A Comparative Study of the Microstructure, Mechanical Properties and Corrosion Resistance of Ni- or Fe- Based Composite Coatings by Laser Cladding
Source abstract
Abstract
Ni- and Fe-based composite coatings were laser cladded on 40Cr steel to improve the surface mechanical property and corrosion resistance, respectively. The microstructure and phase composition were analyzed by x-ray diffraction (XRD) and field emission scanning electron microscope (FESEM) equipped with an energy-dispersive spectrometer (EDS). The micro-hardness, tribological properties and electrochemical corrosion behavior of the coatings were evaluated. The results show that the thickness of both the coatings is around 0.7 mm, the Ni-based coating is mainly composed of γ-(Ni, Fe), FeNi3, Ni31Si12, Ni3B, CrB and Cr7C3, and the Fe-based coating is mainly composed of austenite and (Fe, Cr)7C3. Micro-hardness of the Ni-based composite coating is about 960 HV0.3, much higher than that of Fe-based coating (357.4 HV0.3) and the 40Cr substrate (251 HV0.3). Meanwhile, the Ni-based composite coating possesses better wear resistance than the Fe-based coating validated by the worn appearance and the wear loss. Electrochemical results suggested that Ni-based coating exhibited better corrosion resistance than the Fe-based coating. The 40Cr substrate could be well protected by the Ni-based coating.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Additive Manufacturing Materials and Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. H.X. Liu, Q. Xu, C. Wang, and X. Zhang, Corrosion and Wear Behavior of Ni60CuMoW Coatings Fabricated by Combination of Laser Cladding and Mechanical Vibration Processing, J. Alloys Compd., 2015, 621, p 357–36310.1016/j.jallcom.2014.10.030 ↗
2. H.M. Wang and G. Duan, Wear and Corrosion Behavior of Laser Clad Cr3Si Reinforced Intermetallic Composite Coatings, Intermetallics, 2003, 11(8), p 755–76210.1016/S0966-9795(03)00078-5 ↗
3. X.C. Zhang, B.S. Xu, S.T. Tu, F.Z. Xuan, H.D. Wang, and Y.X. Wu, Effect of Spraying Power on the Microstructure and Mechanical Properties of Supersonic Plasma-Sprayed Ni-Based Alloy Coatings, Appl. Surf. Sci., 2008, 254(20), p 6318–632610.1016/j.apsusc.2008.03.148 ↗
4. B. Bouchaud, J. Balmain, G. Bonnet, and F. Pedraza, Optimizing Structural and Compositional Properties of Electrodeposited Ceria Coatings for Enhanced Oxidation Resistance of a Nickel-Based Superalloy, Appl. Surf. Sci., 2013, 268(3), p 218–22410.1016/j.apsusc.2012.12.065 ↗
5. H.X. Li, Y.Y. Qi, Z.D. Li, Z.G. Ji, and X. Wu, ZnO Photoanodes Coated with Ni-Based Nanostructured Electrocatalyst for Water Oxidation, J. Alloys Compd., 2015, 661, p 201–20510.1016/j.jallcom.2015.11.153 ↗
6. L. Ding, S.S. Hu, X. Quan, and J.Q. Shen, Effect of Mo and Nano-Nd2O3 on the Microstructure and Wear Resistance of Laser Cladding Ni-Based Alloy Coatings, Appl. Phys. A, 2016, 122(4), p 1–710.1007/s00339-016-9905-1 ↗
7. E.L. Chen, K.M. Zhang, and J.X. Zou, Laser Cladding of a Mg Based Mg-Gd-Y-Zr Alloy with Al-Si Powders, Appl. Surf. Sci., 2016, 367, p 11–1810.1016/j.apsusc.2016.01.124 ↗
8. F.X. Huang, Z.H. Jiang, X.M. Liu, J.S. Lian, and L. Chen, Microstructure and Properties of Thin Wall by Laser Cladding Forming, J. Mater. Process. Technol., 2009, 209(11), p 4970–497610.1016/j.jmatprotec.2009.01.019 ↗
