Effects of Cooling Rate and Silicon Content on Microstructure and Mechanical Properties of Directional Solidification of Eutectic Al-Si Alloys
Source abstract
Abstract
This study investigates the directional solidification of hypoeutectic aluminum-silicon (Al-Si) alloys, with a focus on the influence of solidification parameters and silicon content (1 to 11 wt.%) on structural and mechanical properties. Among significant conclusions regarding the influence of thermal gradients and cooling rates on the position of the columnar-to-equiaxed transition (CET) and the conditions governing its formation, it can be resumed: CET is observed only under low or negative thermal gradients, with critical values ranging between 2.4 and 2 2.6 C/cm above which, and assuming constant cooling rates, the structure remains entirely columnar. Variations in cooling rate, in turn, have a strong impact on the CET position, while silicon content influence is only significant at lower cooling rates. Relationship between microstructure and mechanical properties of Al-Si alloys was analyzed. As cooling rate and Si content increased, an improvement in microhardness and tensile strength was observed, with maximum tensile strength values ranging from 58.54 MPa measured in the equiaxed zone of an Al-1wt.% Si sample to 188 MPa measured in the columnar zone of an Al-11wt.% Si sample. Mechanical properties were found to be superior in the columnar zones for all measured samples. Eutectic phase showed similar values independently of its placement in columnar or equiaxed zone, but the values were incremented with silicon content while keeping cooling rate constant at 9.5 ºC/min. In effect, measurements of 53.41 and 44.48 kg/ cm2 were obtained for an Al-1wt.%Si alloy sample while 91.4 and 84.5 kg/cm2 values were measured for an Al-11wt.% Si alloy sample, for columnar and equiaxed zone, respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Solidification and crystal growth phenomena · Metallurgy and Material Forming
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (59)
Show source-provided references
1. J.A. Spittle, Columnar to Equiaxed Grain Transition in as Solidified Alloys, Int. Mater. Rev., 2006, 51(4), p 247–269. https://doi.org/10.1179/174328006X10249310.1179/174328006X102493 ↗
2. U. Böyük, N. Maraşlı, E. Çadırlı, H. Kaya, and K. Keşlioğlu, Variations of Microhardness with Solidification Parameters and Electrical Resistivity with Temperature for Al-Cu-Ag Eutectic Alloy, Curr. Appl. Phys., 2012, 12, p 7–10. https://doi.org/10.1016/j.cap.2011.04.01810.1016/j.cap.2011.04.018 ↗
3. Y. Kaygısız and N. Maraşlı, Microstructural, Mechanical and Electrical Characterization of Directionally Solidified Al–Si–Mg Eutectic Alloy, J. Alloys Compd., 2015, 618, p 197. https://doi.org/10.1016/j.jallcom.2014.08.05610.1016/j.jallcom.2014.08.056 ↗
4. H. Kaya, U. Böyük, E. Çadırlı, and N. Maraşlı, Measurements of the Microhardness, Electrical and Thermal Properties of the Al–Ni Eutectic Alloy, Mater. Des., 2012, 34, p 707–712. https://doi.org/10.1016/j.matdes.2011.05.03010.1016/j.matdes.2011.05.030 ↗
