Effect of Nickel Contents on the Microstructure and Mechanical Properties for Low-Carbon Bainitic Weld Metals
Source abstract
Abstract
Multi-pass weld metals were deposited on Q345 base steel using metal powder-flux-cored wire with various Ni contents to investigate the effects of the Ni content on the weld microstructure and property. The types of the microstructures were identified by optical microscope, scanning electron microscope, transmission electron microscope, and micro-hardness tests. As a focusing point, the lath bainite and lath martensite were distinguished by their compositions, morphologies, and hardness. In particular, a number of black plane facets appearing between lath bainite or lath martensite packets were characterized by laser scanning confocal microscope. The results indicated that with the increase in Ni contents in the range of 0, 2, 4, and 6%, the microstructures in the weld-deposited metal were changed from the domination of the granular bainite to the majority of the lath bainite and/or the lath martensite and the micro-hardness of the weld-deposited metal increased. Meanwhile, the average width of columnar grain displays a decreasing trend and prior austenite grain size decreases while increases with higher Ni content above 4%. Yield strength and ultimate tensile strength decrease, while the reduction in fracture area increases with the decreasing Ni mass fraction and the increasing test temperature, respectively. And poor yield strength in Ni6 specimen can be attributed to elements segregation caused by weld defect. Finally, micro-hardness distribution in correspondence with specimens presents as a style of cloud-map.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Welding Techniques and Residual Stresses · Metal Alloys Wear and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Seamless Steel Pipe and Method for Manufacturing the Same. A1, United States Patent Application, 2013, 0000790
2. B.G. Tang, Challenge on Weld Materials from the Development of Modern Steel and Several Advice, Welding, 2009, 12, p 20–25 (in Chinese)
3. M.K. Graf and H.G. Hillenbrand, High-Strength Large-Diameter Pipe for Long-Distance High Pressure Gas Pipelines, IJOPE, 2004, 14, p 117–121
4. W.W. Bose-Filho, A.L.M. Carvalho, and M. Strangwood, Effects of Alloying Elements on the Microstructure and Inclusion Formation in HSLA Multipass Welds, Mater. Charact., 2007, 58, p 29–3910.1016/j.matchar.2006.03.004 ↗
5. D.P. Fairchild, M.L. Macia, N.V. Bangaru, and J.Y. Koo, Girth Welding Development for X120 Linepipe, IJOPE, 2004, 14, p 1–3
6. G.M. Evans and N. Bailey, Metallurgy of Basic Weld Metal, Abington Publishing, Cambridge, 1997, p 178–17910.1533/9781845698850 ↗
7. V.T.T. Miihkinen and D.V. Edmonds, Microstructural Examination of Two Experimental High-Strength Bainitic Low-Alloy Steels Containing Silicon, Mater. Sci. Technol., 1987, 3, p 423–431
8. P.T. Oldland, C.W. Ramsay, D.K. Matlock, and D.L. Olson, Significant Features of High-Strength Weld Metal Microstructures, Weld. J., 1989, 68, p 159–168
9. A.F. Gourgues, H.M. Flower, and T.C. Lindley, Electron Backscattering Differaction Study of Acicular Ferrite, Bainite and Martensite Steel Microstructures, Mater. Sci. Technol., 2000, 16, p 28–40
10. J.H. Park, H.K.D.H. Bhadeshia, L. Karlsson, and E. Keehan, Coalesced Bainite by Isothermal Transformation of Reheated Weld Metal, Sci. Technol. Weld. Join., 2008, 13, p 593–59710.1179/136217108X338926 ↗
11. C.Y. Wang, Y. Chang, J. Yang, K.M. Zhao, and H. Dong, The Combines Effect of Hot Deformation Plus Quenching and Partitioning Treatment on Martensite Transformation of Low Carbon Alloyed Steel, Acta Metall. Sin., 2015, 51, p 913–919 (in Chinese)
