Bioactive comparison of a borate, phosphate and silicate glass
Source abstract
Abstract
A borate glass, phosphate glass, and silicate glass were converted to hydroxyapatite (HA) by soaking the substrates in a solution of K2HPO4with a pH value of 9.0 at 37 °C. The weight loss of the substrates was studied as a function of time. Unlike the silicate glasses, the reaction processes of the borate glasses and phosphate glasses were bulk dissolution. X-ray diffraction and scanning electron microscopy revealed an initially amorphous product that subsequently crystallized to HA. The data suggest good bioactive characteristics for the borate and phosphate glass and the potential use of them as a favorable template for bone-tissue formation.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Dental Implant Techniques and Outcomes · Dental materials and restorations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. A comparative study between in vivo bone ingrowth and in vitro apatite formation on Na2O–CaO–SiO2 glasses.10.1016/S0142-9612(02)00511-2 ↗
2. 10.1002/(SICI)1097-4636(199710)37:1<114::AID-JBM14>3.0.CO;2-G10.1002/(SICI)1097-4636(199710)37:1<114::AID-JBM14>3.0.CO;2-G ↗
3. 10.1111/j.1151-2916.1992.tb04470.x10.1111/j.1151-2916.1992.tb04470.x ↗
4. 19. Han X. Reaction of sodium calcium borate glass to form hydroxyapatite and preliminary evolution of hydroxyapatite microspheres used to absorb and separate proteins. Master's Thesis, University of Missouri-Rolla, Rolla, MO (2002).
5. Preparation of porous Ca10(PO4)6(OH)2 and β–Ca3(PO4)2.10.1111/j.1151-2916.2000.tb01434.x ↗
6. Novel bioactive materials with different mechanical properties.10.1016/S0142-9612(03)00044-9 ↗
7. Synergistic reinforcement of in situ hardening calcium phosphate composite scaffold for bone tissue engineering.10.1016/S0142-9612(03)00608-2 ↗
8. 10.1016/j.biomaterials.2003.09.09410.1016/j.biomaterials.2003.09.094 ↗
9. 10.1016/S0022-3093(00)00245-310.1016/S0022-3093(00)00245-3 ↗
10. 10.1016/S0142-9612(03)00200-X10.1016/S0142-9612(03)00200-X ↗
11. 10.1002/(SICI)1097-4636(200007)51:1<37::AID-JBM6>3.0.CO;2-T10.1002/(SICI)1097-4636(200007)51:1<37::AID-JBM6>3.0.CO;2-T ↗
12. 10.1016/j.biomaterials.2003.07.00110.1016/j.biomaterials.2003.07.001 ↗
13. 10.1023/A:102598830154210.1023/A:1025988301542 ↗
14. 10.1016/0022-3093(89)90495-X10.1016/0022-3093(89)90495-X ↗
15. 10.1023/A:102297162982210.1023/A:1022971629822 ↗
16. 10.1023/A:102349972858810.1023/A:1023499728588 ↗
17. 10.1023/B:JMSM.0000032821.32577.fc10.1023/B:JMSM.0000032821.32577.fc ↗
18. 10.1016/S0142-9612(03)00547-710.1016/S0142-9612(03)00547-7 ↗
19. Transformation of borate glasses into biologically useful materials.
20. 10.1016/S0022-3093(98)00784-410.1016/S0022-3093(98)00784-4 ↗
21. 20. Richard M.N. Reaction of a borate glass with K2HPO4 solutions. Master's Thesis, University of Missouri-Rolla, MO (2000).