Fabrication of nanocomposites through diffusion bonding under high-pressure torsion

Megumi Kawasaki, Jae-Kyung Han, Dong-Hyun Lee, Jae-il Jang, Terence G. Langdon

Journal of Materials Research· Volume 33· Issue 18

Abstract

This report summarizes a recent study demonstrating simple and rapid synthesis of a new Al–Mg alloy system and ultimately synthesizing a metal matrix nanocomposite, which was achieved by processing stacked disks of the two dissimilar metals by conventional high-pressure torsion (HPT) processing. The synthesized Al–Mg alloy system exhibits exceptionally high hardness through rapid diffusion bonding and simultaneous nucleation of intermetallic phases with increased numbers of HPT turns through 20, and improved plasticity was demonstrated by increasing strain rate sensitivity in the alloy system after post-deformation annealing. An additional experiment demonstrated that the alternate stacking of high numbers of dissimilar metal disks may produce a faster metal mixture during HPT. Metal combinations of Al–Cu, Al–Fe, and Al–Ti were processed by the same HPT procedure from separate pure metals to examine the feasibility of the processing technique. The microstructural analysis confirmed the capability of HPT for the formation of heterostructures across the disk diameters in these processed alloy systems. The HPT processing demonstrates a considerable potential for the joining and bonding of dissimilar metals at room temperature and the expeditious fabrication of a wide range of new metal systems.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advanced materials and composites · Aluminum Alloys Composites Properties · Metal and Thin Film Mechanics

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (64)

Show source-provided references
1. 10.1016/j.actamat.2010.11.06310.1016/j.actamat.2010.11.063 ↗
2. 10.1002/adem.20100027010.1002/adem.201000270 ↗
3. 10.1007/s11661-999-0051-710.1007/s11661-999-0051-7 ↗
4. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
5. Microstructural evolution in commercial purity aluminum during high-pressure torsion
6. 10.1016/j.actamat.2008.04.01310.1016/j.actamat.2008.04.013 ↗
7. 10.1002/adem.20150052010.1002/adem.201500520 ↗
8. 10.1016/j.msea.2015.03.06810.1016/j.msea.2015.03.068 ↗
9. 10.1016/0956-7151(91)90054-510.1016/0956-7151(91)90054-5 ↗
10. 10.1016/j.msea.2015.02.01110.1016/j.msea.2015.02.011 ↗
11. 10.1073/pnas.132406911110.1073/pnas.1324069111 ↗
12. 10.1016/j.actamat.2013.02.04210.1016/j.actamat.2013.02.042 ↗
13. 10.1002/adem.20160057810.1002/adem.201600578 ↗
14. 10.1557/JMR.2002.000210.1557/JMR.2002.0002 ↗
15. 10.1126/science.125594010.1126/science.1255940 ↗
16. 10.1016/j.msea.2016.12.10610.1016/j.msea.2016.12.106 ↗
17. 10.1007/s10853-015-9143-510.1007/s10853-015-9143-5 ↗
18. 10.1080/21663831.2014.93582110.1080/21663831.2014.935821 ↗
19. 10.1016/j.nimb.2009.09.05310.1016/j.nimb.2009.09.053 ↗
20. 10.1016/S0921-5093(99)00764-910.1016/S0921-5093(99)00764-9 ↗
21. 10.1016/j.jallcom.2011.07.01110.1016/j.jallcom.2011.07.011 ↗
22. Local investigations of the mechanical properties of ultrafine grained metals by nanoindentations
23. 10.1016/j.pmatsci.2018.02.00210.1016/j.pmatsci.2018.02.002 ↗
24. 10.1016/j.msea.2015.03.04210.1016/j.msea.2015.03.042 ↗
25. 10.2320/matertrans.M200943110.2320/matertrans.M2009431 ↗
26. 10.1016/j.scriptamat.2014.09.01410.1016/j.scriptamat.2014.09.014 ↗
27. 10.1016/j.msea.2011.07.04010.1016/j.msea.2011.07.040 ↗
28. 10.1016/j.cirp.2015.05.00610.1016/j.cirp.2015.05.006 ↗
29. 10.1557/jmr.2015.25710.1557/jmr.2015.257 ↗
30. 10.1016/j.msea.2013.07.03310.1016/j.msea.2013.07.033 ↗
31. 10.1007/s10853-013-7201-410.1007/s10853-013-7201-4 ↗
32. 10.1016/j.msea.2007.08.07010.1016/j.msea.2007.08.070 ↗
33. 10.2320/matertrans.MB20091410.2320/matertrans.MB200914 ↗
34. 10.1038/nmat118010.1038/nmat1180 ↗
35. 10.1007/s11661-015-3151-610.1007/s11661-015-3151-6 ↗
36. 10.1016/j.matlet.2016.06.03510.1016/j.matlet.2016.06.035 ↗
37. 10.1016/j.msea.2017.12.06510.1016/j.msea.2017.12.065 ↗
38. 10.1080/21663831.2015.106054310.1080/21663831.2015.1060543 ↗
39. New hierarchy of solute architecture breaks strength ceiling in a nanocrystalline aluminium alloy
40. 10.1016/j.msea.2017.12.09510.1016/j.msea.2017.12.095 ↗
41. 10.1126/science.118586610.1126/science.1185866 ↗
42. 10.1002/adem.20120026110.1002/adem.201200261 ↗
43. 10.1557/jmr.2013.3910.1557/jmr.2013.39 ↗
44. 10.1007/s10853-013-7687-910.1007/s10853-013-7687-9 ↗
45. 10.1016/j.msea.2016.12.06710.1016/j.msea.2016.12.067 ↗
46. 10.1016/S0965-9773(98)00157-310.1016/S0965-9773(98)00157-3 ↗
47. 10.1016/j.msea.2012.08.02910.1016/j.msea.2012.08.029 ↗
48. 10.1016/j.actamat.2013.08.01810.1016/j.actamat.2013.08.018 ↗
49. 10.1016/j.msea.2017.02.03210.1016/j.msea.2017.02.032 ↗
50. 10.1016/S1359-6462(01)00955-110.1016/S1359-6462(01)00955-1 ↗
51. 10.1107/S0365110X6500513310.1107/S0365110X65005133 ↗
52. 10.1590/1980-5373-mr-2017-021810.1590/1980-5373-mr-2017-0218 ↗
53. 10.1016/j.pmatsci.2008.03.00210.1016/j.pmatsci.2008.03.002 ↗
54. 10.1038/419887a10.1038/419887a ↗
55. 10.1016/j.actamat.2012.10.03810.1016/j.actamat.2012.10.038 ↗
56. 10.1016/j.scriptamat.2012.07.03010.1016/j.scriptamat.2012.07.030 ↗
57. 10.1080/21663831.2017.134320810.1080/21663831.2017.1343208 ↗
58. 10.1007/s11661-010-0400-610.1007/s11661-010-0400-6 ↗
59. 10.1007/s11661-003-0259-x10.1007/s11661-003-0259-x ↗
60. 10.1016/j.msea.2011.09.03910.1016/j.msea.2011.09.039 ↗
61. 10.1557/jmr.2015.23910.1557/jmr.2015.239 ↗
62. 10.1016/S0921-5093(00)00919-910.1016/S0921-5093(00)00919-9 ↗
63. 10.1016/S1359-6462(03)00395-610.1016/S1359-6462(03)00395-6 ↗
64. 10.1016/j.msea.2012.01.08010.1016/j.msea.2012.01.080 ↗