708664 ↗
27. 10.1016/S0304-8853(01)01165-910.1016/S0304-8853(01)01165-9 ↗
28. 10.1002/(SICI)1521-4079(199902)34:2<181::AID-CRAT181>3.0.CO;2-110.1002/(SICI)1521-4079(199902)34:2<181::AID-CRAT181>3.0.CO;2-1 ↗
29. 10.1016/j.actamat.2009.10.04810.1016/j.actamat.2009.10.048 ↗
30. 10.1016/j.jmmm.2016.10.16310.1016/j.jmmm.2016.10.163 ↗
31. 10.1016/j.cossms.2012.08.00110.1016/j.cossms.2012.08.001 ↗
32. 10.1002/pssa.221068012210.1002/pssa.2210680122 ↗
33. 10.1002/1521-396X(200103)184:1<211::AID-PSSA211>3.0.CO;2-L10.1002/1521-396X(200103)184:1<211::AID-PSSA211>3.0.CO;2-L ↗
34. 10.1016/j.jmmm.2003.11.01210.1016/j.jmmm.2003.11.012 ↗
35. 10.1016/0022-0248(81)90333-X10.1016/0022-0248(81)90333-X ↗
36. 10.1557/jmr.2011.13610.1557/jmr.2011.136 ↗