Effects of aging on shape memory and wear resistance of a Fe–Mn–Si-based alloy
Source abstract
Abstract
The influence of aging treatment on shape memory effect (SME) and wear resistance of Fe–20Mn–5Si–10Cr–5Ni–0.7V–0.2N (mass%) alloy was investigated. Results showed that vanadium nitride (VN) particles precipitated during aging treatment, and the amount and size of the particles increased with increasing aging time. The sample aged for 8 h exhibited the maximal shape recovery ratio of 74% (compared with that of 16% for unaged) and favorable wear resistance in both dry wear and oil-lubricant wear conditions. The fine VN particles are the key factor to improve the SME by strengthening the alloy and acting as preferential nucleation sites for martensite. However, more and larger particles due to further aging treatment appeared to have negative effects on the SME and wear resistance. After oil-lubricant friction, there existed large amounts of friction-stress-induced ε martensite in the worn surface of the sample. As a result, the wear resistance of samples in oil-lubricant wear condition was remarkably higher than that in dry wear condition.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Shape Memory Alloy Transformations · Aluminum Alloy Microstructure Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. 10.1007/s10853-009-3987-510.1007/s10853-009-3987-5 ↗
2. 10.1016/j.msea.2007.05.04310.1016/j.msea.2007.05.043 ↗
3. 10.1016/0921-5093(91)90277-T10.1016/0921-5093(91)90277-T ↗
4. Analysis of wear resistance and its mechanism in an Fe–Mn–Si–Cr–Ni shape memory alloy
5. 10.1016/j.msea.2008.11.04810.1016/j.msea.2008.11.048 ↗
6. 10.1016/j.matdes.2011.01.03210.1016/j.matdes.2011.01.032 ↗
7. Effect of pre-deformation at room temperature on shape memory properties of stainless type Fe–15Mn–5Si–9Cr–5Ni–(0.5–1.5)NbC alloys
8. 10.1016/j.apsusc.2008.01.15410.1016/j.apsusc.2008.01.154 ↗
9. 10.1002/adem.20080031210.1002/adem.200800312 ↗
10. Shape memory effect of Fe-14 % Mn-6 % Si-9 % Cr-6 % Ni alloy polycrystals
11. 10.1016/0001-6160(82)90011-610.1016/0001-6160(82)90011-6 ↗
12. 10.1016/j.actamat.2004.09.03710.1016/j.actamat.2004.09.037 ↗
13. 10.1016/j.msea.2003.10.35910.1016/j.msea.2003.10.359 ↗
14. 10.1016/j.jallcom.2008.05.02410.1016/j.jallcom.2008.05.024 ↗
15. 10.1016/j.jallcom.2008.07.01410.1016/j.jallcom.2008.07.014 ↗
16. 10.2320/matertrans1989.41.59310.2320/matertrans1989.41.593 ↗
17. 10.1016/j.msea.2003.10.35710.1016/j.msea.2003.10.357 ↗
18. 10.1016/j.msea.2011.03.07210.1016/j.msea.2011.03.072 ↗
19. 10.1016/S0921-5093(99)00290-710.1016/S0921-5093(99)00290-7 ↗