Preferential growth and orientation relationship of Ag₃Sn grains formed between molten Sn and (001) Ag single crystal

H.F. Zou; H.J. Yang; J. Tan; Z.F. Zhang

doi:10.1557/jmr.2009.0237

journal article·2009-06

Preferential growth and orientation relationship of Ag₃Sn grains formed between molten Sn and (001) Ag single crystal

H.F. Zou, H.J. Yang, J. Tan, Z.F. Zhang

Journal of Materials Research· Volume 24· Issue 6

Publisher page

Source abstract

Abstract

The current study shows that there is a preferred orientation relationship between Ag₃Sn and Ag in reaction between molten Sn and Ag. Due to the preferred orientation relationship, the morphology of Ag₃Sn grains formed on (001) Ag single crystal is different from those formed on (011), (358) single crystal Ag, and polycrystalline Ag Facet scallop-type Ag₃Sn grains formed irregularly on (011), (358) single crystal Ag, and polycrystalline Ag; whereas the regular Ag₃Sn grains with parallel edges grew on (001) Ag single crystal, and they were elongated along two perpendicular directions. The orientation relationship between Ag₃Sn grains and (001) Ag single crystal was determined using electron backscattered diffraction. The preferential growth of regular Ag₃Sn grains with parallel edges formed on (001) Ag single crystal can be attributed to their minimum misfit.

Source: crossref · Quality: baseline

Research context

OpenAlex topics: Electronic Packaging and Soldering Technologies · Aluminum Alloy Microstructure Properties · Metallurgical Processes and Thermodynamics

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (16)

Show source-provided references

1. 10.1107/S056774087200243210.1107/S0567740872002432 ↗

2. 10.1016/j.actamat.2008.01.00610.1016/j.actamat.2008.01.006 ↗

3. 10.1007/s11664-002-0202-810.1007/s11664-002-0202-8 ↗

4. 10.1021/cm047806910.1021/cm0478069 ↗

5. 10.1016/j.actamat.2008.01.05510.1016/j.actamat.2008.01.055 ↗

6. 10.1557/JMR.2002.010810.1557/JMR.2002.0108 ↗

7. 10.1021/cm000803l10.1021/cm000803l ↗

8. 10.1021/cm048152710.1021/cm0481527 ↗

9. 10.1016/S0927-796X(00)00010-310.1016/S0927-796X(00)00010-3 ↗

10. 10.1016/j.mser.2005.03.00110.1016/j.mser.2005.03.001 ↗

11. 10.1016/j.jallcom.2007.07.00110.1016/j.jallcom.2007.07.001 ↗

12. 10.1103/PhysRevB.53.1602710.1103/PhysRevB.53.16027 ↗

13. 10.1557/jmr.2006.036910.1557/jmr.2006.0369 ↗

14. 10.1016/j.actamat.2007.11.00910.1016/j.actamat.2007.11.009 ↗

15. 10.1063/1.276184010.1063/1.2761840 ↗

16. 10.1063/1.277600210.1063/1.2776002 ↗