Validated measurement of Young's modulus, Poisson ratio, and thickness for thin coatings by combining instrumented nanoindentation and acoustical measurements
Source abstract
Abstract
Nanoindentation is one of the very few techniques that can measure both the elastic and plastic properties of very small volumes of materials. Recently it has been shown that the properties of thin coatings can be determined by nanoindentation, even when the normal indentation response includes a significant component due to the substrate. This paper takes the method a step further and shows how by combining acoustical test methods with nanoindentation, a validated set of values for the thickness, Young's modulus, and Poisson ratio for a coating can be obtained.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Ultrasonics and Acoustic Wave Propagation · Acoustic Wave Resonator Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. 10.1016/0040-6090(95)06875-910.1016/0040-6090(95)06875-9 ↗
2. 10.1016/S0040-6090(01)01338-410.1016/S0040-6090(01)01338-4 ↗
3. 10.1016/S0257-8972(99)00316-310.1016/S0257-8972(99)00316-3 ↗
4. 5. ASTM C 1259-98, Standard Method for Dynamic Young’s Modulus, Shear Modulus and Poisson’s Ratio for Advanced Ceramics by Impulse Excitation of Vibration (American Society for Testing and Materials, West Conshohocken, PA).
5. 10.1016/S0257-8972(96)03147-710.1016/S0257-8972(96)03147-7 ↗
6. 10.1006/jsvi.1993.124810.1006/jsvi.1993.1248 ↗
7. 10.1051/metal/19999602025910.1051/metal/199996020259 ↗
8. 10.1557/JMR.1992.156410.1557/JMR.1992.1564 ↗
9. 2. BS EN ISO 14577: 2002 parts 1–3, Metallic Materials—Instrumented Indentation Test for Hardness and Materials Parameters (International Organization for Standardization, Geneva, Switzerland).
10. 3. European report, INDICOAT SMT-CT98-2249, NPL Report MATC (A) 24 (National Physical Laboratory, Middlesex, U.K., 2001).
11. 10.1063/1.147239310.1063/1.1472393 ↗
12. 10.1088/0957-0233/12/9/31510.1088/0957-0233/12/9/315 ↗
13. 10.1121/1.149913110.1121/1.1499131 ↗
14. 10.1016/S0925-9635(97)00337-310.1016/S0925-9635(97)00337-3 ↗
15. Jennett · 2002 · 695 · 73
16. Farnell · 1972 · IX · 35
17. 10.1016/S0925-8388(97)00297-110.1016/S0925-8388(97)00297-1 ↗
18. 10.1063/1.37073010.1063/1.370730 ↗
19. 10.1016/S0040-6090(96)09163-810.1016/S0040-6090(96)09163-8 ↗
20. 4. ASTM E 1876-99, Standard Method for Dynamic Young’s Modulus, Shear Modulus, and Poisson’s Ratio by Impulse Excitation of Vibration (American Society for Testing and Materials, West Conshohocken, PA).
21. 10.1007/BF0153819310.1007/BF01538193 ↗