Wetting by liquid sodium and fracture path analysis of sodium induced embrittlement of 304L stainless steel

The wettability of the 304L steel is an important parameter in Liquid Metal Embrittlement studies. Empirically, it is found to be greatly enhanced by pre-exposure to oxygenated liquid sodium. The corrosion interface formed during exposure to sodium has been analyzed at the nanoscale by transmission electron microscopy using the focused ion beam sampling. A thin layer of sodium chromite (NaxCrO2withx≤ 1) is detected at the interface validating wetting on an oxide mechanism for the enhanced wetting after pre-exposure. Fracture micromechanisms and the crack path of liquid sodium-embrittled austenitic steel 304L at 573 K have been investigated down to the nanoscale. High-resolution orientation mapping analyses immediately below the fracture surface show that abundant martensitic transformations (γ → α) and twinning occur during deformation of austenite. The preferential crack path is intergranular along the newly formed γ/γ interfaces. It is concluded that these transformations play a major role in the fracture process.