9. T.M. Yue, H. Xie, X. Lin, H.O. Yang, and G.H. Meng, Solidification Behaviour in Laser Cladding of AlCoCrCuFeNi High-Entropy Alloy on Magnesium Substrates, J. Alloys Compd., 2014, 587, p 588–59310.1016/j.jallcom.2013.10.254 ↗
10. R. Subramanian, S. Sircar, and J. Mazumder, Laser Cladding of Zirconium on Magnesium for Improved Corrosion Properties, J. Mater. Sci., 1991, 26(4), p 951–95610.1007/BF00576771 ↗
11. P.F. Mendez, N. Barnes, K. Bell, S.D. Borle, S.S. Gajapathi, S.D. Guest, H. Izadi, A.K. Gol, and G. Wood, Welding Processes for Wear Resistant Overlays, J. Manuf. Process., 2014, 16(1), p 4–2510.1016/j.jmapro.2013.06.011 ↗
12. D.Z. Wang, Q.W. Hu, and X.Y. Zeng, Influences of Parameters on Microstructures and Mechanical Properties of Cr13Ni5Si2 Based Composite Coating by Laser-Induction Hybrid Cladding, Surf. Coat. Technol., 2015, 280, p 359–36910.1016/j.surfcoat.2015.09.029 ↗
13. Y. Lu, G. Lu, F. Liu, Z. Chen, and K. Tang, Phase-Field Study on the Pre-precipitated Phase of Ordered Intermetallic Compounds in Binary and Ternary Ni-Al Base Alloys, J. Alloys Compd., 2015, 637, p 149–15410.1016/j.jallcom.2015.03.006 ↗
14. K. Liu, Y.J. Li, and J. Wang, In-situ Reactive Fabrication and Effect of Phosphorus on Microstructure Evolution of Ni/Ni-Al Intermetallic Composite Coating by Laser Cladding, Mater. Design, 2016, 105, p 171–17810.1016/j.matdes.2016.05.074 ↗
15. H.H. Sun, M.H. Guo, F.L. Meng, and A.G. Liu, Studies on Hardfaced Overlay of Diamond Grits Reinforced Ni-Based Alloy Fabricated by Laser Cladding, T. Indian I. Metals, 2016, 69(7), p 1369–137610.1007/s12666-015-0668-8 ↗
16. G.D. Río, M.A. Garrido, J.E. Fernández, M. Cadenas, and J. Rodríguez, Influence of the Deposition Techniques on the Mechanical Properties and Microstructure of NiCrBSi Coatings, J. Mater. Process. Technol., 2008, 204(1–3), p 304–312
17. L.X. Cai, H.M. Wang, and C.M. Wang, Corrosion Resistance of Laser Clad Cr-Alloyed Ni2Si/NiSi Intermetallic Coatings, Surf. Coat. Technol., 2003, 176(1), p 294–299
18. Z.K. Weng, A.H. Wang, X.H. Wu, Y.Y. Wang, and Z.X. Yang, Wear Resistance of Diode Laser-Clad Ni/WC Composite Coatings at Different Temperatures, Surf. Coat. Technol., 2016, 304, p 283–29210.1016/j.surfcoat.2016.06.081 ↗
19. J. Nurminen, J. Näkki, and P. Vuoristo, Microstructure and Properties of Hard and Wear Resistant MMC Coatings Deposited by Laser Cladding, Int. J. Refract. Met. Hard Mater., 2009, 27(2), p 472–47810.1016/j.ijrmhm.2008.10.008 ↗
20. L. Venkatesh, I. Samajdar, M. Tak, R.D. Doherty, R.C. Gundakaram, K.S. Prasad, and S.V. Joshi, Microstructure and Phase Evolution in Laser Clad Chromium Carbide-NiCrMoNb, Appl. Surf. Sci., 2015, 357, p 2391–240110.1016/j.apsusc.2015.09.260 ↗
21. D.Y. Lou, D. Liu, C.L. He, P. Bennett, L. Chen, Q.B. Yang, E. Fearon, and G. Dearden, Effect of Cr/C Ratio on Microstructure and Corrosion Performance of Cr3C2-NiCr Composite Fabricated by Laser Processing, J. Mater. Eng. Perform., 2016, 25(1), p 1–810.1007/s11665-015-1843-0 ↗
22. D. Deschuyteneer, F. Petit, M. Gonon, and F. Cambier, Processing and Characterization of Laser Clad NiCrBSi/WC Composite Coatings—Influence of Microstructure on Hardness and Wear, Surf. Coat. Technol., 2015, 283, p 162–17110.1016/j.surfcoat.2015.10.055 ↗
