Grazing incidence synchrotron x-ray diffraction method for analyzing thin films

A method using synchrotron radiation parallel beam x-ray optics with a small incidence angle α on the specimen and 2Θ-detector scanning is described for depth profiling analysis of thin films. The instrumentation is the same as used for Θ:2Θ synchrotron parallel beam powder diffractometry, except that the specimen is uncoupled from the detector. There is no profile distortion. Below the critical angle for total reflection α_c, the top tens of Angstroms are sampled. Depth profiling is controlled to a few Angstroms using a small α and 0.005° steps. The penetration depth increases to several hundred Angstroms as α approaches α_c. Above α_c there is a rapid increase in penetration depth to a thousand Angstroms or more and the profiling cannot be sensitively controlled. At grazing incidence the peaks are shifted several tenths of a degree by the x-ray refraction and an experimental procedure for calculating the shifts is described. The method is illustrated with an analysis of iron oxide films.