Crystal orientation and surface morphology of face-centered-cubic metal thin films deposited upon single-crystal ceramic substrates using pulsed laser deposition

Cu, Pt, Ag, and Au were deposited on (100)-oriented ceramic substrates (SrTiO₃, LaAlO₃, and MgO). Over a wide range of temperatures (room temperature to 600 °C), Cu films were (100)-oriented and exhibited cube-on-cube epitaxy. Epitaxial Pt(100) films were obtained only at high temperature; oriented Pt(111) films were obtained at lower temperatures. Ag and Au were never obtained as purely (100)-oriented samples, although the amount of (100)-film increased with increasing temperature. Three-dimensional islands formed for all metals at higher temperatures, while flatter film surfaces developed at lower temperatures. At any given temperature, the surface roughness of films on SrTiO₃(100) increased in the order Pt < Cu < Au < Ag. The variations in film structural characteristics are described well by considering the metals’ (i) surface/interfacial energies, (ii) surface energy anisotropies, and (iii) surface diffusion coefficients. Flat, epitaxial growth is promoted by low-energy interfaces, low surface energy anisotropies, and slow surface diffusion.