23. F. Arias-González, J.D. Val, R. Comesaña, J. Penide, F. Lusquiños, F. Quintero, A. Riveiro, M. Boutinguiza, and J. Pou, Fiber Laser Cladding of Nickel-Based Alloy on Cast Iron, Appl. Surf. Sci., 2016, 374, p 197–20510.1016/j.apsusc.2015.11.023 ↗
24. A.S. Khanna, S. Kumari, S. Kanungo, and A. Gasser, Hard Coatings Based on Thermal Spray and Laser Cladding, Int. J. Refract. Met. Hard Mater., 2009, 27(2), p 485–49110.1016/j.ijrmhm.2008.09.017 ↗
25. S. Katakam, S. Santhanakrishnan, and N.B. Dahotre, Fe-Based Amorphous Coatings on AISI, 4130 Structural Steel for Corrosion Resistance, JOM, 2012, 64(6), p 709–71510.1007/s11837-012-0338-9 ↗
26. S.D. Sun, D. Fabijanic, A. Ghaderi, M. Leary, J. Toton, S. Sun, M. Brandt, and M. Easton, Microstructure and Hardness Characterisation of Laser Coatings Produced with a Mixture of AISI, 420 Stainless Steel and Fe-C-Cr-Nb-B-Mo Steel Alloy Powders, Surf. Coat. Tech., 2016, 296, p 76–8710.1016/j.surfcoat.2016.03.061 ↗
27. M. Doubenskaia, A.K. Gilmutdinov, and K.Y. Nagulin, Laser Cladding of Metal Matrix Composites Reinforced by Cermet Inclusions for Dry Friction Application at Ambient and Elevated Temperatures, Surf. Coat. Tech., 2015, 276(3), p 696–70310.1016/j.surfcoat.2015.05.044 ↗
28. X.Z. Li, Z.D. Liu, H.C. Li, Y.T. Wang, and B. Li, Investigations on the Behavior of Laser Cladding Ni-Cr-Mo Alloy Coating on TP347H Stainless Steel Tube in HCl Rich Environment, Surf. Coat. Tech., 2013, 232(10), p 627–63910.1016/j.surfcoat.2013.06.048 ↗
29. G.J. Li, J. Li, and X. Luo, Effects of High Temperature Treatment on Microstructure and Mechanical propeRties of Laser-Clad NiCrBSi/WC Coatings on Titanium Alloy Substrate, Mater. Charact., 2014, 98, p 83–9210.1016/j.matchar.2014.10.003 ↗
30. J.L. Chen, J. Li, R. Song, L.L. Bai, J.Z. Shao, and C.C. Qu, Effect of the Scanning Speed on Microstructural Evolution and Wear Behaviors of Laser Cladding NiCrBSi Composite Coatings, Opt. Laser Technol., 2015, 72, p 86–8910.1016/j.optlastec.2015.03.015 ↗
31. X.B. Liu and H.M. Wang, Modification of Tribology and High-Temperature behAvior of Ti-48Al-2Cr-2Nb Intermetallic Alloy by Laser Cladding, Appl. Surf. Sci., 2006, 252(16), p 5735–574410.1016/j.apsusc.2005.07.064 ↗
32. R.J. Klein, D.A. Fischer, and J.L. Lenhart, Thermal and Mechanical Aging of Self-Assembled Monolayers as Studies by Near X-ray Absorption Fine Structure, Langmuir, 2011, 27(20), p 12423–1243310.1021/la202294f ↗
33. G. Chakraborty, C.R. Das, S.K. Albert, A.K. Bhaduri, S. Murugesan, and A. Dasgupta, Effect of Alloy 625 Buffer Layer on Hardfacing of Modified 9Cr-1Mo Steel Using Nickel Base Hardfacing Alloy, J. Mater. Eng. Perform., 2016, 25(4), p 1663–167210.1007/s11665-016-1965-z ↗
34. F. Weng, H.J. Yu, C.Z. Chen, J.L. Liu, L.J. Zhao, J.J. Dai, and Z.H. Zhao, Effect of Process Parameters on the Microstructure Evolution and Wear Property of the Laser Cladding Coatings on Ti-6Al-4V Alloy, J. Alloys Compd., 2017, 692, p 989–99610.1016/j.jallcom.2016.09.071 ↗
35. H. Chen, G.Q. Gou, M.J. Tu, and Y. Liu, Research on the Friction and Wear Behavior at Elevated Temperature of Plasma-Sprayed Nanostructured WC-Co Coatings, J. Mater. Eng. Perform., 2010, 19(1), p 1–610.1007/s11665-009-9411-0 ↗
36. L. Lei, J. Shi, X. Wang, D. Liu, and H.G. Xu, Microstructure and Electrochemical Behavior of Cerium Conversion Coating Modified with Silane Agent on magnesium Substrates, Appl. Surf. Sci., 2016, 376, p 161–17110.1016/j.apsusc.2016.03.150 ↗