Synthesis, characterization, and properties of nanophase TiO₂

Ultrafine-grained, nanophase samples of TiO₂ (rutile) were synthesized by the gas-condensation method and subsequent in situ compaction. The samples were studied by a number of techniques, including transmission electron microscopy, Vickers microharness measurements, and positron annihilation spectroscopy, as a function of sintering temperature. The nanophase compacts with average initial grain sizes of 12 nm were found to densify rapidly above 500 °C, with only a small increase in grain size. The hardness values obtained by this method are comparable to or greater than those for coarser-grained compacts, but are achieved at temperatures 400 to 600 °C lower than conventional sintering temperatures and without the need for sintering aids.