Wear Characteristics and Mechanisms of H13 Steel with Various Tempered Structures
Source abstract
Abstract
Wear tests of H13 steel with various tempering microstructures were performed under atmospheric conditions at room temperature (RT), 200 °C, and 400 °C. The wear characteristics and wear mechanisms of various tempered microstructures of the steel were focused by investigating the structure, morphology, and composition of the worn surfaces. Under atmospheric conditions at RT, 200 °C, and 400 °C, adhesive wear, mild oxidation wear, and oxidation wear prevailed, respectively. The wear rate at 200 °C was substantially lower than those at RT and 400 °C due to the protection of tribo-oxides. In mild oxidation wear, the tempered microstructures of the steel presented almost no obvious influence on the wear resistance. However, in adhesive wear and oxidation wear, the wear resistance strongly depended on the tempered microstructures of the steel. The steel tempered at 600-650 °C presented pronouncedly lower wear rates than the one tempered at 200-550 or 700 °C. It can be suggested that the wear resistance of the steel was closely related with its fracture resistance.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical stress and fatigue analysis · Metal Alloys Wear and Properties · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. G.A. Fontalvo and C. Mitterer, The Effect of Oxide-Forming Alloying Elements on the High Temperature Wear of a Hot Work Steel, Wear, 2005, 258(10), p 1491–149910.1016/j.wear.2004.04.014 ↗
2. O. Barrau, C. Boher, R. Gras, and F. Rezai-Aria, Analysis of the Friction and Wear Behaviour of Hot Work Tool Steel for Forging, Wear, 2003, 255(7–12), p 1444–145410.1016/S0043-1648(03)00280-1 ↗
3. R. Tyagi, S.K. Nath, and S. Ray, Modelling of Dry Sliding Oxidation-Modified Wear in Two Phase Materials, Wear, 2003, 255(1–6), p 327–33210.1016/S0043-1648(03)00209-6 ↗
4. M. Aksoy, M.B. Karamiş, and E. Evin, An Evaluation of the Wear Behaviour of a Dual-Phase Low-Carbon Steel, Wear, 1996, 193(2), p 248–25210.1016/0043-1648(95)06796-5 ↗
5. H.J. Kim and Y.G. Kweon, The Effects of Retained Austenite on Dry Sliding Wear Behavior of Carburized Steels, Wear, 1996, 193(1), p 8–1510.1016/0043-1648(95)06634-9 ↗
6. Y. Wang, T.C. Lei, and J.J. Liu, Tribo-Metallographic Behavior of High Carbon Steels in Dry Sliding: II. Microstructure and Wear, Wear, 1999, 231(1), p 12–1910.1016/S0043-1648(99)00116-7 ↗
7. E. Marui, N. Hasegawa, H. Endo, K. Tanaka, and T. Hattori, Research on the Wear Characteristics of Hypereutectoid Steel, Wear, 1997, 205(1–2), p 186–19910.1016/S0043-1648(96)07316-4 ↗
8. S.Q. Wang, F. Wang, X.H. Cui, and K.M. Chen, Effect of Secondary Carbides on Oxidation Wear of the Cr–Mo–V Cast Steels, Mater. Lett., 2008, 62(2), p 279–28110.1016/j.matlet.2007.05.018 ↗
9. M. Vardavoulias, The Role of Hard Second Phases in the Mild Oxidational Wear Mechanism of High-Speed Steel-Based Materials, Wear, 1994, 173(1–2), p 105–11410.1016/0043-1648(94)90262-3 ↗
10. C. Rodenburg and W.M. Rainforth, A Quantitative Analysis of the Influence of Carbides Size Distributions on Wear Behaviour of High-Speed Steel in Dry Rolling/Sliding Contact, Acta Mater., 2007, 55(7), p 2443–245410.1016/j.actamat.2006.11.039 ↗
11. X.Z. Feng and S.W. Li, Die Steels and Heat Treatment, Mechanical Industry Press, Beijing, 1984, p 234 (in Chinese)
12. X.B. Hu, L. Lin, X.C. Wu, and M. Zhang, Coarsening Behavior of M23C6 Carbides After Ageing or Thermal Fatigue in AISI, H13 Steel with Niobium, Int. J. Fatigue, 2006, 28(3), p 175–18210.1016/j.ijfatigue.2005.06.042 ↗
13. J. Jiang, F.H. Stott, and M.M. Stack, A Generic Model for Dry Sliding Wear of Metals at Elevated Temperatures, Wear, 2004, 256(9–10), p 973–98510.1016/j.wear.2003.09.005 ↗
14. T.F.J. Quinn, J.L. Sullivan, and D.M. Rowson, Developments in the Oxidational Theory of Mild Wear, Tribol. Int., 1980, 13(4), p 153–15810.1016/0301-679X(80)90031-6 ↗
15. T.F.J. Quinn, Oxidational Wear Modelling Part III. The Effects of Speed and Elevated Temperatures, Wear, 1998, 216(2), p 262–27510.1016/S0043-1648(98)00137-9 ↗
16. J.E. Wilson, F.H. Stott, and G.C. Wood, The Development of Wear Protective Oxides and their Influence on Sliding Friction, Proc. R. Soc., 1980, 369A, p 557–57410.1098/rspa.1980.0016 ↗
17. H. So, D.S. Yu, and C.Y. Chuang, Formation and Wear Mechanism of Tribo-Oxides and the Regime of Oxidational Wear of Steel, Wear, 2002, 253(9–10), p 1004–101510.1016/S0043-1648(02)00230-2 ↗
18. S.Q. Wang, M.X. Wei, F. Wang, X.H. Cui, and C. Dong, Transition of Mild Wear to Severe Wear in Oxidative Wear of H21 Steel, Tribol. Lett., 2008, 32(2), p 67–7210.1007/s11249-008-9361-y ↗
19. X.H. Cui, S.Q. Wang, F. Wang, and K.M. Chen, Research on Oxidative Wear Mechanism of the Cast Steels, Wear, 2008, 265(3–4), p 468–47610.1016/j.wear.2007.11.015 ↗