The microstructure and corrosion resistance of biological Mg–Zn–Ca alloy processed by high-pressure torsion and subsequently annealing
Source abstract
Abstract
Magnesium alloy has great potential for bone implantation. However, its corrosion rate is fast in physiological environment. In this paper, biological Mg–Zn–Ca alloy was processed by high pressure torsion (HPT) and subsequently annealed at 90–270 °C for 30 min. The microstructure and corrosion resistance in simulated body fluid were investigated. The results revealed that with the rise of the annealing temperature, the grain size of the HPT alloy gradually increased and the relative diffraction peak intensity of (0002) grain orientation decreased. The amount of second phases increased first and then decreased, while the surface stress decreased first and then increased. All of these changes affected the corrosion rate simultaneously. The corrosion resistance of the HPT alloy increased first and then decreased with the rise of annealing temperature. After annealing at 210 °C for 30 min, the corrosion resistance was the best. Therefore, it was feasible to control the corrosion rate via annealing treatment.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Metal and Thin Film Mechanics · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (80)
Show source-provided references
1. 10.1016/j.matdes.2013.07.04510.1016/j.matdes.2013.07.045 ↗
2. 10.1016/j.corsci.2015.09.01810.1016/j.corsci.2015.09.018 ↗
3. 10.1016/j.jmrt.2015.11.00610.1016/j.jmrt.2015.11.006 ↗
4. 10.1016/j.matlet.2010.11.01510.1016/j.matlet.2010.11.015 ↗
5. 10.1016/j.matchar.2014.09.02010.1016/j.matchar.2014.09.020 ↗
6. 10.1016/j.msea.2011.01.06610.1016/j.msea.2011.01.066 ↗
7. 10.1023/A:100868241514110.1023/A:1008682415141 ↗
8. 10.1016/j.actbio.2011.11.01410.1016/j.actbio.2011.11.014 ↗
9. 10.1557/jmr.2006.021410.1557/jmr.2006.0214 ↗
10. 10.1016/j.mseb.2010.12.01710.1016/j.mseb.2010.12.017 ↗
11. 10.1533/9780857091413.3.29910.1533/9780857091413.3.299 ↗
12. 10.1016/j.scriptamat.2007.10.02710.1016/j.scriptamat.2007.10.027 ↗
13. 10.1016/j.proeng.2011.04.08710.1016/j.proeng.2011.04.087 ↗
14. 10.1016/j.msea.2015.11.07410.1016/j.msea.2015.11.074 ↗
15. 10.1016/j.msea.2011.02.04810.1016/j.msea.2011.02.048 ↗
16. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
17. 10.1016/j.pmatsci.2008.03.00210.1016/j.pmatsci.2008.03.002 ↗
18. 10.1016/j.actamat.2008.10.01610.1016/j.actamat.2008.10.016 ↗
19. 10.1016/0001-6160(65)90039-810.1016/0001-6160(65)90039-8 ↗
20. 10.1016/j.matlet.2010.11.05110.1016/j.matlet.2010.11.051 ↗
21. 10.1016/j.matdes.2011.04.03110.1016/j.matdes.2011.04.031 ↗
22. 10.1016/j.injury.2007.01.03610.1016/j.injury.2007.01.036 ↗
23. 10.1016/j.actbio.2010.12.00410.1016/j.actbio.2010.12.004 ↗
24. 10.1016/j.scriptamat.2011.01.02310.1016/j.scriptamat.2011.01.023 ↗
25. 10.1016/j.jmatprotec.2007.06.06810.1016/j.jmatprotec.2007.06.068 ↗
26. 10.1016/j.msea.2007.12.04610.1016/j.msea.2007.12.046 ↗
27. 10.1016/j.actamat.2014.02.00310.1016/j.actamat.2014.02.003 ↗
28. 10.1016/j.corsci.2013.06.01910.1016/j.corsci.2013.06.019 ↗
29. 10.1016/j.mseb.2011.05.02810.1016/j.mseb.2011.05.028 ↗
30. 10.1002/(SICI)1527-2648(199909)1:1<11::AID-ADEM11>3.0.CO;2-N10.1002/(SICI)1527-2648(199909)1:1<11::AID-ADEM11>3.0.CO;2-N ↗
31. 10.1016/S0257-8972(03)00163-410.1016/S0257-8972(03)00163-4 ↗
