Improved Adhesion and Corrosion Resistant Performance of Polyurethane Coatings on Anodized Mg Alloy for Aerospace Applications
Source abstract
Abstract
In the current investigation, we targeted to improve the adhesion and corrosion resistant behavior of AZ31 Mg alloy by executing the two-stage treatment; initially by anodization then followed by the deposition of polyurethane (PU) coatings. The impact of the different anodized layers on the adhesion and corrosion protective performance of PU-coated AZ31 Mg substrates was systematically estimated by various characterization techniques. Surface characterization results revealed the influence of silicate content in the anodization bath on the surface microstructure of anodized layers. Surface wettability of Mg substrates after anodization was significantly improved (nearly 25°), confirming the enhanced surface hydrophilicity, possibly due to the higher surface roughness. From the scratch test results, the PU/A75Si coating exhibited the highest adhesion strength with a critical load of 4.8 ± 0.3, which corresponds to about ten-fold of improvement in comparison to PU/Bare. Corrosion test results confirmed the enhanced corrosion protection behavior of PU/A75Si coatings with higher values of Rct (8.72 × 107 Ω cm2), and Rf (1.881 × 107 Ω cm2) with the lowest values of icorr (2.0120 × 10−10 Acm−2) compared to that of PU/Bare samples. Based on the attained outcomes, it was concluded that the anodized layer could increase the adhesion between the polyurethane coatings and base substrate, which is the necessary factor in enhancing the corrosion resistant behavior of polyurethane coatings on AZ31 Mg substrates.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. M.P. Staiger, A.M. Pietak, J. Huadmai, and G. Dias, Magnesium and Its Alloys as Orthopedic Biomaterials: A Review, Biomaterials, 2006, 27, p 1728–173410.1016/j.biomaterials.2005.10.003 ↗
2. H. Liu, F. Cao, G.L. Song, D. Zheng, Z. Shi, M.S. Dargusch, and A. Atrens, Review of the Atmospheric Corrosion of Magnesium Alloys, J. Mater. Sci. Technol., 2019, 35, p 2003–201610.1016/j.jmst.2019.05.001 ↗
3. X. Tiancai, Y. Yang, X. Peng, J. Song, and F. Pan, Overview of Advancement and Development Trend on Magnesium Alloy, J. Mag. Alloys, 2019, 7, p 536–54410.1016/j.jma.2019.08.001 ↗
4. S. Virtanen, Biodegradable Mg and Mg Alloys: Corrosion and Biocompatibility, Mater. Sci. Eng. B, 2011, 176, p 1600–160810.1016/j.mseb.2011.05.028 ↗
5. M. Esmaily, J.E. Svensson, S. Fajardo, N. Birbilis, G.S. Frankel, S. Virtanen, R. Arrabal, S. Thomas, and L.G. Johansson, Fundamentals and Advances in Magnesium Alloy Corrosion, Prog. Mater Sci., 2017, 89, p 92–19310.1016/j.pmatsci.2017.04.011 ↗
6. S.S. Viswanathan, Review of Rare-Earth-Based Conversion Coatings for Magnesium and Its Alloys, J. Mater. Res. Technol., 2019, 8, p 5012–503510.1016/j.jmrt.2019.08.013 ↗
7. H. Hornberger, S. Virtanen, and A.R. Boccaccini, Biomedical Coatings on Magnesium Alloys—A Review, Acta Biomater., 2012, 8, p 2442–245510.1016/j.actbio.2012.04.012 ↗
8. S.S. Viswanathan, Organic Conversion Coatings for Magnesium and Its Alloys, J. Indus. Eng. Chem., 2019, 75, p 20–3710.1016/j.jiec.2019.03.018 ↗
