Enhancement in physical properties of barium hexaferrite with substitution
Source abstract
Abstract
M-type barium hexaferrite powders were synthesized using modified Pechini sol gel auto combustion method. The powder samples were heat treated at 900 °C for 5 h and were subjected to the structural, thermal, dielectric, magnetic, and optical studies. X-ray powder diffraction patterns show the formation of pure phase of M-type hexaferrite. Thermal analysis reveals that the weight loss of precursor becomes constant after 680 °C. The presence of two prominent peaks near 430 and 580 cm−1in Fourier transform infrared spectroscopy spectra indicates the formation of M-type hexaferrites. TheM—Hcurve has been used to study the magnetic behavior. The maximum value of coercivity is found forx= 0.41, which is higher than that of the pure barium hexaferrite. The band gap dependency on composition was studied using UV–Vis NIR spectroscopy. It was found that the dielectric constant is high at low frequency and decreases with an increase in frequency. Hexagonal structure of hexaferrite is visualized in transmission electron images.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties and Synthesis of Ferrites · Multiferroics and related materials · Electromagnetic wave absorption materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. 10.1016/S0167-577X(99)00238-410.1016/S0167-577X(99)00238-4 ↗
2. 10.1111/j.1551-2916.2007.01690.x10.1111/j.1551-2916.2007.01690.x ↗
3. 10.1007/s10832-007-9206-310.1007/s10832-007-9206-3 ↗
4. Electrical and magnetic properties of rare earth substituted strontium hexaferrites
5. 10.1016/j.matlet.2011.10.05210.1016/j.matlet.2011.10.052 ↗
6. 10.1016/j.jallcom.2014.01.05910.1016/j.jallcom.2014.01.059 ↗
7. 10.1016/j.snb.2013.09.03510.1016/j.snb.2013.09.035 ↗
8. 10.1016/j.ceramint.2012.12.08910.1016/j.ceramint.2012.12.089 ↗
9. 10.1016/j.jmmm.2006.02.09610.1016/j.jmmm.2006.02.096 ↗
10. 10.1134/S199507801205011410.1134/S1995078012050114 ↗
11. 10.1016/S0304-8853(01)01141-610.1016/S0304-8853(01)01141-6 ↗
12. Effect of aluminum substitution on microwave absorption properties of barium hexaferrite10.1063/1.2135412 ↗
13. 10.1016/S0921-4526(02)01712-X10.1016/S0921-4526(02)01712-X ↗
14. 10.1016/j.jmatprotec.2006.03.01510.1016/j.jmatprotec.2006.03.015 ↗
15. 10.1007/s10948-013-2180-x10.1007/s10948-013-2180-x ↗
16. 10.1016/j.matchemphys.2013.05.06310.1016/j.matchemphys.2013.05.063 ↗
17. 10.1007/s11665-013-0484-410.1007/s11665-013-0484-4 ↗
18. 10.1088/0022-3727/44/43/43530610.1088/0022-3727/44/43/435306 ↗
19. 10.1007/s11051-012-0881-x10.1007/s11051-012-0881-x ↗
20. 10.1021/jp064628t10.1021/jp064628t ↗
21. Structural, magnetic, and optical properties of zinc- and copper-substituted nickel ferrite nanocrystals10.1007/s10948-012-1655-5 ↗
22. 10.1016/j.jmmm.2009.11.00910.1016/j.jmmm.2009.11.009 ↗
23. 10.1016/j.cej.2007.05.04610.1016/j.cej.2007.05.046 ↗
24. 10.1016/S0025-5408(00)00382-210.1016/S0025-5408(00)00382-2 ↗
25. 10.1007/s11664-013-2900-910.1007/s11664-013-2900-9 ↗
26. Structural and dielectric spectroscopy studies of the M-type barium strontium hexaferrite alloys (BaxSr1–xFe12O19)
27. 10.1016/j.ceramint.2013.11.00510.1016/j.ceramint.2013.11.005 ↗
28. 10.1016/j.matchemphys.2009.10.04810.1016/j.matchemphys.2009.10.048 ↗
29. 10.1016/j.jmmm.2008.02.03410.1016/j.jmmm.2008.02.034 ↗
30. 10.1016/j.jmmm.2012.08.03810.1016/j.jmmm.2012.08.038 ↗
31. 10.1109/TMAG.2011.214457110.1109/TMAG.2011.2144571 ↗
32. A strong magneto-optical activity in rare-earth La3+ substituted M-type strontium ferrites10.1063/1.3587181 ↗
33. 10.1007/s10948-013-2167-710.1007/s10948-013-2167-7 ↗
34. 10.1103/PhysRevLett.105.25720110.1103/PhysRevLett.105.257201 ↗
35. 10.1103/PhysRevLett.112.25390110.1103/PhysRevLett.112.253901 ↗
36. 10.1016/j.jmmm.2011.02.01210.1016/j.jmmm.2011.02.012 ↗
37. 10.1039/c4ra00448e10.1039/c4ra00448e ↗
38. 10.1016/j.ceramint.2003.12.17310.1016/j.ceramint.2003.12.173 ↗
39. 10.1007/s10853-012-6727-110.1007/s10853-012-6727-1 ↗
40. 10.1016/j.jmmm.2013.04.06610.1016/j.jmmm.2013.04.066 ↗
41. 10.1016/j.jmmm.2003.08.00110.1016/j.jmmm.2003.08.001 ↗
42. 10.1016/j.physb.2010.11.09410.1016/j.physb.2010.11.094 ↗
43. 10.1016/j.jallcom.2011.05.09110.1016/j.jallcom.2011.05.091 ↗
44. 10.1109/TMAG.2009.202604410.1109/TMAG.2009.2026044 ↗
45. 10.1016/j.ssc.2006.03.02010.1016/j.ssc.2006.03.020 ↗
46. Effect of divalent cation substitution in the magnetoplumbite structured BaFe12O19 system
47. 10.1016/j.jallcom.2009.09.02410.1016/j.jallcom.2009.09.024 ↗
48. Microwave dielectric properties of M-Type barium, calcium and strontium hexaferrite substituted with Co and Ti
49. 10.1016/j.jmmm.2011.07.01610.1016/j.jmmm.2011.07.016 ↗
50. 10.4028/www.scientific.net/KEM.264-268.122910.4028/www.scientific.net/KEM.264-268.1229 ↗
51. 10.1007/s10853-006-6676-710.1007/s10853-006-6676-7 ↗
52. 10.1016/j.physb.2014.09.00310.1016/j.physb.2014.09.003 ↗
53. Determination of the thickness and optical constants of transparent indium-doped ZnO thin films by the envelope method
54. 10.1016/S0304-8853(97)01141-410.1016/S0304-8853(97)01141-4 ↗
55. 10.1016/j.jmmm.2011.06.07010.1016/j.jmmm.2011.06.070 ↗
56. 10.1016/S0304-8853(01)00988-X10.1016/S0304-8853(01)00988-X ↗
57. 10.1007/s10948-011-1323-110.1007/s10948-011-1323-1 ↗
58. 10.1007/BF0058487610.1007/BF00584876 ↗
59. 10.1007/s10971-009-2052-910.1007/s10971-009-2052-9 ↗
60. 10.1016/j.jallcom.2013.01.08110.1016/j.jallcom.2013.01.081 ↗
61. 10.1016/j.jmmm.2011.08.05910.1016/j.jmmm.2011.08.059 ↗
62. Er3+-substituted W-type barium ferrite: Preparation and electromagnetic properties10.1016/S1002-0721(09)60211-8 ↗