Sol-gel Lithium Borophosphates
Source abstract
Abstract
In this paper we present sol-gel synthesis and thermal and structural characterization of some lithium borophosphates. The as-prepared samples are mostly partially crystalline, and densification heat treatments at 500 °C cause samples to crystallize. In the phosphorus-rich part of the composition triangle we have lithium excess with respect to the nominal composition, which is likely due to the low reactivity of the phosphorus precursor. On the boron-rich side, in contrast, lithium losses are found which probably occur during syneresis.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Chemical Synthesis and Characterization · Zeolite Catalysis and Synthesis · Inorganic Chemistry and Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. 10.1016/0022-3093(82)90186-710.1016/0022-3093(82)90186-7 ↗
2. Bray · Phys. Chem. Glasses · 1963 · 4 · 37
3. 10.1016/0022-3093(82)90112-010.1016/0022-3093(82)90112-0 ↗
4. 10.1016/0025-5408(67)90148-110.1016/0025-5408(67)90148-1 ↗
5. 10.1111/j.1151-2916.1958.tb13496.x10.1111/j.1151-2916.1958.tb13496.x ↗
6. 10.1107/S0365110X6200050X10.1107/S0365110X6200050X ↗
7. 10.1016/0022-3093(94)90077-910.1016/0022-3093(94)90077-9 ↗
8. 10.1016/S0022-3093(05)80548-410.1016/S0022-3093(05)80548-4 ↗
9. 10.1016/0040-6031(95)02786-610.1016/0040-6031(95)02786-6 ↗
10. 10.1021/cm950277b10.1021/cm950277b ↗
11. 10.1111/j.1151-2916.1995.tb08615.x10.1111/j.1151-2916.1995.tb08615.x ↗
12. 10.1016/S0022-3093(05)80586-110.1016/S0022-3093(05)80586-1 ↗
13. 10.1016/0022-3093(86)90118-310.1016/0022-3093(86)90118-3 ↗
14. 10.1016/S0025-5408(97)00038-X10.1016/S0025-5408(97)00038-X ↗
15. 10.1016/S0022-3093(05)80382-510.1016/S0022-3093(05)80382-5 ↗
16. Brinker · 1986 · 73 · 57
17. 10.1016/0022-3093(84)90021-810.1016/0022-3093(84)90021-8 ↗
18. Brinker · 1990
19. Mackenzie · 1984 · 15
20. 10.1016/S0022-3093(87)80264-810.1016/S0022-3093(87)80264-8 ↗
21. 10.1016/S0022-3093(87)80180-110.1016/S0022-3093(87)80180-1 ↗
22. 10.1016/0167-2738(86)90140-210.1016/0167-2738(86)90140-2 ↗
23. 10.1007/BF0040089810.1007/BF00400898 ↗
24. 10.1016/0378-7753(85)88016-210.1016/0378-7753(85)88016-2 ↗
25. Greenblatt · Phys. Chem. Glasses · 1967 · 8 · 213
26. 10.1016/0022-3093(91)90008-T10.1016/0022-3093(91)90008-T ↗
27. 10.1557/JMR.1996.001710.1557/JMR.1996.0017 ↗
28. 10.1016/0022-3093(90)90105-U10.1016/0022-3093(90)90105-U ↗
29. 10.1051/jcp/198683085110.1051/jcp/1986830851 ↗
30. 10.1016/S0022-3093(97)00026-410.1016/S0022-3093(97)00026-4 ↗
31. 10.1107/S056774086800191310.1107/S0567740868001913 ↗
32. 10.1021/ic960808d10.1021/ic960808d ↗
33. 10.1111/j.1151-2916.1961.tb15361.x10.1111/j.1151-2916.1961.tb15361.x ↗
34. 10.1016/0022-3093(91)90450-K10.1016/0022-3093(91)90450-K ↗
35. 10.1107/S0365110X5900236510.1107/S0365110X59002365 ↗
36. 10.1016/0378-7753(85)88016-210.1016/0378-7753(85)88016-2 ↗
37. 10.1016/0022-3093(80)90439-110.1016/0022-3093(80)90439-1 ↗
38. Magistris · 1992 · 213
39. 10.1111/j.1151-2916.1995.tb09069.x10.1111/j.1151-2916.1995.tb09069.x ↗
40. 10.1016/S0025-5408(98)00046-410.1016/S0025-5408(98)00046-4 ↗