12. S.G. Park, K.H. Lee, K.D. Min, M.C. Kim, and B.S. Lee, Characterization of Phase and Misorientations on Tempered Bainitic/Martensite Ni-Cr-Mo Low Alloy RPV Steel with Various Ni Content, Met. Mater. Int., 2013, 19, p 49–5410.1007/s12540-013-1009-2 ↗
13. Z.Y. Zhang and R.A. Farrar, Columnar Grain Development in C-Mn-Ni Low-Alloy Weld Metals and the Influence of Nickel, J. Mater. Sci., 1995, 30, p 5581–558810.1007/BF00356690 ↗
14. S. Patra, S.M. Hasan, N. Narasaiah, and D. Chakrabarti, Mater. Sci. Eng., A, 2012, 538, p 145–15510.1016/j.msea.2011.12.114 ↗
15. F.G. Caballero, H.K.D.H. Bhadeshia, K.J.A. Mawella, D.G. Jones, and P. Brown, Design of novel high strength bainitic steels: Part 1, Mater. Sci. Technol., 2001, 17, p 512–51610.1179/026708301101510348 ↗
16. F.G. Caballero, M.K. Miller, C. Garcia-Mateo, C. Capdevila, and C. Garcia de Andres, Phase transformation tool for the design of advanced steels, JOM, 2008, 60, p 16–2110.1007/s11837-008-0159-z ↗
17. Quintana MA, Babu SS, Major J, Dallam C, James M. Weld Metal Toughness-Sources of Variation, Proceedings of the 8th International Pipeline Conference IPC, 2010, p 1–810.1115/IPC2010-31402 ↗
18. N. Isaati, D. Jorge-Badiola, M.L. Taheri, and P. Uranga, Microstructural Features Controlling Mechanical Properties in Nb-Mo Microalloyed Steels Part I: Yield Strength, Metall. Mater. Trans. A, 2014, 45A, p 4960–497110.1007/s11661-014-2450-7 ↗
19. X.D. Li, C.J. Shang, C.C. Han, Y.R. Fan, and J.B. Sun, Influence of Necklace-Type M-A Constituent on Impact Toughness and Fracture Mechanism in the Heat Affected Zone of X100 Pipeline Steel, Acta Metall. Sin., 2016, 52, p 1025–1035
20. V. Chaudhari, H.P. Ritzmann, G. Wwllnitz et al., German Gas Pipeline First to Use New Generation Line Pipe, Oil Gas J., 1995, 1, p 40–47
21. E. Keehan, L. Karlsson, H.K.D.H. Bhadeshia, and M. Thuvander, Three-Dimensional Analysis of Coalesced Bainite Using Focused Ion Beam Tomography, Mater. Charact., 2008, 59, p 877–88210.1016/j.matchar.2007.07.011 ↗
22. H.S. Fang, J.J. Wang, Z.G. Yang, C.M. Li, X.Z. Bo, and Y.K. Zhen, Bainitic Transformation, Science Press, Beijing, 1999, p 100–104
23. Wang Z. Study on Microstructure and Mechanical Property in Different Metal Materials, Master thesis, 2013, p 22–25
24. X. Li, X. Ma, and S.V. Subramanian, Influence of Prior Austenite Grain Size on Martensite–Austenite Constituent and Toughness in the Heat Affected Zone of 700 MPa High Strength Linepipe Steel, Mater. Sci. Eng., 2014, 616, p 141–14710.1016/j.msea.2014.07.100 ↗
25. Y.H. Tan and Y.X. Ma, New Morphology of Martensite, Metallurgical Industry Press, Beijing, 2014, p 42–52
26. Y.H. Tan and Y.X. Ma, New Morphology of Martensite, Metallurgical Industry Press, Beijing, 2014, p 53–54
27. X.L. Wan, R. Wei, and K.M. Wu, Effect of Acicular Ferrite Formation on Grain Refinement in the Coarse-Grained Region of Heat Affected Zone, Mater. Charact., 2010, 61, p 726–73110.1016/j.matchar.2010.04.004 ↗
28. X.L. Wan, K.M. Wu, G. Huang, and R. Wei, In Situ Observations of the Formation of Fine-Grained Mixed Microstructures of Acicular Ferrite and Bainite in the Simulated Coarse-Grained Heated-Affected Zone, Steel Res., 2014, 2, p 243–25010.1002/srin.201200313 ↗
29. N. Hansen, Hall-Petch Relation and Boundary Strengthening, Scr. Mater., 2004, 51, p 801–80610.1016/j.scriptamat.2004.06.002 ↗
30. X. Mao, X. Huo, X. Sun, and Y. Chai, Strengthening Mechanisms of a New 700 MPa Hot Rolled Ti-Microalloyed Steel Produced by Compact Strip Production, J. Mater. Process. Technol., 2010, 210, p 1660–166610.1016/j.jmatprotec.2010.05.018 ↗
31. Y.J. Yan, R. Cao, W.S. Du, Y. Peng, Z.L. Tian, and J.H. Chen, Tensile Fracture Tests of a 980 MPa High Strength Steel at Various Temperatures, J. Mater. Sci. Eng., 2009, 27, p 246–249