9. H. Hoche, S. Gro, and M. Oechsner, Development of New PVD Coatings for Magnesium Alloys with Improved Corrosion Properties, Surf. Coat. Technol., 2014, 259, p 102–10810.1016/j.surfcoat.2014.04.038 ↗
10. H.H. Elsentriecy, K. Azumi, and H. Konno, Effects of pH and Temperature on the Deposition Properties of Stannate Chemical Conversion Coatings Formed by the Potentiostatic Technique on AZ91D Magnesium Alloy, Electrochim. Acta, 2008, 53, p 4267–427510.1016/j.electacta.2008.01.009 ↗
11. W. Xue, Q. Jin, Q. Zhu, M. Hua, and Y. Ma, Anti-corrosion Microarc Oxidation Coatings on SiCP/AZ31 Magnesium Matrix Composite, J. Alloys Comp., 2009, 482, p 208–21210.1016/j.jallcom.2009.03.159 ↗
12. N. Ostrowski, B. Lee, N. Enick, B. Carlson, S. Kunjukunju, A. Roy, and P.N. Kumta, Corrosion Protection and Improved Cytocompatibility of Biodegradable Polymeric Layerby-Layer Coatings on AZ31 Magnesium Alloys, Acta Biomater., 2013, 9, p 8704–871310.1016/j.actbio.2013.05.010 ↗
13. X. Luo and X.T. Cui, Electrochemical Deposition of Conducting Polymer Coatings on Magnesium Surfaces in Ionic Liquid, Acta Biomater., 2011, 7, p 441–44610.1016/j.actbio.2010.09.006 ↗
14. S. Shadanbaz and G.J. Dias, Calcium Phosphate Coatings on Magnesium Alloys for Biomedical Applications: A Review, Acta Biomater., 2012, 8, p 20–3010.1016/j.actbio.2011.10.016 ↗
15. D.K. Chattopadhyay and C. Dean, Webster, Thermal Stability and Flame Retardancy of Polyurethanes, Prog. Polym. Sci., 2009, 34, p 1068–113310.1016/j.progpolymsci.2009.06.002 ↗
16. M.M. Rahman, E.Y. Kim, K.T. Lim, and W.K. Lee, Morphology and Properties of Waterborne Polyurethane/CNT Nanocomposite Adhesives with Various Carboxyl Acid Salt Groups, J. Adhes. Sc. Technol., 2009, 23, p 839–85010.1163/156856109X411210 ↗
17. D.K. Chattopadhyay and K.V.S.N. Raju, Structural Engineering of Polyurethane Coatings For High Performance Applications, Prog. Polym. Sci., 2007, 32, p 352–41810.1016/j.progpolymsci.2006.05.003 ↗
18. M.M. Rahman, H.D. Kim, and W.K. Lee, Properties of Cross-Linked Waterborne Polyurethane Adhesives with Modified Melamine: Effect of Curing Time, Temperature, and HMMM Content, Fiber Polym., 2009, 10, p 6–1310.1007/s12221-009-0006-z ↗
19. S. Jiang, S. Cai, Y. Lin, X. Bao, R. Ling, D. Xie, J. Sun, J. Wei, and X. Guohua, Effect of Alkali/Acid Pretreatment on the Topography and Corrosion Resistance of as-Deposited CaP Coating on Magnesium Alloys, J. Alloy. Comp., 2019, 793, p 202–21110.1016/j.jallcom.2019.04.198 ↗
20. P. Zhou, Y. Liu, L. Liu, Yu Baoxing, T. Zhang, and F. Wang, Critical Role of Pretreatment on the Corrosion Resistance of Zr Conversion Coating on 6061 Aluminum Alloy: The Combined Effect of Surface Topography and Potential Difference Between Different Phases, Surf. Coat. Technol., 2019, 377, p 12490410.1016/j.surfcoat.2019.124904 ↗
21. Z. Shi, G.L. Song, and A. Atrens, Influence of the b Phase on the Corrosion Performance of Anodized Coatings on Mg-Aluminum Alloys, Corros. Sci., 2005, 47, p 2760–277710.1016/j.corsci.2004.11.004 ↗
