Sodium Hypochlorite Treatment and Nitinol Performance for Medical Devices
Source abstract
Abstract
Processing of nitinol medical devices has evolved over the years as manufacturers have identified methods of reducing surface defects such as inclusions. One recent method proposes to soak nitinol medical devices in a 6% sodium hypochlorite (NaClO) solution as a means of identifying surface inclusions. Devices with surface inclusions could in theory then be removed from production because inclusions would interact with NaClO to form a visible black material on the nitinol surface. To understand the effects of an NaClO soak on performance, we compared as-received and NaClO-soaked nitinol wires with two different surface finishes (black oxide and electropolished). Pitting corrosion susceptibility was equivalent between the as-received and NaClO-soaked groups for both surface finishes. Nickel ion release increased in the NaClO-soaked group for black oxide nitinol, but was equivalent for electropolished nitinol. Fatigue testing revealed a lower fatigue life for NaClO-soaked black oxide nitinol at all alternating strains. With the exception of 0.83% alternating strain, NaClO-soaked and as-received electropolished nitinol had similar average fatigue life, but the NaClO-soaked group showed higher variability. NaClO-soaked electropolished nitinol had specimens with the lowest number of cycles to fracture for all alternating strains tested with the exception of the highest alternating strain 1.2%. The NaClO treatment identified only one specimen with surface inclusions and caused readily identifiable surface damage to the black oxide nitinol. Damage from the NaClO soak to electropolished nitinol surface also appears to have occurred and is likely the cause of the increased variability of the fatigue results. Overall, the NaClO soak appears to not lead to an improvement in nitinol performance and seems to be damaging to the nitinol surface in ways that may not be detectable with a simple visual inspection for black material on the nitinol surface.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Endodontics and Root Canal Treatments · Shape Memory Alloy Transformations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. M.J. Mahtabi, N. Shamsaei, and M.R. Mitchell, Fatigue of Nitinol: The State-of-the-art and Ongoing Challenges, J. Mech. Behav. Biomed. Mater., 2015, 50, p 228–25410.1016/j.jmbbm.2015.06.010 ↗
2. T. Duerig, A. Pelton, and D. Stockel, An Overview of Nitinol Medical Applications, Mater. Sci. Eng. Struct Mater Prop Microstruct. Process., 1999, 273, p 149–16010.1016/S0921-5093(99)00294-4 ↗
3. S.M. Russell, Design Considerations for Nitinol Bone Staples, J. Mater. Eng. Perform., 2009, 18(5–6), p 831–83510.1007/s11665-009-9402-1 ↗
4. A.R. Pelton, J. Fino-Decker, L. Vien, C. Bonsignore, P. Saffari, M. Launey, and M.R. Mitchell, Rotary-Bending Fatigue Characteristics of Medical-Grade Nitinol Wire, J. Mech. Behav. Biomed. Mater., 2013, 27, p 19–3210.1016/j.jmbbm.2013.06.003 ↗
5. S. Sullivan, M. Dreher, J. Zheng, L. Chen, D. Madamba, K. Miyashiro, C. Trepanier, and S. Nagaraja, Effects of Oxide Layer Composition and Radial Compression on Nickel Release in Nitinol Stents, Shape Mem. Superelast., 2015, 1(3), p 319–32710.1007/s40830-015-0028-x ↗
6. Z.J. Bai and H.H. Rotermund, The Intrinsically High Pitting Corrosion Resistance of Mechanically Polished Nitinol in Simulated Physiological Solutions, J. Biomed. Mater. Res. Part B Appl. Biomater., 2011, 99b(1), p 1–1310.1002/jbm.b.31865 ↗
7. S. Shabalovskaya, G. Rondelli, J. Anderegg, J.P. Xiong, and M. Wu, Comparative Corrosion Performance of Black Oxide, Sandblasted, and Fine-Drawn Nitinol Wires in Potentiodynamic and Potentiostatic Tests: Effects of Chemical Etching and Electropolishing, J. Biomed. Mater. Res. Part B Appl. Biomater., 2004, 69b(2), p 223–23110.1002/jbm.b.30006 ↗
8. ASTM F2063-12, Standard Specification for Wrought Nickel-Titanium Shape Memory Alloys for Medical Devices and Surgical Implants, ASTM International, West Conshohocken, 2012
9. M. Rahim, J. Frenzel, M. Frotscher, J. Pfetzing-Micklich, R. Steegmuller, M. Wohlschlogel, H. Mughrabi, and G. Eggeler, Impurity Levels and Fatigue Lives of Pseudoelastic NiTi Shape Memory Alloys, Acta Mater., 2013, 61(10), p 3667–368610.1016/j.actamat.2013.02.054 ↗
10. S.W. Robertson, M. Launey, O. Shelley, I. Ong, L. Vien, K. Senthilnathan, P. Saffari, S. Schlegel, and A.R. Pelton, A Statistical Approach to Understand the Role of Inclusions on the Fatigue Resistance of Superelastic Nitinol Wire and Tubing, J. Mech. Behav. Biomed. Mater., 2015, 51, p 119–13110.1016/j.jmbbm.2015.07.003 ↗
11. M. Urbano, A. Cadelli, F. Sczerzenie, P. Luccarelli, S. Beretta, and A. Coda, Inclusions Size-based Fatigue Life Prediction Model of NiTi Alloy for Biomedical Applications, Shape Mem. Superelast., 2015, 1(2), p 240–25110.1007/s40830-015-0016-1 ↗
12. ASTM E1245–03(2016), Standard Practice for Determining the Inclusion or Second-Phase Constituent Content of Metals by Automatic Image Analysis, ASTM International, West Conshohocken, 2016
13. R. Rokicki, T. Hryniewicz, C. Pulletikurthi, K. Rokosz, and N. Munroe, Towards a Better Corrosion Resistance and Biocompatibility Improvement of Nitinol Medical Devices, J. Mater. Eng. Perform., 2015, 24(4), p 1634–164010.1007/s11665-015-1429-x ↗
14. R. Rokicki, W. Haider, and T. Hryniewicz, Influence of Sodium Hypochlorite Treatment of Electropolished and Magnetoelectropolished Nitinol Surfaces on Adhesion and Proliferation of MC3T3 Pre-Osteoblast Cells, J. Mater. Sci. Mater. Med., 2012, 23(9), p 2127–213910.1007/s10856-012-4696-1 ↗
15. C.C. Lasley, M.R. Mitchell, B.A.Dooley, W.C. Bruchman, and C.P. Warner The Corrosion of Nitinol by Exposure to Decontamination Solutions, in SMST-2003: Proceedings of the International Conference on Shape Memory and Superelastic Technologies( 2004), pp. 375–384.
