Morphological Evolution of S-Phase in 2024 Aluminum under Tensile Creep at 448-463 K
Source abstract
Abstract
The morphological evolution behavior of S-phase in 2024 aluminum alloy under uniaxial tensile creep test at 448 and 463 K under 175, 200 and 225 MPa was studied in detail by HRTEM. Results showed that the S-phase was arranged in the zigzag manner, similar to a zebra pattern, under tensile stress at 448-463 K. And it maintained cubic structure, remarkably grew along the tension direction under uniaxial tensile stress, but grew minimally perpendicular to the stress direction. Compared with applied stress, the temperature had a greater effect on the growth of S-phase. The length of S-phase reached 100 ± 20 nm after testing for 24 h at 448 K under 200 MPa and 200 ± 50 nm after testing for 18 h at 463 K under 175 MPa. The S-phase not only grew significantly in length but also coarsened at 463 K, the lamellar structure becoming fuzzy, which caused the alloy to enter the tertiary creep stage, unsuitable for creep-aging forming.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Microstructure and mechanical properties · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. M.C. Holman, Autoclave Age Forming Large Aluminium Aircraft Panels, J. Mech. Work. Technol., 1989, 20(89), p 477-488 (in English)10.1016/0378-3804(89)90055-7 ↗
2. D.M. Hambrick. Age Forming Technology Expanded In An Autoclave. Society of Automotive Engineers. SAE Technical Paper Series 850885, 1985 (in English).10.4271/850885 ↗
3. L. Zhan, J. Lin, and T.A. Dean, A Review of the Development of Creep Age Forming: Experimentation, Modelling and Applications, Int. J. Mach. Tools Manuf, 2011, 51(1), p 1-17 (in English)10.1016/j.ijmachtools.2010.08.007 ↗
4. P.P. Jeunechamps, K.C. Ho, J. Lin, J.P. Ponthot, and T.A. Dean, A Closed Form Technique to Predict Springback in Creep Age-Forming, Int. J. Mech. Sci., 2006, 48(6), p 621-629 (in English)10.1016/j.ijmecsci.2006.01.005 ↗
5. G. Sha, R.K.W. Marceau, X. Gao, B.C. Muddle, and S.P. Ringer, Nanostructure of Aluminium Alloy 2024: Segregation, Clustering and Precipitation Processes, Acta Mater., 2011, 59(4), p 1659-1670 (in English)10.1016/j.actamat.2010.11.033 ↗
6. L.M. Wang, H.M. Flower, and T.C. Lindley, Precipitation of the Ω Phase in 2024 and 2124 Aluminium Alloys, Scr. Mater., 1999, 41(4), p 391-396 (in English)10.1016/S1359-6462(99)00150-5 ↗
7. Y.C. Lin, Y.C. Xia, Y.Q. Jiang, and L.T. Li, Precipitation in Al-Cu-Mg Alloy During Creep Exposure, Mater. Sci. Eng. A, 2012, 556, p 796-800 (in English)10.1016/j.msea.2012.07.069 ↗
8. Y.C. Lin, Y.C. Xia, Y.Q. Jiang, H.M. Zhou, and L.T. Li, Precipitation Hardening of 2024-T3 Aluminium Alloy During Creep Aging, Mater. Sci. Eng. A, 2013, 565(5), p 420-429 (in English)10.1016/j.msea.2012.12.058 ↗
9. Y.C. Lin, Y.-Q. Jiang, Y.-C. Xia, X.-C. Zhang, H.-M. Zhou, and J. Deng, Effects of Creep-Aging Processing on the Corrosion Resistance and Mechanical Properties of an Al-Cu-Mg Alloy, Mater. Sci. Eng. A, 2014, 605(5), p 192-202 (in English)10.1016/j.msea.2014.03.055 ↗
10. Metallic Materials—Creep and Stress-Rupture Test in Tension [S],GB/T2039—1997, ISO, 1997, pp. 132-133
11. Z.R. Liu, J.H. Chen, S.B. Wang, D.W. Yuan, M.J. Yin, and C.L. Wu, The Structure and the Properties of S-Phase in Al-Cu-Mg Alloys, Acta Mater., 2011, 59(19), p 7396-7405 (in English)10.1016/j.actamat.2011.08.009 ↗
12. G. Liu, Y.C. Lin, X.C. Zhang, and Y.Q. Jiang, Effects of Two-Stage Creep-Aging on Precipitates of an Al-Cu-Mg Alloy, Mater. Sci. Eng. A, 2014, 614(5), p 45-53 (in English)
13. Y. Xia, 2024 铝合金的蠕变时效特性研究 (Study on Creep-Aging Characteristics of 2024 Aluminium Alloy). Central South University, 2012 (in Chinese)
14. S.C. Wang and M.J. Starink, Precipitates and Intermetallic Phases in Precipitation Hardening Al-Cu-Mg-(Li) Based Alloys, Metall Rev, 2005, 50(4), p 193-215 (in English)10.1179/174328005X14357 ↗
15. B. Skrotzki, G.J. Shiflet, and E.A. Starke, On the Effect of Stress on Nucleation and Growth of Precipitates in an Al-Cu-Mg-Ag Alloy, Metall. Mater. Trans. A, 1996, 27(11), p 3431-3444 (in English)10.1007/BF02595436 ↗
16. T. Eto, A. Sato, and T. Mori, Stress-Oriented Precipitation of G.P. Zones and θ′ in an Al-Cu Alloy, Acta Metall., 1978, 26(3), p 499-508 (in English)10.1016/0001-6160(78)90175-X ↗
17. F.-S. Xu, J. Zhang, Y.L. Deng, and X.M. Zhang, Precipitation Orientation Effect of 2124 Aluminium Alloy in Creep Aging, Chin. J. Nonferrous Met., 2014, 24(7), p 2067-2071 (in English)10.1016/S1003-6326(14)63313-6 ↗
18. Z.Q. Feng, Y.Q. Yang, B. Huang, M.H. Li, Y.X. Chen, and J.G. Ru, Crystal Substructures of the Rotation-Twinned T (Al20Cu2Mn3) Phase in 2024 Aluminium Alloy, J. Alloys Compd., 2014, 583, p 445-451 (in English)10.1016/j.jallcom.2013.08.200 ↗
19. X. Xu, Y. Zhao, B. Ma, and M. Zhang, Rapid Precipitation of T-Phase in the 2024 Aluminium Alloy via Cyclic Electropulsing Treatment, J. Alloys Compd., 2014, 610, p 506-510 (in English)10.1016/j.jallcom.2014.05.063 ↗