CoCrFeMnNi high-entropy alloys reinforced with Laves phase by adding Nb and Ti elements
Source abstract
Abstract
Laves phase plays a positive role in improving the strength of high-entropy alloys (HEAs); Nb and Ti elements have potential to promote Laves phase formation in some HEAs. For improving the strength of the face-centered cubic (FCC) CoCrFeMnNi HEA, a series of (CoCrFeMnNi)100−xNbx(atomic ratio:x= 0, 4, 8, 12, 16) and (CoCrFeMnNi)100−xTix(atomic ratio:x= 0, 2, 4, 6, 8, 12) HEAs were prepared by melting. The effects of Nb and Ti on the microstructure evolution and compressive properties of the CoCrFeMnNi HEAs were investigated. For (CoCrFeMnNi)100−xNbxHEAs, the second-phase (Laves and σ phase) volume fraction increased from 0 to 42%. The yield strength also increased gradually from 202 to 1010 MPa. However, the fracture strain decreased from 60% (no fracture) to 12% with increasing Nb content. For (CoCrFeMnNi)100−xTixHEAs, the yield strength increased from 202 to 1322 MPa. The Laves phase volume fraction also increased from 0 to 27%. However, the fracture strain decreased from 60% (no fracture) to 7.5% with increasing Ti content. Addition of Nb and Ti has a good effect on improving the strength of FCC CoCrFeMnNi HEA.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Additive Manufacturing Materials and Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (57)
Show source-provided references
1. 10.1016/j.jmst.2017.11.00710.1016/j.jmst.2017.11.007 ↗
2. 10.1016/j.intermet.2013.05.00210.1016/j.intermet.2013.05.002 ↗
3. Laves-phase formation criterion for high-entropy alloys
4. Criteria for predicting the formation of single-phase high-entropy alloys
5. 10.1038/srep0620010.1038/srep06200 ↗
6. 10.1063/1.358722810.1063/1.3587228 ↗
7. Microstructure of Al1.3CrFeNi eutectic high entropy alloy and oxidation behavior at 1000 °C
8. 10.1038/nature1798110.1038/nature17981 ↗
9. 10.1016/j.matlet.2014.09.10010.1016/j.matlet.2014.09.100 ↗
10. 10.1016/j.jallcom.2015.09.15310.1016/j.jallcom.2015.09.153 ↗
11. 10.1016/j.jmst.2016.09.01610.1016/j.jmst.2016.09.016 ↗
12. 10.1016/j.actamat.2016.06.06310.1016/j.actamat.2016.06.063 ↗
13. 10.1016/j.jallcom.2017.11.07510.1016/j.jallcom.2017.11.075 ↗
14. 10.1016/j.intermet.2015.01.00410.1016/j.intermet.2015.01.004 ↗
15. 10.1016/j.jallcom.2014.12.15710.1016/j.jallcom.2014.12.157 ↗
16. 10.1016/j.matdes.2016.01.03310.1016/j.matdes.2016.01.033 ↗
17. 10.1016/j.actamat.2016.11.01610.1016/j.actamat.2016.11.016 ↗
18. 10.1016/j.jallcom.2016.10.01410.1016/j.jallcom.2016.10.014 ↗
19. 10.1557/jmr.2016.44510.1557/jmr.2016.445 ↗
20. Chemical short-range orders and the induced structural transition in high-entropy alloys
21. 10.1016/j.msea.2011.10.11010.1016/j.msea.2011.10.110 ↗
22. 10.1007/s11837-012-0366-510.1007/s11837-012-0366-5 ↗
23. 10.1016/j.actamat.2013.09.03710.1016/j.actamat.2013.09.037 ↗
24. Murty · 2014
25. 10.1016/0022-3093(84)90210-210.1016/0022-3093(84)90210-2 ↗
26. 10.1016/j.matdes.2013.12.04810.1016/j.matdes.2013.12.048 ↗
27. 10.1016/j.pmatsci.2013.10.00110.1016/j.pmatsci.2013.10.001 ↗
28. 10.3390/e1809033310.3390/e18090333 ↗
29. Microstructural development in equiatomic multicomponent alloys
30. 10.1016/j.matdes.2017.08.03010.1016/j.matdes.2017.08.030 ↗
31. 10.1016/j.jallcom.2010.03.07410.1016/j.jallcom.2010.03.074 ↗
32. 10.1016/j.intermet.2013.03.01810.1016/j.intermet.2013.03.018 ↗
33. 10.1016/j.msea.2017.10.08810.1016/j.msea.2017.10.088 ↗
34. 10.1016/S1002-0071(12)60080-X10.1016/S1002-0071(12)60080-X ↗
35. Tsai · 1992
36. 10.1080/21663831.2013.83138210.1080/21663831.2013.831382 ↗
37. 10.1002/adem.20170090810.1002/adem.201700908 ↗
38. 10.1016/j.intermet.2018.04.02310.1016/j.intermet.2018.04.023 ↗
39. 10.1557/mrc.2014.1110.1557/mrc.2014.11 ↗
40. 10.1063/1.273451710.1063/1.2734517 ↗
41. 10.1016/j.matdes.2017.07.05410.1016/j.matdes.2017.07.054 ↗
42. 10.1016/j.actamat.2017.10.05810.1016/j.actamat.2017.10.058 ↗
43. Microstructure and mechanical performance of AlxCoCrCuFeNi high-entropy alloys
44. 10.1016/j.intermet.2006.08.00510.1016/j.intermet.2006.08.005 ↗
45. 10.1080/21663831.2015.112116810.1080/21663831.2015.1121168 ↗
46. 10.1007/s11661-018-4549-810.1007/s11661-018-4549-8 ↗
47. 10.1016/j.msea.2012.06.07510.1016/j.msea.2012.06.075 ↗
48. 10.1002/adem.20030056710.1002/adem.200300567 ↗
49. 10.1002/adem.20070024010.1002/adem.200700240 ↗
50. 10.1016/j.jallcom.2015.10.27910.1016/j.jallcom.2015.10.279 ↗
51. 10.1016/j.intermet.2014.05.01410.1016/j.intermet.2014.05.014 ↗
52. 10.1016/j.msea.2010.07.04910.1016/j.msea.2010.07.049 ↗
53. 10.1016/j.matchemphys.2011.11.02110.1016/j.matchemphys.2011.11.021 ↗
54. 10.1016/j.msea.2017.12.02210.1016/j.msea.2017.12.022 ↗
55. 10.1016/S1003-6326(15)63922-X10.1016/S1003-6326(15)63922-X ↗
56. 10.1016/j.actamat.2016.04.00510.1016/j.actamat.2016.04.005 ↗
57. 10.1016/j.matlet.2016.03.09210.1016/j.matlet.2016.03.092 ↗