Characterization of AlN-based ceramic composites for use as millimeter-wave susceptor materials at high temperature: Dielectric properties of AlN:Mo with 0.25 vol% to 4.0 vol% Mo from 25 to 550 °C

Microstructural analysis and bulk dielectric property analysis (real and imaginary permittivity at 95 GHz) were performed at temperatures ranging from 25 to 550 °C for ceramic composites comprising a hot-pressed aluminum nitride matrix (containing yttria and trace carbon as sintering additives) with molybdenum powder as a millimeter-wave radiation-absorbing additive. Loading percentages in the range of 0.25 vol% to 4.0 vol% Mo were characterized. For the temperature regime evaluated, the temperature-related changes in real and imaginary components of permittivity were found to be relatively modest compared with those driven by Mo loading. Energy-dispersive X-ray spectroscopic analysis of Mo grains and surrounding regions showed the presence of a mixed-phase layer, containing Mo2C, at the AlN–Mo interface. The Mo2C-containing mixed-phase layer, typically a few micrometers thick, surrounded the Mo grains. Further characterization of this mixed-phase layer is required to determine its contribution to the dielectric properties of the composite.