Slow and rapid cooling of Al–Cu–Si ultrafine eutectic composites: Interplay of cooling rate and microstructure in mechanical properties
Source abstract
Abstract
Ternary Al–15 wt% Cu–7 wt% Si and Al–22 wt% Cu–7 wt% Si alloy specimens were generated by transient directional solidification (DS) and rapid solidification (RS) techniques. The microstructures are constituted by an α-Al dendritic matrix surrounded by two eutectic, that is, a binary eutectic (Si + α-Al) and a bimodal eutectic, consisting of cellular-type binary eutectic colonies (α-Al + Al2Cu) in a ternary eutectic matrix consisting of α-Al + Al2Cu + Si. The bimodal eutectic exists at cooling rates from 0.5 to 250 K/s. The secondary dendritic spacing, λ2, of the DS samples varied from 5 to 20 µm and from 10 to 18 µm for both examined alloys. The λ2from 2.7 to 4.0 µm characterized the RS samples. Mechanical properties have been determined for various samples related to different dendritic spacing values. Based on the evaluation of the rapidly solidified microstructures, it was possible to assess the cooling rates.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Aluminum Alloy Microstructure Properties · Metallic Glasses and Amorphous Alloys
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. 10.1016/j.matdes.2014.03.04810.1016/j.matdes.2014.03.048 ↗
2. 10.1016/j.msea.2016.12.09610.1016/j.msea.2016.12.096 ↗
3. Mater. Sci. Forum · 2006 · 519–521 · 359
4. 10.1038/nature0113310.1038/nature01133 ↗
5. Nat. Commun. · 2010 · 1 · 1
6. 2017 · 17
7. 10.1038/nmat79710.1038/nmat797 ↗
8. 10.1088/0370-1301/64/9/30310.1088/0370-1301/64/9/303 ↗
9. 10.1557/jmr.2009.029710.1557/jmr.2009.0297 ↗
10. 10.1007/BF0264469210.1007/BF02644692 ↗
11. 10.1080/0950083041000172833610.1080/09500830410001728336 ↗
12. 1992 · 93
13. 10.1016/j.scriptamat.2007.08.00410.1016/j.scriptamat.2007.08.004 ↗
14. 10.1016/j.intermet.2010.02.04210.1016/j.intermet.2010.02.042 ↗
15. 10.1038/nmat79210.1038/nmat792 ↗
16. Sci. Rep. · 2014 · 4 · 1
17. 10.1007/s11661-012-1308-010.1007/s11661-012-1308-0 ↗
18. 10.1016/S1005-0302(11)60006-610.1016/S1005-0302(11)60006-6 ↗
19. 10.1016/B978-0-408-70932-3.50213-810.1016/B978-0-408-70932-3.50213-8 ↗
20. 10.1007/s11661-000-0096-010.1007/s11661-000-0096-0 ↗
21. 10.1016/j.jallcom.2016.10.01010.1016/j.jallcom.2016.10.010 ↗
22. 10.1016/S0921-5093(01)01649-510.1016/S0921-5093(01)01649-5 ↗
23. 1993 · 808
24. 10.1016/j.jallcom.2016.11.39910.1016/j.jallcom.2016.11.399 ↗
25. 10.1007/s11664-016-5225-710.1007/s11664-016-5225-7 ↗
26. 1958 · 276
27. 10.1038/s41598-016-0028-x10.1038/s41598-016-0028-x ↗
28. 10.1016/j.matdes.2015.12.08010.1016/j.matdes.2015.12.080 ↗
29. 10.1016/j.jallcom.2015.11.11710.1016/j.jallcom.2015.11.117 ↗
30. 10.1016/S1468-6996(01)00023-710.1016/S1468-6996(01)00023-7 ↗
31. 10.1016/S1359-6462(97)00542-310.1016/S1359-6462(97)00542-3 ↗
32. Mater. Sci. Forum · 1996 · 215–216 · 331
33. Mater. Sci. Eng., A · 2005 · 413–414 · 165
34. Dyn. Curved Front · 1988 · 236 · 363
35. 10.1179/106678509X1248947852353710.1179/106678509X12489478523537 ↗
36. 10.1016/S1359-6462(03)00394-410.1016/S1359-6462(03)00394-4 ↗