5. A.S. Chaus, E.I. Marukovich, and M. Sahul, Microstructure and Properties of Secondary Al-12%Si Alloy Rapidly Quenched from the Melt, J. Mater. Eng. Perform., 2016, 25, p 4776–4784. https://doi.org/10.1007/s11665-016-2367-y10.1007/s11665-016-2367-y ↗
6. S. Engin, U. Büyük, and N. Maraşlı, The Effects of Microstructure and Growth Rate on Microhardness, Tensile Strength, and Electrical Resistivity for Directionally Solidified Al-Ni-Fe Alloys, J. Alloys Compd., 2016, 660, p 23–31. https://doi.org/10.1016/j.jallcom.2015.11.08010.1016/j.jallcom.2015.11.080 ↗
7. E. Çadırlı, Effect of Solidification Parameters on Mechanical Properties of Directionally Solidified Al-Rich Al-Cu Alloys, Met. Mater. Int., 2013, 19, p 411–422. https://doi.org/10.1007/s12540-013-3006-x10.1007/s12540-013-3006-x ↗
8. A.E. Ares, S.F. Gueijman, and C.E. Schvezov, Semi-empirical Modeling for Columnar and Equiaxed Growth of Alloys, J. Cryst. Growth, 2002, 241(1–2), p 235–240. https://doi.org/10.1016/S0022-0248(02)01136-310.1016/S0022-0248(02)01136-3 ↗
9. A.S. Roman, E.R. Ibañez, C.M. Méndez, M. Pedrozo, G.R. Kramer, N.S. Zadorozne, and A.E. Ares, Electrochemical Properties of Diluted Al-Mg Alloys with Columnar-to-Equiaxed Transition, Front. Mater., 2022, 9, 857671. https://doi.org/10.3389/fmats.2022.85767110.3389/fmats.2022.857671 ↗
10. M.D. Peres, C.A. Siqueira, and A. Garcia, Macrostructural and Microstructural Development in Al–Si Alloys Directionally Solidified Under Unsteady-State Conditions, J. Alloys Compd., 2004, 381(1–2), p 168–181. https://doi.org/10.1016/j.jallcom.2004.03.10710.1016/j.jallcom.2004.03.107 ↗
11. J.D. Hunt, Steady State Columnar and Equiaxed Growth of Dendrites and Eutectic, Mater. Sci. Eng., 1984, 65(1), p 75–83. https://doi.org/10.1016/0025-5416(84)90201-510.1016/0025-5416(84)90201-5 ↗
12. A.E. Ares and C.E. Schvezov, Influence of Solidification Thermal Parameters on the Columnar-to-Equiaxed Transition of Aluminum-Zinc and Zinc-Aluminum Alloys, Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2007, 38(7), p 1485–1499. https://doi.org/10.1007/s11661-007-9111-z10.1007/s11661-007-9111-z ↗
13. H. Kaya, U. Böyük, E. Çadırlı, and N. Maraşlı, Influence of Growth Rate on Microstructure, Microhardness, and Electrical Resistivity of Directionally Solidified Al-7 wt% Ni Hypo-Eutectic Alloy, Met. Mater. Int., 2013, 19, p 39. https://doi.org/10.1007/s12540-013-1007-410.1007/s12540-013-1007-4 ↗
14. A. Barros, C. Cruz, A.P. Silva, N. Cheung, A. Garcia, O. Rocha, and A. Moreira, Horizontally Solidified Al–3 wt%Cu–(0.5 wt%Mg) Alloys: Tailoring Thermal Parameters, Microstructure, Microhardness, and Corrosion Behavior, Acta Metall. Sin. (Engl. Lett.), 2019, 32, p 695. https://doi.org/10.1007/s40195-018-0852-z10.1007/s40195-018-0852-z ↗
15. H. Kaya, U. Böyük, S. Engin, E. Çadirli, and N. Maraşli, Measurements of Microhardness and Thermal and Electrical Properties of the Binary Zn-0.7wt.%Cu Hypoperitectic Alloy, J. Electron. Mater., 2010, 39, p 303. https://doi.org/10.1007/s11664-009-1061-310.1007/s11664-009-1061-3 ↗
16. I.A. Magno, F.A. Souza, M.O. Costa, J.M. Nascimento, A.P. Silva, T.S. Costa, and O.L. Rocha, Investigation on Microstructural and Microhardness Evolution in As-Cast and T6/Heat-Treated Samples of a Horizontally Solidified AlSiCu Alloy, Mater. Sci. Technol., 2019, 35, p 791. https://doi.org/10.1016/j.jmrt.2019.06.05410.1016/j.jmrt.2019.06.054 ↗
