Meso-Porous Alumina Capillary Tube as a Support for High-Temperature Gas Separation Membranes by Novel Pulse Sequential Anodic Oxidation Technique

A meso-porous anodic alumina capillary tube (MAAC) having highly oriented radial meso-pore channels with a minimum diameter of 3 nm has been successfully synthesized using a novel pulse sequential anodic oxidation technique at 100 Hz of pulse frequency. A value resulting in a high channel-pore formation rate at 1 V of the pulse sequential voltage was determined to be the optimum pulse frequency for the anodization. Transmission electron microscopy observation and N₂ sorption analysis revealed that controlling the minimum pore channel diameter at 3 nm was possible by the voltage of 1 V. The gas permeance according to Knudsen’s diffusion mechanism was demonstrated at 500 °C, by evaluating gas permeation properties through the meso-porous anodic alumina capillary tube with radial meso-pore channels with minimum diameter of 3 nm, achieving hydrogen permeance of 1.8 × 10⁻⁶ mol/m² s Pa.