Ni₃N compound layers produced by gaseous nitriding of nickel substrates; layer growth, macrostresses and intrinsic elastic anisotropy

Ni3N was prepared by gaseous nitriding of nickel substrates using gas mixtures of high nitrogen activities, composed of NH3and H2at 1 atm and at temperatures between 175 °C and 550 °C. At least above 300 °C closed Ni3N layers developed, which possess distinct compressive macrostrain parallel to the surface. The observed hkl-anisotropy of the macrostrain could be ascribed to the elastic anisotropy as indicated by the single-crystal elastic constants of Ni3N obtained from firstprinciples calculations performed in this work. The macrostress originates from the thermal misfit between layer and substrate, developing upon cooling. The extent of macrostress is reduced by partial misfit accommodation by plastic deformation as well as by porosity.