Synthesis of positively charged polyelectrolyte multilayer membranes for removal of divalent metal ions
Source abstract
Abstract
Alternating layer-by-layer (LbL) deposition of polycations and polyanions on porous substrates is a convenient and versatile method for forming high-flux nanofiltration (NF) membranes. In this work, positively charged NF membranes were fabricated by the LbL assembly of poly(ethyleneimine) (PEI) and poly(sodium 4-styrenesulfonate) (PSS) on the modified polyacrylonitrile ultra-filtration substrate. The charge variation with each layer was characterized by zeta potential. ATR-FTIR, SEM, N2adsorption and the weight changes with bi-layers were used to confirm the LbL deposition of the polyelectrolytes. NF performances of the prepared membrane with a number of bi-layers as well as solute concentrations were also investigated. The results of zeta potential showed that the whole multilayer films exhibited periodic variations in positive charge. NF results indicated that the rejection of Ni2+and Cd2+ions increased, while the permeate fluxes decreased with the number of bi-layers. And the rejections of the metal ion solutes were 98.02% for CuSO4, 95.53% for ZnSO4, 95.66% for NiCl2, 94.9% for CdCl2, along with permeation fluxes of 19.02, 19.72, 24.02, and 21.19 L/m2·h, respectively.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Polymer Surface Interaction Studies · Membrane Separation Technologies · Electrostatics and Colloid Interactions
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (54)
Show source-provided references
1. 10.1016/j.memsci.2003.11.00310.1016/j.memsci.2003.11.003 ↗
2. 10.1016/S0376-7388(02)00356-310.1016/S0376-7388(02)00356-3 ↗
3. 10.1021/la034603a10.1021/la034603a ↗
4. 10.1002/app.1045210.1002/app.10452 ↗
5. 10.1016/j.memsci.2010.05.02110.1016/j.memsci.2010.05.021 ↗
6. 10.1016/j.memsci.2010.03.00210.1016/j.memsci.2010.03.002 ↗
7. 10.1021/la020926f10.1021/la020926f ↗
8. 10.1016/j.memsci.2008.10.05110.1016/j.memsci.2008.10.051 ↗
9. 10.1016/j.memsci.2005.12.01410.1016/j.memsci.2005.12.014 ↗
10. 10.1016/j.colsurfa.2009.01.03910.1016/j.colsurfa.2009.01.039 ↗
11. 10.1016/S1383-5866(98)00096-310.1016/S1383-5866(98)00096-3 ↗
12. 10.1016/j.jhazmat.2011.10.01610.1016/j.jhazmat.2011.10.016 ↗
13. 10.1016/j.desal.2005.04.03910.1016/j.desal.2005.04.039 ↗
14. 10.1016/j.jhazmat.2008.02.08510.1016/j.jhazmat.2008.02.085 ↗
15. 10.1016/S0376-7388(02)00328-910.1016/S0376-7388(02)00328-9 ↗
16. 10.1016/S0011-9164(03)00435-110.1016/S0011-9164(03)00435-1 ↗
17. 10.1016/j.memsci.2010.04.00310.1016/j.memsci.2010.04.003 ↗
18. 10.1016/j.memsci.2010.10.02910.1016/j.memsci.2010.10.029 ↗
19. Removal of transition metal ions from aqueous solutions by adsorption using a novel hybrid material silica gel chemically modified by triethylenetetraminomethylenephosphonic acid10.1016/j.cej.2010.05.065 ↗
20. 10.1016/j.memsci.2011.04.03410.1016/j.memsci.2011.04.034 ↗
21. 10.1016/j.memsci.2008.06.02810.1016/j.memsci.2008.06.028 ↗
22. 10.1016/j.desal.2008.10.00910.1016/j.desal.2008.10.009 ↗
23. 10.1016/j.jhazmat.2010.06.07610.1016/j.jhazmat.2010.06.076 ↗
24. 10.1016/j.desal.2004.08.02710.1016/j.desal.2004.08.027 ↗
25. 10.1016/j.seppur.2007.11.01210.1016/j.seppur.2007.11.012 ↗
26. 10.1016/j.desal.2004.10.00910.1016/j.desal.2004.10.009 ↗
27. 10.1016/j.memsci.2004.03.02910.1016/j.memsci.2004.03.029 ↗
28. 10.1016/j.desal.2005.06.01710.1016/j.desal.2005.06.017 ↗
29. 10.1016/j.memsci.2004.03.02710.1016/j.memsci.2004.03.027 ↗
30. 10.1016/j.colsurfa.2007.03.01910.1016/j.colsurfa.2007.03.019 ↗
31. 10.1016/j.watres.2005.03.03310.1016/j.watres.2005.03.033 ↗
32. 10.1016/j.jhazmat.2005.03.04810.1016/j.jhazmat.2005.03.048 ↗
33. 10.1016/j.jhazmat.2006.05.09010.1016/j.jhazmat.2006.05.090 ↗
34. 10.2166/wst.1995.035010.2166/wst.1995.0350 ↗
35. 6. Song J. , Oh H. , Kong H. , and Jang J. : Polyrhodanine modified anodic aluminum oxide membrane for heavy metal ions removal. J. Hazard. Mater. 187, 311–317.10.1016/j.jhazmat.2011.01.026 ↗
36. 10.1016/j.memsci.2008.07.01810.1016/j.memsci.2008.07.018 ↗
37. 10.1021/cm020639x10.1021/cm020639x ↗
38. 10.1016/j.seppur.2004.10.01110.1016/j.seppur.2004.10.011 ↗
39. 10.1016/j.memsci.2012.06.01310.1016/j.memsci.2012.06.013 ↗
40. 10.1016/j.desal.2012.05.02210.1016/j.desal.2012.05.022 ↗
41. 10.1016/S1383-5866(02)00095-310.1016/S1383-5866(02)00095-3 ↗
42. 10.1016/j.memsci.2006.05.01510.1016/j.memsci.2006.05.015 ↗
43. 10.1016/j.jcis.2009.06.02010.1016/j.jcis.2009.06.020 ↗
44. 10.1016/S0376-7388(97)00125-710.1016/S0376-7388(97)00125-7 ↗
45. 10.1021/la800179z10.1021/la800179z ↗
46. 10.1016/j.memsci.2007.10.03110.1016/j.memsci.2007.10.031 ↗
47. 10.1021/la051669s10.1021/la051669s ↗
48. 10.1016/j.memsci.2006.07.00710.1016/j.memsci.2006.07.007 ↗
49. 10.1016/j.seppur.2011.01.00510.1016/j.seppur.2011.01.005 ↗
50. 10.1016/0376-7388(94)00196-610.1016/0376-7388(94)00196-6 ↗
51. 10.1016/S0376-7388(97)00114-210.1016/S0376-7388(97)00114-2 ↗
52. 10.1016/S0376-7388(98)00079-910.1016/S0376-7388(98)00079-9 ↗
53. 10.1016/j.cej.2008.12.02310.1016/j.cej.2008.12.023 ↗
54. 10.1016/j.jcis.2009.12.03310.1016/j.jcis.2009.12.033 ↗