22. L. Chai, Yu Xia, Z. Yang, Y. Wang, and M. Okido, Anodizing of Magnesium Alloy AZ31 in Alkaline Solutions with Silicate Under Continuous Sparking, Corros. Sci., 2008, 50, p 3274–327910.1016/j.corsci.2008.08.038 ↗
23. H.Y. Hsiao, H.C. Tsung, and W.T. Tsai, Anodization of AZ91D Magnesium Alloy in Silicate-Containing Electrolytes1-J3, Surf. Coat. Technol., 2005, 199, p 127–13410.1016/j.surfcoat.2004.12.010 ↗
24. Y. Mizutani, S.J. Kim, and R. Ichino, Anodizing of Mg Alloys in Alkaline Solution, Surf. Coat. Technol., 2003, 161, p 143–14610.1016/S0257-8972(03)00214-7 ↗
25. A.F. Cipriano, J. Lin, C. Miller, A. Lin, M.C.C. Alcaraz, P. Soria, and H. Liu, Anodization of Magnesium for Biomedical Applications—Processing, Characterization, Degradation and Cytocompatibility, Acta Biomater., 2017, 62, p 397–41710.1016/j.actbio.2017.08.017 ↗
26. A. Yabuki and M. Sakai, Anodic Films Formed on Magnesium in Organic, Silicate Containing Electrolytes, Corros. Sci., 2009, 51, p 793–79810.1016/j.corsci.2009.02.001 ↗
27. S. Hiromoto and A. Yamamoto, Control of Degradation Rate of Bio Absorbable Magnesium by Anodization and Steam Treatment, Mater. Sci. Eng. C, 2010, 30, p 1085–109310.1016/j.msec.2010.06.001 ↗
28. A.M. Kumar, M.A. Hussein, A.Y. Adesina, S. Ramakrishna, and N. Al-Aqeeli, Influence of Surface Treatment on PEDOT Coatings: Surface and Electrochemical Corrosion Aspects of Newly Developed Ti Alloy, RSC Adv., 2018, 8, p 19181–1919510.1039/C8RA01718B ↗
29. H. Laouamri, S. Giljean, G. Arnold, M. Kolli, N. Bouaouadja, and M.H. Tuilier, Roughness Influence on the Optical Properties and Scratch Behavior of Acrylic Coating Deposited on Sandblasted Glass, Prog. Org. Coat., 2016, 101, p 400–40610.1016/j.porgcoat.2016.09.014 ↗
30. R.M. Bandeira, J. van Drunen, A.C. Garcia, and G. Tremiliosi-Filho, Influence of the Thickness and Roughness of Polyaniline Coatings on Corrosion Protection of AA7075 Aluminum Alloy, Electrochim. Acta, 2017, 240, p 215–22410.1016/j.electacta.2017.04.083 ↗
31. M.M. Rahman and H.D. Kim, Synthesis and Characterization of Waterborne Polyurethane Adhesives Containing Different Amount of Ionic Groups (I), J. Appl. Polym. Sci., 2006, 102, p 5684–569110.1002/app.25052 ↗
32. G. Christopher, M.A. Kulandainathan, and G. Harichandran, Comparative Study of Effect of Corrosion on Mild Steel with Waterborne Polyurethane Dispersion Containing Graphene Oxide Versus Carbon Black Nanocomposites, Prog. Org. Coat., 2015, 89, p 199–21110.1016/j.porgcoat.2015.09.022 ↗
33. M.M. Rahman, H. Zahir, M. Haq, D.A.A. Shehri, and A.M. Kumar, Corrosion Inhibition Properties of Waterborne Polyurethane/Cerium Nitrate Coatings on Mild Steel, Coatings, 2018, 8, p 3410.3390/coatings8010034 ↗
34. K. Sujeet, Sinha, Scratching of Polymers: Deformation Mapping and Wear Modeling, Tribol. Interface Eng. Ser., 2006, 51, p 124–13510.1016/S0167-8922(06)80042-8 ↗
35. H. Jiang, R. Browning, J.D. Whitcomb, M. Ito, M. Shimouse, T.A. Chang, and H.J. Sue, Mechanical Modeling of Scratch Behavior of Polymeric Coatings on Hard and Soft Substrates, Tribol. Lett., 2010, 37, p 159–16710.1007/s11249-009-9505-8 ↗
