Corrosion Inhibition Study of Mg-Nd-Y High Strength Magnesium Alloy Using Organic Inhibitor
Source abstract
Abstract
A study on corrosion inhibition mechanism has been performed on rare earth containing WE43 magnesium alloy in 3.5 wt.% NaCl containing 8-hydroxyquinoline (HQ). After an initial increase in corrosion rate due to the formation of sparingly soluble MgQ2 complex, it was found to decrease owing to inhibition effect of the complex. Scanning electrochemical microscopic analysis showed a decrease in corrosion currents and enhanced resistance to pitting corrosion was observed for WE43 samples in the presence of HQ after an exposure of 48 h. With time, the MgQ2 thus generated formed a protective layer on the Mg alloy surface to prevent further corrosion. The corrosion rate of WE43 samples decreased by ~ 50% in HQ containing medium after a constant exposure of 28 days (from ~ 0.22 mg/cm2 day in no HQ to ~ 0.11 mg/cm2 day in HQ). For the WE43 samples in the presence of HQ, formation of MgO and MgQ2 was detected by x-ray photoelectron spectroscopy and x-ray diffraction. Shallower and smaller pits appeared on the magnesium alloy with HQ in the solution as compared to deeper and larger pits on the samples with no HQ in the solution. The significance of metal-complexing organic agent, hydroxyquinoline, in initial acceleration and subsequent prevention of Mg corrosion via protective MgQ2 complex layer formation is demonstrated.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Hydrogen Storage and Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (32)
Show source-provided references
1. A. Atrens, G.L. Song, M. Liu, Z. Shi, F. Cao, and M.S. Dargusch, Review of Recent Developments in the Field of Magnesium Corrosion, Adv. Eng. Mater., 2015, 17, p 400–45310.1002/adem.201400434 ↗
2. G. Song and A. Atrens, Understanding Magnesium Corrosion—A Framework for Improved Alloy Performance, Adv. Eng. Mater., 2003, 5, p 837–85810.1002/adem.200310405 ↗
3. E. Ghali, W. Dietzel, and K.U. Kainer, General and Localized Corrosion of Magnesium Alloys: A Critical Review, J. Mater. Eng. Perform., 2004, 13, p 7–2310.1361/10599490417533 ↗
4. M. Esmaily, J.E. Svensson, S. Fajardo, N. Birbilis, G.S. Frankel, S. Virtanen, R. Arrabal, S. Thomas, and L.G. Johansson, Fundamentals and Advances in Magnesium Alloy Corrosion, Prog. Mater Sci., 2017, 89, p 92–19310.1016/j.pmatsci.2017.04.011 ↗
5. G. Williams, H.N. McMurray, and R. Grace, Inhibition of Magnesium Localised Corrosion in Chloride Containing Electrolyte, Electrochim. Acta, 2010, 55, p 7824–783310.1016/j.electacta.2010.03.023 ↗
6. N.H. Helal and W.A. Badawy, Environmentally Safe Corrosion Inhibition of Mg-Al-Zn Alloy in Chloride Free Neutral Solutions by Amino Acids, Electrochim. Acta, 2011, 56, p 6581–658710.1016/j.electacta.2011.04.031 ↗
7. O.V. Karavai, A.C. Bastos, M.L. Zheludkevich, M.G. Taryba, S.V. Lamaka, and M.G.S. Ferreira, Localized Electrochemical Study of Corrosion Inhibition in Microdefects on Coated AZ31 Magnesium Alloy, Electrochim. Acta, 2010, 55, p 5401–540610.1016/j.electacta.2010.04.064 ↗
8. I.A. Kartsonakis, S.G. Stanciu, A.A. Matei, E.K. Karaxi, R. Hristu, A. Karantonis, and C.A. Charitidis, Evaluation of the Protective Ability of Typical Corrosion Inhibitors for Magnesium Alloys Towards the Mg ZK30 Variant, Corrs. Sci., 2015, 100, p 194–20810.1016/j.corsci.2015.07.028 ↗
9. D. Huang, J. Hu, G.L. Song, and X. Guo, Inhibition Effect of Inorganic and Organic Inhibitors on the Corrosion of Mg-10Gd-3Y-0.5Zr Alloy in an Ethylene Glycol Solution at Ambient and Elevated Temperatures, Electrochim. Acta, 2011, 56, p 10166–1017810.1016/j.electacta.2011.09.002 ↗
10. D. Seifzadeh, H. Basharnavaz, and A. Bezaatpour, A Schiff Base Compound as Effective Corrosion Inhibitor for Magnesium in Acidic Media, Mater. Chem. Phys., 2013, 138, p 794–80210.1016/j.matchemphys.2012.12.063 ↗
11. T. Ishizaki, J. Hieda, N. Saito, N. Saito, and O. Takai, Corrosion Resistance and Chemical Stability of Super-Hydrophobic Film Deposited on Magnesium Alloy AZ31 by Microwave Plasma-Enhanced Chemical Vapor Deposition, Electrochim. Acta, 2010, 55, p 7094–710110.1016/j.electacta.2010.06.064 ↗
12. H. Gao, Q. Li, Y. Dai, F. Luo, and H.X. Zhang, High Efficiency Corrosion Inhibitor 8-Hydroxyquinoline and Its Synergistic Effect with Sodium Dodecylbenzenesulphonate on AZ91D Magnesium Alloy, Corros. Sci., 2010, 52, p 1603–160910.1016/j.corsci.2010.01.033 ↗