16. M.K. Lonn, J.M. Metcalf, and B.D. Choules, In Vivo and In Vitro Nitinol Corrosion Properties, Shape Mem. Superelast., 2015, 1(3), p 328–33810.1007/s40830-015-0036-x ↗
17. ASTM F2129–15, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices, ASTM International, West Conshohocken, 2015
18. ASTM E2948–16a, Standard Test Method for Conducting Rotating Bending Fatigue Tests of Solid Round Fine Wire, ASTM International, West Conshohocken, 2016
19. S. Sivan, M. Di Prima, and J.D. Weaver, Effect of Applied Potential on Fatigue Life of Electropolished Nitinol Wires, Shape Mem. Superelast., 2017. doi: 10.1007/s40830-017-0109-010.1007/s40830-017-0109-0 ↗
20. L. Zhu, C. Trépanier, A. Pelton, and J.M. Fino, Oxidation of Nitinol and its Effect on Corrosion Resistance, in ASM Materials and Processes for Medical Devices, 2003, p 156–161
21. B. Clarke, W. Carroll, Y. Rochev, M. Hynes, D. Bradley, and D. Plumley, Influence of Nitinol Wire Surface Treatment on Oxide Thickness and Composition and its Subsequent Effect on Corrosion Resistance and Nickel Ion Release, J. Biomed. Mater. Res. Part A, 2006, 79(1), p 61–7010.1002/jbm.a.30720 ↗
22. M. Di Prima, E. Gutierrez, and J.D. Weaver, The Effect of Fatigue on the Corrosion Resistance of Common Medical Alloys, J. Biomed. Mater. Res. Part B Appl. Biomater., 2016. doi: 10.1002/jbm.b.3373810.1002/jbm.b.33738 ↗
23. E. Berutti, E. Angelini, M. Rigolone, G. Migliaretti, and D. Pasqualini, Influence of Sodium Hypochlorite on Fracture Properties and Corrosion of ProTaper Rotary Instruments, Int. Endod. J., 2006, 39(9), p 693–69910.1111/j.1365-2591.2006.01134.x ↗
24. O.A. Peters, J.O. Roehlike, and M.A. Baumann, Effect of Immersion in Sodium Hypochlorite on Torque and Fatigue Resistance of Nickel-Titanium Instruments, J. Endod., 2007, 33(5), p 589–59310.1016/j.joen.2007.01.007 ↗
25. R.D. Martins, M.G.A. Bahia, and V.T.L. Buono, The Effect of Sodium Hypochlorite on the Surface Characteristics and Fatigue Resistance of ProFile Nickel-Titanium Instruments, Oral Surg. Oral Med. Oral Pathol. Oral Radiol. Endodontol., 2006, 102(4), p E99–E10510.1016/j.tripleo.2006.02.018 ↗
26. E. Pedulla, N.M. Grande, G. Plotino, A. Pappalardo, and E. Rapisarda, Cyclic Fatigue Resistance of Three Different Nickel-Titanium Instruments after Immersion in Sodium Hypochlorite, J. Endod., 2011, 37(8), p 1139–114210.1016/j.joen.2011.04.008 ↗
27. H.S. Topcuoglu, K. Pala, A. Akti, S. Duzgun, and G. Topcuoglu, Cyclic Fatigue Resistance of D-RaCe, ProTaper, and Mtwo Nickel-Titanium Retreatment Instruments After Immersion in Sodium Hypochlorite, Clin. Oral Invest., 2016, 20(6), p 1175–117910.1007/s00784-015-1611-4 ↗
28. R. Guidoin, Y. Marois, Y. Douville, M.W. King, M. Castonguay, A. Traore, M. Formichi, L.E. Staxrud, L. Norgren, P. Bergeron, J.P. Becquemin, J.M. Egana, and P.L. Harris, First-Generation Aortic Endografts: Analysis of Explanted Stentor Devices from the EUROSTAR Registry, J. Endovasc. Ther., 2000, 7(2), p 105–12210.1177/152660280000700205 ↗