The effects of heating/cooling rate on the phase transformations and thermal expansion coefficient of C–Mn as-cast steel at elevated temperatures

Zhang Jian, Chen Deng-Fu, Zhang Cheng-Qian, Hwang Weng-Sing, Han Ming-Rong

Journal of Materials Research· Volume 30· Issue 13
Publisher page

Abstract

Dilatometric studies of C–Mn hypoeutectoid steel with an as-cast structure were carried out to study the effects of the heating or cooling rate, heating and cooling process on phase transformation, and the thermal expansion coefficient. As the heating or cooling rate (Vc) increased, the characteristic temperatures ofAc1,Acp, andAc3also rose, whileAr3,Ar1, andArpfell. In addition, the phase transformation temperature range (Ac3–Ac1) rose, while (Ar3–Arp) fell as the heating or cooling rate increased. At the same time, the maximum thermal expansion coefficients│αT│ between the heating and cooling processes during phase transformation showed significant differences, and the difference (│ΔαT│) in the maximum │αT│ between these processes increased along with the heating or cooling rate, and this is because of the different phase transformation rates, with regard to the change from austenite to ferrite on cooling and ferrite to austenite on heating. During the heating process, the phase transformation rate of ferrite to austenite first decreases and then increases as the temperature rises, and the phase transformation rate of austenite to ferrite first increases and then decreases during the cooling process. The evolution of carbon and substitutional alloying elements (Si and Mn) in austenite during heating and cooling is also analyzed in this work.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Microstructure and Mechanical Properties of Steels · Metallurgical Processes and Thermodynamics · Metallurgical and Alloy Processes

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (27)

Show source-provided references
1. 10.1016/0956-716X(93)90169-S10.1016/0956-716X(93)90169-S ↗
2. 10.1016/S1044-5803(98)00024-210.1016/S1044-5803(98)00024-2 ↗
3. 10.1016/S1359-6462(98)00131-610.1016/S1359-6462(98)00131-6 ↗
4. 10.1179/1743281214Y.000000022710.1179/1743281214Y.0000000227 ↗
5. 10.1016/j.matchar.2006.04.02710.1016/j.matchar.2006.04.027 ↗
6. Dilatometric examination of continuously heated austenite formation in hypoeutectoid steels
7. 10.1016/j.msea.2004.03.04010.1016/j.msea.2004.03.040 ↗
8. 10.1016/S0921-5093(03)00587-210.1016/S0921-5093(03)00587-2 ↗
9. 10.1016/j.actamat.2006.12.00710.1016/j.actamat.2006.12.007 ↗
10. 10.1007/s11661-010-0267-610.1007/s11661-010-0267-6 ↗
11. 10.2355/isijinternational1966.22.4810.2355/isijinternational1966.22.48 ↗
12. 10.1179/1743281211Y.000000004610.1179/1743281211Y.0000000046 ↗
13. Barber · 1998
14. Critical points of hypoeutectoid steel–prediction of the pearlite dissolution finish temperature Ac1f
15. 10.1016/S1044-5803(02)00259-010.1016/S1044-5803(02)00259-0 ↗
16. A CCT diagram for an offshore pipeline steel of X70 type
17. 10.1023/A:100480540240410.1023/A:1004805402404 ↗
18. 10.1088/0957-0233/12/3/20110.1088/0957-0233/12/3/201 ↗
19. 10.1179/174328408X26564010.1179/174328408X265640 ↗
20. 10.2355/isijinternational1966.24.16910.2355/isijinternational1966.24.169 ↗
21. 10.1007/s11665-010-9825-810.1007/s11665-010-9825-8 ↗
22. 10.1016/j.matchar.2004.07.00510.1016/j.matchar.2004.07.005 ↗
23. 2011
24. 10.1023/A:101657951072310.1023/A:1016579510723 ↗
25. 10.1016/j.scriptamat.2008.01.01910.1016/j.scriptamat.2008.01.019 ↗
26. 10.1016/j.matchar.2013.08.00210.1016/j.matchar.2013.08.002 ↗
27. 10.2355/isijinternational.41.109310.2355/isijinternational.41.1093 ↗