13. Q. Zong, L. Wang, W. Sun, and G. Liu, Active Deposition of bis (8-Hydroxyquinoline) Magnesium Coating for Enhanced Corrosion Resistance of AZ91D Alloy, Corros. Sci., 2014, 89, p 127–13610.1016/j.corsci.2014.08.024 ↗
14. S. Shen, Y. Zuo, and X. Zhao, The Effects of 8-Hydroxyquinoline on Corrosion Performance of a Mg-Rich Coating on AZ91D Magnesium Alloy, Corros. Sci., 2013, 76, p 275–28310.1016/j.corsci.2013.06.050 ↗
15. J. Hu, D. Zeng, Z. Zhang, T. Shi, G.L. Song, and X. Guo, 2-Hydroxy-4-Methoxy-Acetophenone as an Environment-Friendly Corrosion Inhibitor for AZ91D Magnesium Alloy, Corros. Sci., 2013, 74, p 35–4310.1016/j.corsci.2013.04.005 ↗
16. J. Hu, D. Huang, G.L. Song, and X. Guo, The Synergistic Inhibition Effect of Organic Silicate and Inorganic Zn Salt on Corrosion of Mg-10Gd-3Y Magnesium Alloy, Corros. Sci., 2011, 53, p 4093–410110.1016/j.corsci.2011.08.017 ↗
17. L. Yang, Y. Li, B. Qian, and B. Hou, Polyaspartic Acid as a Corrosion Inhibitor for WE43 Magnesium Alloy, J. Mag. Alloys, 2015, 3, p 47–5110.1016/j.jma.2014.12.009 ↗
18. M. Borrel and R.A. Paris, Precipitation Domains and Solubility Products of Some Oxinates and Methyloxinates, Anal. Chim. Acta, 1952, 6, p 389–399 (in French)10.1016/S0003-2670(00)86965-2 ↗
19. S.H. Salleh, S. Thomas, J.A. Yuwono, K. Venkatesan, and N. Birbilis, Enhanced Hydrogen Evolution on Mg(OH)2 Covered Mg Surfaces, Electrochim. Acta, 2015, 161, p 144–15210.1016/j.electacta.2015.02.079 ↗
20. S.K. Panigrahi, W. Yuan, R.S. Mishra, R. Delorme, B. Davis, R.A. Howell, and K. Cho, A Study on the Combined Effect of Forging and Aging in Mg-Y-RE Alloy, Mater. Sci. Eng., A, 2011, 530, p 28–3510.1016/j.msea.2011.08.065 ↗
21. R. Pinto, M.G.S. Ferreira, M.J. Carmezim, and M.F. Montemor, Passive Behavior of Magnesium Alloys (Mg-Zr) Containing Rare-Earth Elements in Alkaline Media, Electrochim. Acta, 2010, 55, p 2482–248910.1016/j.electacta.2009.12.012 ↗
22. H. Ardelean, A. Seyeux, S. Zanna, F. Prima, I. Frateur, and P. Marcus, Corrosion Processes of Mg-Y-Nd-Zr Alloys in Na2SO4 Electrolyte, Corros. Sci., 2013, 73, p 196–20710.1016/j.corsci.2013.03.036 ↗
23. S.V. Lamaka, B. Vaghefinazari, D. Mei, R.P. Petrauskas, D. Hoche, and M.L. Zheludkevich, Comprehensive Screening of Mg Corrosion Inhibitors, Corros. Sci., 2017, 128, p 224–24010.1016/j.corsci.2017.07.011 ↗
24. A. Atrens and W. Dietzel, The Negative Difference Effect and Unipositive Mg+, Adv. Eng. Mater., 2007, 9, p 292–29710.1002/adem.200600275 ↗
25. S. Bender, J. Goellner, A. Heyn, and S. Schmigalla, A New Theory for the Negative Difference Effect in Magnesium Corrosion, Mater. Corros., 2012, 63, p 707–71210.1002/maco.201106225 ↗
26. K.C. Tekin, U. Malayoglu, and S. Shrestha, Electrochemical Behavior of Plasma Electrolytic Oxide Coatings on Rare Earth Element Containing Mg Alloys, Surf. Coat. Technol., 2013, 236, p 540–54910.1016/j.surfcoat.2013.10.051 ↗
27. W. Jin, G. Wu, H. Feng, W. Wang, X. Zhang, and P.K. Chu, Improvement of Corrosion Resistance and Biocompatibility of Rare-Earth WE43 Magnesium Alloy by Neodymium Self-Ion Implantation, Corros. Sci., 2015, 94, p 142–15510.1016/j.corsci.2015.01.049 ↗
28. A.D. King, N. Birbilis, and J.R. Scully, Accurate Electrochemical Measurement of Magnesium Corrosion Rates; A Combined Impedance, Mass-Loss and Hydrogen Collection Study, Electrochim. Acta, 2014, 121, p 394–40610.1016/j.electacta.2013.12.124 ↗
29. V. Shkirskiy, A.D. King, O. Gharbi, P. Volovitch, J.R. Scully, K. Ogle, and N. Birbilis, Revisiting the Electrochemical impedance Spectroscopy of Magnesium with Online Inductively Coupled Plasma Atomic Emission Spectroscopy, ChemPhysChem, 2015, 16, p 536–53910.1002/cphc.201402666 ↗
30. G.R. Argade, K. Kandasamy, S.K. Panigrahi, and R.S. Mishra, Corrosion Behavior of a Friction Stir Processed Rare-Earth Added Magnesium Alloy, Corros. Sci., 2012, 58, p 321–32610.1016/j.corsci.2012.01.007 ↗
31. S. Thomas, J. Izquierdo, N. Birbilis, and R.M. Souto, Possibilities and Limitations of Scanning Electrochemical Microscopy of Mg and Mg Alloys, Corrosion, 2014, 71, p 171–18310.5006/1483 ↗
32. J.R. Lakowicz, Principles of Fluorescence Spectroscopy, 3rd ed., Springer, Singapore, 200610.1007/978-0-387-46312-4 ↗