Quantitative evaluation of indentation-induced densification in glass

To estimate the ratio of densification to Vickers indentation volume, three-dimensional images of Vickers indentations on several glasses, including silicate glasses and bulk metallic glass (BMG), were obtained before and after annealing using an atomic force microscope. Large volume recovery of Vickers indentation by annealing was observed for all glasses but BMG. Following previous studies, this recovered volume almost corresponded to the densified volume under a Vickers indenter, and the compositional dependence of densification was discussed. The ratios of densification to the total indentation volume for silica and soda-lime glasses were 92% and 61%, respectively. It was concluded that densification was a general property for silicate glasses and that the ratios of densification to the total indentation volume for all the glasses correlated well with Poisson’s ratios of the glasses.