Using differential scanning calorimetry to characterize the precipitation and dissolution of V(CN) and VC particles during continuous casting and reheating process
Source abstract
Abstract
In this work, differential scanning calorimetry (DSC) was used to characterize and analyze the precipitation/dissolution kinetics of second phase particles during the cooling/reheating process in a vanadium microalloyed steel. The results indicated that three obvious exothermic peaks were detected on the cooling DSC curve. Furthermore, three corresponding endothermic peaks were also detected on the heating DSC curve. Combined with thermodynamic calculation and transmission electron microscopy analysis, these three exothermic peaks along cooling DSC curve were defined as the precipitation reaction of V(CN), the reaction of austenite transformation into ferrite and the precipitation reaction of VC, respectively. Meanwhile, three corresponding reverse reactions for cooling were also defined along the reheating DSC curve. The linear regression result revealed that the precipitation activation energies for V(CN) and VC were identified as 311.2 kJ/mol and 167.6 kJ/mol, respectively. The dissolution activation energies for VC and V(CN) were identified as 255.4 kJ/mol and 592.6 kJ/mol, respectively.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Metal Extraction and Bioleaching · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. 10.1016/j.jnucmat.2008.09.01210.1016/j.jnucmat.2008.09.012 ↗
2. 10.1007/BF0258613510.1007/BF02586135 ↗
3. 10.1179/1743281214Y.000000022710.1179/1743281214Y.0000000227 ↗
4. 10.1007/s11663-015-0349-310.1007/s11663-015-0349-3 ↗
5. 10.1016/S1003-6326(11)60843-110.1016/S1003-6326(11)60843-1 ↗
6. Yong · 2006
7. Analysis on high-temperature precipitation behavior of V–N microalloyed anti-seismic rebars
8. 10.1016/j.matdes.2011.03.06810.1016/j.matdes.2011.03.068 ↗
9. Ferrite transformation kinetics of X70 pipeline steel during continuous cooling
10. 10.1179/03019230067763310.1179/030192300677633 ↗
11. 10.1016/j.msea.2014.11.00510.1016/j.msea.2014.11.005 ↗
12. Precipitation in V bearing microalloyed steel containing low concentrations of Ti and Nb
13. 10.1016/j.matlet.2004.10.05810.1016/j.matlet.2004.10.058 ↗
14. 10.1016/j.tca.2011.09.00110.1016/j.tca.2011.09.001 ↗
15. 10.1016/j.actamat.2010.03.04810.1016/j.actamat.2010.03.048 ↗
16. 10.1016/j.msea.2011.02.08710.1016/j.msea.2011.02.087 ↗
17. 10.1016/j.matchar.2007.08.01410.1016/j.matchar.2007.08.014 ↗
18. 10.2355/isijinternational1966.26.104510.2355/isijinternational1966.26.1045 ↗
19. 10.1016/S1003-6326(14)63327-610.1016/S1003-6326(14)63327-6 ↗
20. 10.1002/chin.20050422410.1002/chin.200504224 ↗
21. Muller · Precipitation during continuous casting · 2015
22. 10.1179/imr.1991.36.1.18710.1179/imr.1991.36.1.187 ↗
23. 10.1016/j.scriptamat.2005.12.02310.1016/j.scriptamat.2005.12.023 ↗
24. 10.1016/0040-6031(95)02466-210.1016/0040-6031(95)02466-2 ↗
25. 10.1016/j.pnsc.2015.02.00410.1016/j.pnsc.2015.02.004 ↗
26. 10.1016/j.msea.2014.08.03010.1016/j.msea.2014.08.030 ↗
27. 10.1016/j.actamat.2008.04.01510.1016/j.actamat.2008.04.015 ↗
28. 10.1179/030192309X1250680420046510.1179/030192309X12506804200465 ↗
29. 10.1016/j.matdes.2015.09.04610.1016/j.matdes.2015.09.046 ↗
30. 10.1016/j.jallcom.2006.07.07610.1016/j.jallcom.2006.07.076 ↗
31. 10.1007/BF0282570210.1007/BF02825702 ↗
32. Effect of microalloying additions on steel plate to pipe property variations during UOE linepipe processing
33. 10.1134/S0031918X1410008110.1134/S0031918X14100081 ↗
34. 10.1016/j.msea.2011.01.09710.1016/j.msea.2011.01.097 ↗
35. 10.1016/j.msea.2014.05.07210.1016/j.msea.2014.05.072 ↗
36. 10.1016/j.msea.2011.03.08610.1016/j.msea.2011.03.086 ↗
37. Pierson · 1996