17. C.R. Barbosa, G.H. Machado, H.M. Azevedo, F.S. Rocha, C. José Filho, and A. A. Pereira O. L. Rocha, Tailoring of Processing Parameters, Dendritic Microstructure, Si/Intermetallic Particles and Microhardness in As-Cast and Heat-Treated Samples of Al7Si0.3Mg Alloy, Met. Mater. Int., 2020, 26, p 370–383.10.1007/s12540-019-00334-y ↗
18. M. Moreira Coutinho, J.I. Saraiva Silva, T. Primo Sousa, and D. Monteiro Rosa, Upward Unsteady-State Solidification of Dilute Al–Nb Alloys: Microstructure Characterization, Microhardness, Dynamic Modulus of Elasticity, Damping, and XRD Analyses, Metals, 2019, 9(6), 713. https://doi.org/10.3390/met906071310.3390/met9060713 ↗
19. S.M. Albuquerque Sousa, G.L. Gouveia, and J.E. Spinelli, The Influence of NbB Inoculation on Dendritic Spacing and Grain Size of an Aluminum 2017 Alloy at Different Cooling Rates, Mater. Sci. Eng. A, 2022, 835, 142680. https://doi.org/10.21203/rs.3.rs-2264563/v110.21203/rs.3.rs-2264563/v1 ↗
20. S. McFadden, D.J. Browne, and C.H.-A. Gandin, A Comparison of Columnar-to-Equiaxed Transition Prediction Methods Using Simulation of the Growing Columnar Front, Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2009, 40, p 662–672. https://doi.org/10.1007/s11661-008-9708-x10.1007/s11661-008-9708-x ↗
21. L. Sturtz, G. Zimmermann, Ch-A. Gandin, B. Billia, N. Mangelinck, H. Nguyen-Thi, D.J. Browne, W. U. Mirihanage, D. Voss, C. Beckermann, A. Karma, ISS-Experiments of Columnar-to-Equiaxed Transition in Solidification Procesing, Conference: 141st TMS 2012 Annual Meeting and Exhibition, Volume: NASA/CP—2012–217466 (2012) p.p 56-62.
22. R. Chen, Y. Shi, Q. Xu, and B. Liu, Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe alloy, Trans. Nonferrous Met. Soc. China, 2014, 24, p 1645–1652. https://doi.org/10.1016/S1003-6326(14)63236-210.1016/S1003-6326(14)63236-2 ↗
23. T.A. Costa, M. Dias, L.G. Gomes, O.L. Rocha, and A. Garcia, Effect of Solution Time in T6 Heat Treatment on Microstructure and Hardness of a Directionally Solidified Al-Si-Cu Alloy, J. Alloys Compd., 2016, 683, p 485–494. https://doi.org/10.1016/j.jallcom.2016.05.09910.1016/j.jallcom.2016.05.099 ↗
24. R.V. Reyes, T.S. Bello, R. Kakitani, T.A. Costa, A. Garcia, N. Cheung, and J.E. SpineLlli, Tensile Properties and Related Microstructural Aspects of Hypereutectic Al-Si Alloys Directionally Solidified under Different Melt Superheats and Transient Heat Flow Conditions, 2017, 685, p 235–243. https://doi.org/10.1016/j.msea.2016.12.09610.1016/j.msea.2016.12.096 ↗
25. J. Strickland, B. Nenchev, and H. Dong, On Directional Dendritic Growth and Primary Spacing—A Review, Crystals, 2020, 10, 627. https://doi.org/10.3390/cryst1007062710.3390/cryst10070627 ↗
26. L. Fernandes Gomes, C.A. Della Rovere, C.L. Kugelmeier, A. Garcia, and J.E. Spinelli, Influences of Alloying Elements and Dendritic Spacing on the Corrosion Behavior of Al-Si-Ag Alloys, J. Mater. Res. Technol., 2021, 15, p 5880–5893. https://doi.org/10.1016/j.msea.2016.12.09610.1016/j.msea.2016.12.096 ↗
