Characterisation of Ceramic-Coated 316LN Stainless Steel Exposed to High-Temperature Thermite Melt and Molten Sodium
Source abstract
Abstract
Currently, stainless steel grade 316LN is the material of construction widely used for core catcher of sodium-cooled fast reactors. Design philosophy for core catcher demands its capability to withstand corium loading from whole core melt accidents. Towards this, two ceramic coatings were investigated for its application as a layer of sacrificial material on the top of core catcher to enhance its capability. Plasma-sprayed thermal barrier layer of alumina and partially stabilised zirconia (PSZ) with an intermediate bond coat of NiCrAlY are selected as candidate material and deposited over 316LN SS substrates and were tested for their suitability as thermal barrier layer for core catcher. Coated specimens were exposed to high-temperature thermite melt to simulate impingement of molten corium. Sodium compatibility of alumina and PSZ coatings were also investigated by exposing samples to molten sodium at 400 °C for 500 h. The surface morphology of high-temperature thermite melt-exposed samples and sodium-exposed samples was examined using scanning electron microscope. Phase identification of the exposed samples was carried out by x-ray diffraction technique. Observation from sodium exposure tests indicated that alumina coating offers better protection compared to PSZ coating. However, PSZ coating provided better protection against high-temperature melt exposure, as confirmed during thermite melt exposure test.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. K. Plevacova, C. Journeau, P. Piluso, and J. Poirier, Eutectic Crystallization in the UO2–Al2O3–HfO2 Ceramic Phase Diagram, Ceram. Int., 2014, 40, p 2565–257310.1016/j.ceramint.2013.08.047 ↗
2. M. Natta, Safety Issues For LMFBRs: Important Features Drawn from the Assessments of Superphénix, in Workshop Proceedings ‘Advanced Nuclear Reactor Safety Issues and Research Needs’, Paris, France, 18–20 Feb 2002, p 103–117
3. A. Jasmin Sudha, K. Velusamy, and P. Chellapandi, A Multi Layer Core Catcher Concept for Future Sodium Cooled Fast Reactors, Ann. Nucl. Energy, 2014, 65, p 253–26110.1016/j.anucene.2013.11.019 ↗
4. J.K. Fink, J.J. Heiberger, R. Kumar, R.A. Blomquist, L. Leibowitz, E.S. Sowa, J.R. Pavlik, and L. Baker Jr., Interactions of Certain Refractory Materials with Sodium, Report No: ANL-75-74, May 197610.2172/7345638 ↗
5. J.K. Fink, J.J. Heiberger, R. Kumar, and R.A. Blomquist, Interactions of Refractories and Reactor Materials with Sodium, Nucl. Technol., 1977, 35, p 656–66210.13182/NT77-A31874 ↗
6. S.A. Meacham, The Compatibility of Refractory Materials with Boiling Sodium, Report No: CONF-760508, 1976
7. J. Jung, A. Reck, and R. Ziegler, The Compatibility of Alumina Ceramics with Liquid Sodium, J. Nucl. Mater., 1983, 119, p 339–35010.1016/0022-3115(83)90213-1 ↗
8. S. Kano, E. Yoshida, Y. Hirakawa, Y. Tachi, H. Haneda, and T. Mitsuhashi, Sodium Compatibility of Ceramics; Liquid Metal Systems, H.U. Borgstedt and G. Frees, Ed., Plenum Press, New York, 1995, p 85–9410.1007/978-1-4615-1977-5_9 ↗
9. M. Alex, V. Balagi, K.R. Prasad, K.P. Sreekumar, and P.V. Ananthapadmanabhan, Plasma Sprayed Alumina Coatings for Radiation Detector Development, PRAMANA J. Phys., 2000, 55(56), p 927–93210.1007/s12043-000-0061-x ↗
10. A. Ravi Shankar, K. Thyagarajan, C.K. Upadhyay, C. Mallika, and U. Kamachi Mudali, Plasma Sprayed Alumina Coating on Inconel 600 for Neutron Detector Application, in Proceedings 6th Asian Thermal Spray Conference(ATSC 2014), 24–26 Nov 2014, Hyderabad, p 202–203
11. H.Y. Kim, J.H. Kim, K.S. Ha, J.H. Song, and J.H. Park, A Proposed Core Catcher System and Thermite Experimental Results, J. Energy Power Eng., 2011, 5, p 1005–1014
12. K.-H. Kanga, R.-J. Park, S.-B. Kim, K.Y. Suh, F.B. Cheung, and J.L. Rempe, Simulant Melt Experiments on Performance of the In-Vessel Core Catcher, Nucl. Eng. Des., 2007, 237, p 1803–181310.1016/j.nucengdes.2007.03.017 ↗
13. Powder Diffraction File-2 (PDF-2) JCPDS-ICDD, PCPDFWIN Version 2.02, May 1999.
14. A. Ravi Shankar, B.J. Babu, R. Sole, U.K. Mudali, and H.S. Khatak, Laser Remelting of Plasma Sprayed Zirconia Based Ceramic Coating for Pyrochemical Reprocessing Applications, Surf. Eng., 2007, 23, p 147–15410.1179/174329407X169485 ↗
15. L. Duraes, B.F.O. Costa, R. Santos, A. Correia, J. Campos, and A. Portugal, Fe2O3/Aluminum Thermite Reaction Intermediate and Final Products Characterization, Mater. Sci. Eng. A, 2007, 465, p 199–21010.1016/j.msea.2007.03.063 ↗
16. W.H. Cook, Corrosion Resistance of Various Ceramics and Cermets to Liquid Metals, Report No: ORNL-2391, May 196010.2172/4142090 ↗