Effect of Microstructural Characteristics on Mechanical Properties of Ferritic Stainless Steel
Source abstract
Abstract
To improve the mechanical properties of hot-rolled ferritic stainless steel (SUS430), the microstructural characteristics of SUS430 were changed using a heating process under various conditions. The hardness of SUS430 decreased upon the increase in the heating temperature to 900 °C, and the hardness increased when the sample was heated to temperatures greater than 900 °C. The high hardness of the sample heated at 1000 °C (H1000 °C) is attributed to the heating time: A high hardness was obtained for a H1000 °C sample that was heated for 1 h (H1000 °C-1h), but this decreased when the heating time was increased to more than 1 h. The high hardness of H1000 °C-1h is caused by the fine Cr23C6 precipitates that are distributed in the sample around the grain boundaries. On the other hand, the large precipitates of Cr23C6 in H1000 °C-12h decrease the hardness. The hardness value of SUS430 is directly attributed to the mechanical properties and the ultimate tensile strength. The tensile strength of H1000 °C-1h was found to be about 200% and 20% higher than the as-received and H1000 °C-12h samples, respectively. Despite the increase in the tensile strength of the H1000 °C-1h sample, the ductility was not found to decrease significantly, for example, the fracture strain was approximately 25%. This occurrence is affected by a severe slip in the ferrite base grain, and the high strength of H1000 °C-1h is influenced by the interruption of the slip by the Cr23C6 precipitates. Unlike the tensile strength, similar fatigue properties were observed for both H1000 °C-1h and H1000 °C-12h, which is associated with the low crack driving force of H1000 °C-12h, caused by the roughness-induced crack closure arising from the large Cr23C6 precipitates.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Microstructure and Mechanical Properties of Steels · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. T. Fujita, Current Progress Temperature in Advanced High Cr Ferritic Steels for High Applications, ISIJ Int., 1992, 32, p 175–18110.2355/isijinternational.32.175 ↗
2. S. Patra and L.K. Signghal, Influence of Hot Band Annealing and Cold Rolling on Texture and Ridging of 430 Stainless Steel Containing Aluminum, Mater. Sci. Appl., 2013, 4, p 70–76
3. N. Saito, M. Mabuchi, M. Nakanishi, I. Shigematsu, G. Yamauchi, and M. Nakamura, Application of Equal Channel Angular Extrusion on Strengthening of Ferritic Stainless Steel, J. Mater. Sci., 2001, 36, p 3229–323210.1023/A:1017990420563 ↗
4. A.K. Lakshminarayanan and V. Balasubramanian, An Assessment of Microstructure, Hardness, Tensile and Impact Strength of Friction Stir Welded Ferritic Stainless Steel Joints, Mater. Des., 2010, 31, p 4592–460010.1016/j.matdes.2010.05.049 ↗
5. C.H. Hsu, C.K. Lin, K.H. Huang, and K.L. Ou, Improvement on Hardness and Corrosion Resistance of Ferritic Stainless Steel via PVD-(Ti, Cr)N Coatings, Surf. Coat. Technol., 2013, 231, p 380–38410.1016/j.surfcoat.2012.05.095 ↗
6. M.B. Cortie and H. Pollak, Embrittlement and Aging at 470 °C in an Experimental Ferritic Stainless Steel Containing 38 wt.% Chromium, Mater. Sci. Eng., A, 1995, 199, p 153–16310.1016/0921-5093(94)09731-3 ↗
7. A. Miyazaki, K. Takao, and O. Furukimi, Effect of Nb on The Proof Strength of Ferritic Stainless Steels at Elevated Temperatures, ISIJ Int., 2002, 42, p 916–92010.2355/isijinternational.42.916 ↗
8. P.J. Grobner, The 885°F (470 °C) Embrittlement of Ferritic Stainless Steels, Metall. Trans., 1973, 4, p 251–26010.1007/BF02649625 ↗
9. X. Zhang, Z. Wen, R. Dou, G. Zhou, and Z. Li, Evolution of Microstructure and Mechanical Properties of Cold-Rolled SUS430 Stainless Steel during a Continuous Annealing Process, Mater. Sci. Eng. A, 2014, 598, p 22–2710.1016/j.msea.2014.01.017 ↗
10. K. Suzuki, S. Asami, and K. Suzuki, Formation of Ridging Related to the Banded Segregation Pattern of Cr and C on Ferritic Stainless Steel Sheet, Trans. ISIJ, 1983, 23, p 731–73710.2355/isijinternational1966.23.731 ↗
11. X. Huang, D. Wang, and Y. Yang, Effect of Precipitation on Intergranular Corrosion Resistance of 430 Ferritic Stainless Steel, J. Iron. Steel Res. Int., 2015, 22, p 1062–106810.1016/S1006-706X(15)30113-8 ↗
12. J.H. Westbrook, Temperature Dependence of the Hardness of Secondary Phases Common in Turbine Bucket Alloys, J. Metal., 1957, 209, p 898–904
13. Y. Yazawa, Y. Kato, and M. Kobayashi, Development of Ti-Bearing High Performance Ferritic Stainless Steels R430XT and RSX-1, Kawasaki Steel Tech. Rep., 1999, 40, p 23–29
14. C.S. Bandara, S.C. Siriwardane, U.I. Dissanayake, R. Dissanayake, Prediction Methods of Stress Life Curves for Various Stress Ratios for Steels in the High Cycle Region, in ACEPS-2013, pp. 75–81.
15. N.B. Fredj, M.B. Nasr, A.B. Rhouma, C. Braham, and H. Sidhom, Fatigue ife Improvements of the AISI, 304 Stainless Steel Ground Surfaces by Wire Brushing, ASM Int., 2004, 13, p 564–574
16. A.M. Sherman, Fatigue Properties of Alloy Steels High Strength-Low Alloy Steels, Metall. Trans. A, 1975, 6, p 1035–104010.1007/BF02645528 ↗
17. M.L. Roessle and A. Fatemi, Strain-Controlled Fatigue Properties of Steels and Some Simple Approximations, Int. J. Fatigue, 2000, 22, p 495–51110.1016/S0142-1123(00)00026-8 ↗
18. A.V. Makarov, E.S. Gorkunov, IYu Malygina, LKh Kogan, R.A. Savrai, and A.L. Osintseva, Eddy-Current Testing of the Hardness, Wear Resistance, and Thickness of Coatings Prepared by Gas–Powder Laser Cladding, Rus. J. Nondestr. Test., 2009, 45, p 797–80510.1134/S1061830909110060 ↗
19. S. Ishihara, Y. Sugai, and A.J. McEvily, On the Distinction Between Plasticity- and Roughness-Induced Fatigue Crack Closure, Metall. Mater. Trans. A, 2012, 43A, p 3086–309610.1007/s11661-012-1121-9 ↗