27. T.J. Obara, R.O. Minei, R. Kakitani, J.E. Spinelli, A. Garcia, and N. Cheung, Solidification Microstructure and Mechanical Properties of an Al-11wt%Si Alloy Modified with Nb and Sb, J. Phys. Chem. Solids, 2023, 181, 111521. https://doi.org/10.1016/j.jpcs.2023.11152110.1016/j.jpcs.2023.111521 ↗
28. R. Kakitani, A.V. Rodrigues, C. Silva, A. Garcia, and N. Cheung, The Roles of Solidification Cooling Rate and (Mn, Cr) Alloying Elements in the Modification of β-AlFeSi and Hardness Evolvements in Near-Eutectic Al-Si Alloys, J. Alloys Metall. Syst., 2023, 1, 100005. https://doi.org/10.1016/j.jalmes.2023.10000510.1016/j.jalmes.2023.100005 ↗
29. J.A.F. Rodrigues, G.E.M. Santos Júnior, A.D.S. Barros, O.F.L.D. Rocha, and A.L.S. Moreira, Hypoeutectic Al-11wt%Si Alloy: Interfacial Heat Transfer Coefficient, Thermal Variables, Microstructural Parameters and Microhardness, Matéria (Rio de Janeiro), 2022, 26, e13064. https://doi.org/10.1590/S1517-707620210004.136410.1590/S1517-707620210004.1364 ↗
30. R. Kakitani, C.B. Cruz, T.S. Lima, C. Brito, A. Garcia, and N. Cheung, Transient Directional Solidification of a Eutectic Al–Si–Ni Alloy: Macrostructure, Microstructure, Dendritic Growth and Hardness, Materialia, 2019, 7, 100358. https://doi.org/10.1016/j.mtla.2019.10035810.1016/j.mtla.2019.100358 ↗
31. Y. Birol, Impact of Grain Size on Mechanical Properties of AlSi7Mg0.3 Alloy, Mater. Sci. Eng. A, 2013, 559, p 394–400. https://doi.org/10.1016/j.msea.2012.08.11510.1016/j.msea.2012.08.115 ↗
32. E. Samuel, B. Golbahar, A.M. Samuel, H.W. Doty, S. Valtierra, and F.H. Samuel, Effect of Grain Refiner on Tensile and Impact Properties of Cast Al-Si-Mg Alloys, Mater. Des., 2014, 56, p 468–479. https://doi.org/10.1016/j.matdes.2013.11.05810.1016/j.matdes.2013.11.058 ↗
33. S.A. Kori, B.S. Murty, and M. Chakraborty, Development of an Efficient Grain Refiner for Al–7Si Alloy and Its Modification with Strontium, Mater. Sci. Eng. A, 2000, 283(1–2), p 94–104. https://doi.org/10.1016/S0921-5093(99)00794-710.1016/S0921-5093(99)00794-7 ↗
34. K.G. Basavakumar, P.G. Mukunda, and M. Chakraborty, Influence of Grain Refinement and Modification on Microstructure and Mechanical Properties of Al–7Si and Al–7Si–2.5Cu Cast Alloys, Mater Charact, 2008, 59(3), p 283–289. https://doi.org/10.1016/j.matchar.2007.01.01110.1016/j.matchar.2007.01.011 ↗
35. S.P. Nikanorov, V.N. Osipov, and L.I. Regel, Structural and Mechanical Properties of Directionally Solidified Al-Si Alloys, J. Mater. Eng. Perform., 2019, 28, p 7302–7323. https://doi.org/10.1007/s11665-019-04414-310.1007/s11665-019-04414-3 ↗
36. A.E. Ares, S.F. Gueijman, R. Caram, and C.E. Schvezov, Analysis of Solidification Parameters During Solidification of Lead and Aluminum Base Alloys, J. Cryst. Growth, 2005, 275(1–2), p e319–e327. https://doi.org/10.1016/j.jcrysgro.2004.10.11510.1016/j.jcrysgro.2004.10.115 ↗
37. A.E. Ares, S.F. Gueijman, and C.E. Schvezov, An Experimental Investigation of the Columnar-to-Equiaxed Grain Transition in Aluminum-Copper Hypoeutectic and Eutectic Alloys, J. Cryst. Growth, 2010, 312(14), p 2154–2170. https://doi.org/10.1016/j.jcrysgro.2010.04.04010.1016/j.jcrysgro.2010.04.040 ↗