36. K.F. Khaled, Electrochemical Evaluation of Environmentally Friendly Cerium Salt as Corrosion Inhibitor for Steel in 3.5% NaCl, Inter. J. Electrochem. Sci., 2013, 8, p 3974–398710.1016/S1452-3981(23)14446-4 ↗
37. Y. Sasikumar, A.M. Kumar, R.S. Babu, M.M. Rahman, L.M. Samyn, and A.L.F. de Barros, Biocompatible Hydrophilic Brushite Coatings on AZX310 and AM50 Alloys for Orthopaedic Implants, J. Mater. Sci. Mater. Med., 2018, 29, p 1–1410.1007/s10856-018-6131-8 ↗
38. A. Madhan Kumar, S. Hwan Kwon, H. Chul Jung, Y. Hee Park, H.J. Kim, and K.S. Shin, Fabrication and Electrochemical Corrosion Behavior of PEO Coatings on Strip-Cast AZ31Mg Alloy in 35% NaCl Solution, ACS Ind. Eng. Chem. Res., 2014, 53, p 9703–971310.1021/ie404329s ↗
39. A. Madhan Kumar, S. Fida Hassan, A.A. Sorour, M. Paramsothy, and M. Gupta, Investigation on the Controlled Degradation and Invitro Mineralization of Carbon Nanotube Reinforced AZ31 Nanocomposite in Simulated Body Fluid, Met. Mater. Int., 2019, 25, p 105–11610.1007/s12540-018-0161-0 ↗
40. A.M. Kumar, M.Y. Khan, R.K. Suleiman, A. Khan, and H. Dafalla, Promising Graphitic Carbon Nitride/MoOx Nanocomposites: For Surface Protective Performance of AA2024 Alloys in Marine Environment, Surf. Coat. Technol., 2019, 374, p 579–59010.1016/j.surfcoat.2019.06.004 ↗
41. X. Lv, X. Li, N. Li, H. Zhang, Y.-z. Zheng, W. Jiaojiao, and X. Tao, ZrO2 Nanoparticle Encapsulation of Graphene Micro Sheets for Enhancing Anticorrosion Performance of Epoxy Coatings, Sur. Coat. Technol., 2019, 358, p 443–45110.1016/j.surfcoat.2018.11.045 ↗
42. J. Khodabakhshi, H. Mahdavi, and F. Najafi, Investigation of Viscoelastic and Active Corrosion Protection Properties of Inhibitor Modified Silica Nanoparticles/Epoxy Nanocomposite Coatings on Carbon Steel, Corros. Sci., 2019, 147, p 128–14010.1016/j.corsci.2018.11.014 ↗
43. X. Liu, G. Chuanjun, Z. Wen, and B. Hou, Improvement of Active Corrosion Protection of Carbon Steel by Water-Based Epoxy Coating with Smart CeO2 Nanocontainers, Prog. Org. Coat., 2018, 115, p 195–20410.1016/j.porgcoat.2017.10.015 ↗
44. A.M. Kumar, A.Y. Adesina, M.A. Hussein, S. Ramakrishna, N. Al-Aqeeli, S. Akhtar, and S. Saravanan, PEDOT/FHA Nanocomposite Coatings on Newly Developed Ti-Nb-Zr Implants: Biocompatibility and Surface Protection Against Corrosion and Bacterial Infections, Mater. Sci. Eng. C, 2019, 98, p 482–49510.1016/j.msec.2019.01.012 ↗
45. Y. Sasikumar, A. Madhan Kumar, R. Suresh Babu, P. Dhaiveegan, and N. Al-Aqeeli, Fabrication of Brushite Coating on AZ91D and AZ31 Alloys by Two-Step Chemical Treatment and Its Surface Protection in Simulated Body Fluid, J. Mater. Eng. Perform., 2019, 54, p 1–13
46. B. Ramezanzadeh, G. Bahlakeh, and M. Ramezanzadeh, Polyaniline-Cerium Oxide (PAni-CeO2) Coated Graphene Oxide for Enhancement of Epoxy Coating Corrosion Protection Performance on Mild Steel, Corros. Sci., 2018, 137, p 111–12610.1016/j.corsci.2018.03.038 ↗
47. M. Behzadnasab, S. Mirabedini, K. Kabiri, and S. Jamali, Corrosion Performance of Epoxy Coatings Containing Silane Treated ZrO2 Nanoparticles on Mild Steel in 3.5% NaCl Solution, Corros. Sci., 2011, 53, p 89–9810.1016/j.corsci.2010.09.026 ↗