Effects of HIP Temperature on the Microstructural Evolution and Property Restoration of a Ni-Based Superalloy
Source abstract
Abstract
The effects of hot isostatic pressing (HIP) temperature on the evolution of microstructural characteristics around the creep cavities were investigated using five different soaking temperatures during HIP. The restoration of microstructural and material properties under these HIP schedules followed by the same rejuvenation heat treatment (RHT) procedure was then evaluated. The results showed that HIP temperature played a dominant role in the cavity healing process, determining the evolution features of cavities and hence the extending ratio of rupture life. With gradually increasing the adopted HIP temperature, the cavity healing behaviors were revealed. Concentrically oriented N-type γ′ rafting structure in the vicinity of the healing cavity was observed at an appropriate soaking temperature. The driving force for the cavity healing was considered to be the chemical potential gradient induced by the stress gradient field around the cavity. The appropriate HIP schedule followed by RHT process significantly improved the rupture life of damaged alloy, and the extending ratio varied with the adopted HIP temperature.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · High Entropy Alloys Studies · Metal Alloys Wear and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. M.J. Donachie and S.J. Donachie, Superalloys: A Technical Guide, 2nd ed., ASM International, Materials Park, OH, 200210.31399/asm.tb.stg2.9781627082679 ↗
2. T.M. Pollock and S. Tin, Nickel-Based Superalloys for Advanced Turbine Engines: Chemistry, Microstructure and Properties, J. Propul. Power, 2006, 22(2), p 361–37410.2514/1.18239 ↗
3. N. Ejaz, M. Mansoor, and I. Salam, Effect of High Temperature Exposure on the Microstructure of Udimet-500 Super Alloy, J. Mater. Sci., 2010, 45(16), p 4507–451710.1007/s10853-010-4546-9 ↗
4. A. Koul and R. Castillo, Assessment of Service Induced Microstructural Damage and its Rejuvenation in Turbine Blades, Metall. Mater. Trans. A, 1988, 19(8), p 2049–206610.1007/BF02645208 ↗
5. R.C. Reed, Superalloys: Fundamentals and Applications, Cambridge University Press, Cambridge, 200610.1017/CBO9780511541285 ↗
6. M. Tanaka and R. Kato, The Effect of Heat Treatments on the Creep-Rupture Properties of a Wrought Ni-Cr Heat-Resistant Alloy at 973 K, J. Mater. Sci., 2010, 45(15), p 4029–403510.1007/s10853-010-4481-9 ↗
7. A. Baldan, Rejuvenation Procedures to Recover Creep Properties of Nickel-Base Superalloys by Heat Treatment and Hot Isostatic Pressing Techniques, J. Mater. Sci., 1991, 26(13), p 3409–342110.1007/BF00557126 ↗
8. E. Lvova and D. Norsworthy, Influence of Service-Induced Microstructural Changes on the Aging Kinetics of Rejuvenated Ni-Based Superalloy Gas Turbine Blades, J. Mater. Eng. Perform., 2001, 10(3), p 299–31210.1361/105994901770345015 ↗
9. E. Lvova, A Comparison of Aging Kinetics of New and Rejuvenated Conventionally Cast GTD-111 Gas Turbine Blades, J. Mater. Eng. Perform., 2007, 16(2), p 254–26410.1007/s11665-007-9046-y ↗
10. C. Persson and P. Persson, Evaluation of Service-Induced Damage and Restoration of Cast Turbine Blades, J. Mater. Eng. Perform., 1993, 2(4), p 565–56910.1007/BF02661742 ↗
11. T. Maccagno, A. Koul, J. Immarigeon, L. Cutler, R. Allem, and G.L. Espérance, Microstructure, Creep Properties, and Rejuvenation of Service-Exposed Alloy 713C Turbine Blades, Metall. Mater. Trans. A, 1990, 21(12), p 3115–312510.1007/BF02647308 ↗
12. R.A. Stevens and P.E.J. Flewitt, Intermediate Regenerative Heat Treatments for Extending the Creep Life of the Superalloy IN-738, Mater. Sci. Eng. A, 1981, 50(2), p 271–28410.1016/0025-5416(81)90186-5 ↗
13. H. Atkinson and S. Davies, Fundamental Aspects of Hot Isostatic Pressing: An Overview, Metall. Mater. Trans. A, 2000, 31(12), p 2981–300010.1007/s11661-000-0078-2 ↗
14. F.B. Swinkels, D.S. Wilkinson, E. Arzt, and M.F. Ashby, Mechanisms of Hot-Isostatic Pressing, Acta Metall., 1983, 31(11), p 1829–184010.1016/0001-6160(83)90129-3 ↗
15. A. Baldan, Recovery of the Creep Resistance of a Conventionally Cast Nickel-Base Superalloy, J. Mater. Sci. Lett., 1992, 11(19), p 1319–132110.1007/BF00742190 ↗
16. J.X. Yang, Q. Zheng, X.F. Sun, H.R. Guan, and Z.Q. Hu, Morphological Evolution of [Gamma]’ Phase in K465 Superalloy During Prolonged Aging, Mater. Sci. Eng. A, 2007, 457(1–2), p 148–15510.1016/j.msea.2006.12.041 ↗
17. Y. Xie, M. Wang, G. Zhang, and M. Chang, Analysis of Superalloy Turbine Blade Tip Cracking During Service, Eng. Fail. Anal., 2006, 13(8), p 1429–143610.1016/j.engfailanal.2005.07.022 ↗
18. J.X. Yang, Q. Zheng, X.F. Sun, H.R. Guan, and Z.Q. Hu, Morphological Evolution of MC Carbide in K465 Superalloy, J. Mater. Sci., 2006, 41(19), p 6476–647810.1007/s10853-006-0684-5 ↗
19. Z.Y. Pei, W. Han, G. Zhao, X.F. Chen, J.T. Li, and Y.W. Tian, Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy, J. Iron. Steel Res. Int., 2009, 16(6), p 70–7410.1016/S1006-706X(10)60030-1 ↗
20. M. Qian and J.C. Lippold, Investigation of Grain Refinement During a Rejuvenation Heat Treatment of Wrought Alloy 718, Mater. Sci. Eng. A, 2007, 456(1–2), p 147–15510.1016/j.msea.2006.11.161 ↗
21. C.T. Sims, N.S. Stoloff, and W.C. Hagel, Superalloy II, Wiley, New York, 1986
22. S.P. Timoshenko and J.N. Goodier, Theory of Elasticity, 3rd ed., McGraw-Hill, New York, 1970
23. T. Ichitsubo, D. Koumoto, M. Hirao, K. Tanaka, M. Osawa, T. Yokohawa, and H. Harada, Rafting Mechanism for Ni-Base Superalloy Under External Stress: Elastic or Elastic-Plastic Phenomena?, Acta Mater., 2003, 51(14), p 4033–404410.1016/S1359-6454(03)00224-6 ↗
24. F.R.N. Nabarro, Rafting in Superalloys, Metall. Mater. Trans. A, 1996, 27(3), p 513–53010.1007/BF02648942 ↗