38. D.R. Liu, N. Mangelinck-Noël, C.-A. Gandin, G. Zimmermann, L. Sturz, H. Nguyen Thi and B. Billia, Cafe Simulation of Columnar-to-Equiaxed Transition in Al-7wt%Si Alloys Directionally Solidified Under Microgravity, IOP Conf. Ser.: Mater. Sci. Eng., 2016, 117, 012009. https://doi.org/10.1088/1757-899X/117/1/01200910.1088/1757-899X/117/1/012009 ↗
39. M.A. Martorano and V.B. Biscuola, Predicting the Columnar-to-Equiaxed Transition for a Distribution of Nucleation Undercoolings, Acta Mater., 2009, 57, p 607–615. https://doi.org/10.1016/j.actamat.2008.10.00110.1016/j.actamat.2008.10.001 ↗
40. X. Yao, H. Wang, B. He, and X. Zhou, Modeling of Columnar-to-Equiaxed Transition in Solidified Al-Si Alloys, Mater. Sci. Forum, 2005, 475–479, p 3141–3144. https://doi.org/10.4028/www.scientific.net/MSF.475-479.314110.4028/www.scientific.net/MSF.475-479.3141 ↗
41. C.A. Gandin, Experimental Study of the Transition from Constrained to Unconstrained Growth During Directional Solidification, ISIJ Int., 2000, 40, p 971–979. https://doi.org/10.2355/isijinternational.40.97110.2355/isijinternational.40.971 ↗
42. L.A. Tarshis, J.L. Walker, and J.W. Rutter, Experiments on the Solidification Structure of Alloy Castings, Metall. Trans., 1971, 2, p 2589–2597. https://doi.org/10.1007/BF0281489910.1007/BF02814899 ↗
43. M. Gäumann, R. Trivedi, and W. Kurz, Nucleation Ahead of the Advancing Interface in Directional Solidification, 1997, 226–228, p 763–769. https://doi.org/10.1016/S0921-5093(97)80081-010.1016/S0921-5093(97)80081-0 ↗
44. M.M. Makhlouf and H.V. Guthy, The Aluminum-Silicon Eutectic Reaction: Mechanisms and Crystallography, J. Light. Met., 2001, 1, p 199–218. https://doi.org/10.1016/S1471-5317(02)00003-210.1016/S1471-5317(02)00003-2 ↗
45. Y.-H. Lee, S.H. Kayani, J.-M. Lee, S.-I. Lee, S.-J. Kim, J. Jang, and Y.-H. Cho, Microstructural Refinement in a High Elastic Modulus Al-18Si-8Ni Casting Alloy, J. Alloys Compd., 2024, 1008, p 176580. https://doi.org/10.1016/j.jallcom.2024.17658010.1016/j.jallcom.2024.176580 ↗
46. S.-I. Lee, S.H. Kayani, Y.-H. Lee, B.-J. Kim, K. Euh, J.-I. Lee, and Y.-H. Cho, The effect of Melt Thermal-Rate Treatment on Precipitation Hardening and Mechanical Properties of Al–Si–Mg Alloys, J. Mater. Res. Technol., 2024, 33, p 2704–2717. https://doi.org/10.1016/j.jmrt.2024.09.18610.1016/j.jmrt.2024.09.186 ↗
47. S.H. Kayani, S.-U. Lee, K. Euh, J.-M. Lee, and Y.-H. Cho, Effect of as-Cast Microstructure on Precipitation Behavior and Thermal Conductivity of T5-Treated Al7Si0.35Mg Alloy, J. Alloys Compd., 2024, 976, 173004. https://doi.org/10.1016/j.jallcom.2023.17300410.1016/j.jallcom.2023.173004 ↗
48. G.A. Santos, C. de Moura Neto, W.R. Osório, and A. Garcia, Design of Mechanical Properties of a Zn27Al Alloy Based on Microstructure Dendritic Array Spacing, Mater. Des., 2007, 28(9), p 2425–2430. https://doi.org/10.1016/j.matdes.2006.09.00910.1016/j.matdes.2006.09.009 ↗
49. Y. Sui, Q. Wang, G. Wang, and T. Liu, Effects of Sr Content on the Microstructure and Mechanical Properties of cast Al–12Si–4Cu–2Ni–0.8 Mg Alloys, J. Alloys Compd., 2015, 622, p 572–579. https://doi.org/10.1016/j.jallcom.2014.10.14810.1016/j.jallcom.2014.10.148 ↗
50. B.R. Zhang, M. Garro, and C. Tagliano, Dendrite Arm Spacing in Aluminium Alloy Cylinder Heads Produced by Gravity Semi-permanent Mold, Metall. Sci. Technol., 2003, 21(1), p 3–9.
