Effects of ultrafine nanograins on the fracture toughness of nanocrystalline materials

For evaluating the effects of ultrafine nanograins (UFNGs) on the fracture toughness of conventional nanocrystalline (nc) materials, we developed a composite model composed of UFNGs (with a grain sizedbetween 2 and 4 nm) evenly distributed in the conventional nc matrix (20 nm ≤d≤ 100 nm). The UFNGs could be treated as a part of triple junctions, denoted as super triple junctions. In the framework of our model, stress concentration near crack tip initiates intergrain sliding that leads to the generation of edge dislocations at super triple junctions. The dependence of critical crack intensity factors on grain size was calculated. It was demonstrated that the existence of the UFNGs approximately doubles the critical crack intensity factors.