Measurement of the loss tangent of low-density polyethylene with a nanoindentation technique

This paper describes experimental measurements of the linear viscoelastic behavior of the surface of low-density (LD) polyethylene in contact with a pyramidal Berkovich diamond indenter. The experiments were carried out at two different temperatures, 15.9 and 27.2 °C, between frequencies of 0.1 and 800 Hz. Using the shift of the loss tangent between the two temperatures at frequencies lower than 20 Hz and an Arrhenius equation, an activation energy of 105 ± 2 kJ/mol was obtained. This value is in good agreement with the bulk value of the a relaxation of LD polyethylene reported in the literature.