51. K. Singh and B.P. Kashyap, Effects of Remelting on Variations in Composition, Microstructure, and Hardness Property of Binary Al-Si Alloys, J. Mater. Eng. Perform., 2023, 32(7), p 3043–3056. https://doi.org/10.1007/s11665-022-07323-010.1007/s11665-022-07323-0 ↗
52. J. G. Kaufman, Chapter 4 Aluminum Alloys, in Handbook of Materials Selection, 2002, 1–46.10.1002/9780470172551.ch4 ↗
53. C.R. Barbosa, J.O.M.D. Lima, G.M.H. Machado, H.A.M.D. Azevedo, F.S. Rocha, A.S. Barros, and O.F.L.D. Rocha, Relationship Between Aluminum-Rich/Intermetallic Phases and Microhardness of a Horizontally Solidified AlSiMgFe Alloy, Mater. Res., 2018, 22(1), e20180365. https://doi.org/10.1590/1980-5373-MR-2018-036510.1590/1980-5373-MR-2018-0365 ↗
54. H.M. Azevedo, G.H. Machado, C.R. Barbosa, F.S. Rocha, R.B. Costa, T.A. Costa, and O.L. Rocha, Microstructural Development of an AlNiBi Alloy and Influence of the Transient Horizontal Solidification Parameters on Microhardness, Metall. Mater. Trans. A, 2018, 49, p 4722–4734. https://doi.org/10.1007/s11661-018-4747-410.1007/s11661-018-4747-4 ↗
55. P.R. Goulart, K.S. Cruz, J.E. Spinelli, I.L. Ferreira, N. Cheung, and A. Garcia, Cellular Growth During Transient Directional Solidification of Hypoeutectic Al–Fe Alloys, J. Alloys Compd., 2009, 470(1–2), p 589–599. https://doi.org/10.1016/j.jallcom.2008.03.02610.1016/j.jallcom.2008.03.026 ↗
56. D.W. Callister and D.G. Rethwisch, Magnetic Properties. Materials Science and Engineering, An Introduction, 7th ed. Wiley, Hoboken, 2007, p 19–56
57. Q. Li, J. Li, B. Li et al., Mechanical Properties and Microstructural Evolution of Yb-Modified Al-20%Si Alloy, J. Mater. Eng. Perform., 2018, 27, p 3498–3507. https://doi.org/10.1007/s11665-018-3456-x10.1007/s11665-018-3456-x ↗
58. E. Ghassemali, M. Riestra, T. Bogdanoff, B.S. Kumar, and S. Seifeddine, Hall-Petch Equation in a Hypoeutectic Al-Si Cast Alloy: Grain Size vs. Secondary Dendrite Arm Spacing, Procedia Eng., 2017, 207, p 19–24. https://doi.org/10.1016/j.proeng.2017.10.73110.1016/j.proeng.2017.10.731 ↗
59. A.E. Ares and C.E. Schvezov, The Effect of Structure on Tensile Properties of Directionally Solidified Zn-Based Alloys, J. Cryst. Growth, 2011, 318, p 59–65. https://doi.org/10.1016/j.jcrysgro.2010.11.11210.1016/j.jcrysgro.2010.11.112 ↗