Fabrication and properties of HfB2–MoSi2 composites produced by hot pressing and spark plasma sintering
Source abstract
Abstract
HfB2–15 vol% MoSi2 composites were produced from powder mixtures and densified through different techniques, namely hot pressing and spark plasma sintering. Dense materials were obtained at 1900 °C by hot pressing and at 1750 °C by spark plasma sintering. Microstructure and mechanical properties were compared. The most relevant result was for high-temperature strength: independent of the processing technique, the flexural strength in air at 1500 °C was higher than 500 MPa.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. 10.1002/adem.20040001610.1002/adem.200400016 ↗
2. 10.1016/S0921-5093(00)00771-110.1016/S0921-5093(00)00771-1 ↗
3. 10.1557/JMR.2004.046010.1557/JMR.2004.0460 ↗
4. 10.1111/j.1151-2916.1999.tb02156.x10.1111/j.1151-2916.1999.tb02156.x ↗
5. 8. Medri V. and Bellosi A. : Microstructure and properties of hot pressed hafnium diboride with silicon nitride as sintering aid (unpublished).
6. 10.1023/B:JMSC.0000041689.90456.af10.1023/B:JMSC.0000041689.90456.af ↗
7. 10.1007/978-94-007-0868-6_2010.1007/978-94-007-0868-6_20 ↗
8. Materials for ultrahigh temperature structural applications.
9. 10.1179/00325890222500704110.1179/003258902225007041 ↗
10. 10.1557/JMR.2005.011110.1557/JMR.2005.0111 ↗
11. Novel assemblies via spark plasma sintering.
12. 10.1016/S0955-2219(99)00129-610.1016/S0955-2219(99)00129-6 ↗
13. 10.1023/B:JMSC.0000041686.21788.7710.1023/B:JMSC.0000041686.21788.77 ↗
14. 10.1007/BF0035680410.1007/BF00356804 ↗
15. 10.1007/BF0001339310.1007/BF00013393 ↗
16. Chamberlain · 2003 · Vol. 153 · 299
17. Levin · 1969 · 98
18. 10.1023/B:JMSC.0000041690.06117.3410.1023/B:JMSC.0000041690.06117.34 ↗
19. 4. Clougherty E.V. , Kalishi D. , and Peters E.T. : Research and development of refractory oxidation resistant diborides, Technical Report AFML-TR-68-190 (1968).