Corrosion Resistance and Color Properties of Anodized Ti-6Al-4V

In this research, color anodizing of Ti-6Al-4V alloy was performed in phosphoric acid solution of 0.4 M concentration and within 30 s in different voltages (10-120 V) of a DC power supply. The effect of anodizing voltages on the color and thickness of anodized layers on Ti-6Al-4V alloy surface was surveyed. Thickness and refractive index of layers were measured by spectrophotometery and reflectance curves. According to the results, thickness of layers increased with increasing anodizing voltage and was in the range of 38-167 nm. Also the refractive index of anodic film was approximately constant at about 2 and increased inconsiderably with increasing anodizing voltage. Corrosion resistance of the anodized samples in 20 and 50 V was surveyed in physiological solutions of Ringer’s solution, Artificial Saliva solution, and Ringer’s + 150 mM H2O2 solution at the temperature of 37 °C by potentiodynamic polarization method. The anodized sample in 50 V indicated lower corrosion rate than the non-anodized sample as well as the sample which was anodized in 20 V in all solutions. The non-anodized sample indicated the highest corrosion rate of about 0.25 μA cm−2.