32. 10.1016/S0257-8972(99)00325-410.1016/S0257-8972(99)00325-4 ↗
33. 10.1016/j.actamat.2016.02.02610.1016/j.actamat.2016.02.026 ↗
34. 10.1016/j.jmst.2013.02.00510.1016/j.jmst.2013.02.005 ↗
35. 10.1016/j.actbio.2014.07.00510.1016/j.actbio.2014.07.005 ↗
36. 10.4028/www.scientific.net/MSF.706-709.50410.4028/www.scientific.net/MSF.706-709.504 ↗
37. 10.1016/j.apsusc.2009.07.03410.1016/j.apsusc.2009.07.034 ↗
38. 10.1557/jmr.2009.032310.1557/jmr.2009.0323 ↗
39. 10.1016/j.actamat.2014.07.06510.1016/j.actamat.2014.07.065 ↗
40. Using high-pressure torsion to process an aluminum–magnesium nanocomposite through diffusion bonding
41. 10.1016/j.msec.2014.12.04910.1016/j.msec.2014.12.049 ↗
42. 10.1016/j.scriptamat.2014.01.03610.1016/j.scriptamat.2014.01.036 ↗
43. 10.1016/j.matdes.2016.01.07210.1016/j.matdes.2016.01.072 ↗
44. 10.1016/j.scriptamat.2016.03.02310.1016/j.scriptamat.2016.03.023 ↗
45. 10.1016/j.electacta.2010.02.06810.1016/j.electacta.2010.02.068 ↗
46. 10.1016/j.msea.2014.09.01110.1016/j.msea.2014.09.011 ↗
47. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
48. 10.1557/jmr.2014.1810.1557/jmr.2014.18 ↗
49. 10.1016/j.jallcom.2011.06.09410.1016/j.jallcom.2011.06.094 ↗
50. 10.1016/j.corsci.2009.10.01610.1016/j.corsci.2009.10.016 ↗
51. 10.1002/adem.20050007110.1002/adem.200500071 ↗
52. Development and biocompatibility of a novel corrodible fluoride-coated magnesium–calcium alloy with improved degradation kinetics and adequate mechanical properties for cardiovascular applications10.1002/jbm.a.32582 ↗
53. 10.1016/j.mser.2014.10.00110.1016/j.mser.2014.10.001 ↗
54. 10.1016/j.corsci.2011.09.00510.1016/j.corsci.2011.09.005 ↗
55. 10.1016/j.jallcom.2013.02.12810.1016/j.jallcom.2013.02.128 ↗
56. 10.1016/j.biomaterials.2006.01.01710.1016/j.biomaterials.2006.01.017 ↗
57. 10.1016/j.scriptamat.2007.01.00610.1016/j.scriptamat.2007.01.006 ↗
58. 10.1557/jmr.2015.23910.1557/jmr.2015.239 ↗
59. 10.1016/j.actamat.2005.09.02310.1016/j.actamat.2005.09.023 ↗
60. 10.1016/j.matdes.2015.07.02910.1016/j.matdes.2015.07.029 ↗
61. 10.1016/j.actamat.2015.12.05010.1016/j.actamat.2015.12.050 ↗
62. Review of creep behaviour of AZ91 magnesium alloy produced by different technologies10.1179/026708301101510483 ↗
63. Acute oral toxicity evaluations of some zinc(II) complexes derived from 1-(2-salicylaldiminoethyl)piperazine Schiff bases in rats
64. 10.1016/j.corsci.2009.10.01810.1016/j.corsci.2009.10.018 ↗
65. 10.1016/j.msea.2015.07.08610.1016/j.msea.2015.07.086 ↗
66. 10.1016/j.jallcom.2011.01.11610.1016/j.jallcom.2011.01.116 ↗
67. 10.1557/jmr.2007.023310.1557/jmr.2007.0233 ↗
68. 10.1016/j.jallcom.2010.09.12210.1016/j.jallcom.2010.09.122 ↗
69. 10.4028/www.scientific.net/MSF.350-351.1910.4028/www.scientific.net/MSF.350-351.19 ↗
70. 10.1002/adem.20160032610.1002/adem.201600326 ↗
71. 10.1016/j.elecom.2010.05.01110.1016/j.elecom.2010.05.011 ↗
72. 10.1016/j.corsci.2011.05.05010.1016/j.corsci.2011.05.050 ↗
73. 10.1002/adem.20050001310.1002/adem.200500013 ↗
74. 10.1016/j.corsci.2012.01.02110.1016/j.corsci.2012.01.021 ↗
75. 10.1361/1059949041753310.1361/10599490417533 ↗
76. 10.1016/j.actamat.2015.10.00410.1016/j.actamat.2015.10.004 ↗
77. 10.1179/147842209X1255942816780510.1179/147842209X12559428167805 ↗
78. 10.1002/adem.20140043410.1002/adem.201400434 ↗
79. 10.1016/j.corsci.2012.05.01910.1016/j.corsci.2012.05.019 ↗
80. 10.1016/j.msea.2014.04.04610.1016/j.msea.2014.04.046 ↗