Effect of Cooling Rate on Microstructure and Mechanical Properties of Thin-Walled Ductile Iron Castings
Source abstract
Abstract
This article addresses the effect of cooling rate on microstructure and mechanical properties as determined by changing molding media and section size. The research was conducted for thin-walled iron castings with 2-5-mm wall thickness and for the reference casting with 13-mm wall thickness, using different molding materials (silica sand and insulating sand “LDASC”) to achieve various cooling rates. Thermal analysis was performed to determine the real cooling rate at the beginning of the graphite eutectic solidification. In general, it was found that the predictions based on theoretical analysis of the solidification process of ductile iron are in good agreement with the experimental outcomes. Finally, the present study provides insights into the effect of cooling rate on the graphite nodule count, the ferrite fraction and mechanical properties of thin-walled ductile iron castings. The study shows that the cooling rate of thin-walled castings varies in a wide range (80-15 °C/s) when changing the wall thickness from 2 to 5 mm, accompanied by significantly changing the mechanical properties of ductile iron. The cooling rate can be effectively reduced by applying an insulating sand to obtain the desired properties of thin-walled castings practically in the whole range of ductile iron grades in accordance with the ASTM Standard.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Aluminum Alloy Microstructure Properties · Iron and Steelmaking Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (14)
Show source-provided references
1. S.J. Karsay, Ductile Iron Production Practices, American Foundrymen’s Society, Des Plaines, 1994, p 78–88
2. F.R. Salazar, M. Herrera-Trejo, M. Castro, J.N. Méndez, J.T. Torres, and M. Méndez, Effect of Nodule Count and Cooling Rate on As-Cast Matrix of a Cu-Mo Spheroidal Graphite, J. Mater. Eng. Perform., 1999, 8, p 325–32910.1361/105994999770346873 ↗
3. P.J. Ratto, A.F. Ansaldi, V.E. Fierro et al., Low Temperature Impact Tests in Austempered Ductile Iron and Other Spheroidal Graphite Cast Iron Structures, ISIJ Int., 2001, 41, p 372–38010.2355/isijinternational.41.372 ↗
4. E. Fras and H.F. Lopez, A Theoretical and Experimental Study of the Dependence Between Undercooling and Nodular Eutectic Grains Density, Arch. Metall., 1998, 43, p 227–240
5. T. Skaland and O. Grong, Nodule Distribution in Ductile Cast Iron, AFS Trans., 1991, 99, p 153–157
6. D. Venugopalan, Prediction of Matrix Microstructure in Ductile Iron, AFS Trans., 1990, 98, p 465–469
7. E.N. Pan, W.S. Hsu, and C.R. Loper, Jr., Effects of Some Variables on the Matrix and Mechanical Properties of Ferritic Ductile Irons, AFS Trans., 1988, 96, p 645–660
8. S.K. Yu and C.R. Loper, Jr., The Effect of Molybdenum, Copper, and Nickel on the Pearlitic and Martensitic Hardenability of Ductile Cast Iron, AFS Trans., 1988, 96, p 8115–8118
9. J. Lacaze, C. Wilson, and C. Bak, Experimental Study of the Eutectoid Transformation in Spheroidal Graphite Cast Iron, Scand. J. Metall., 1994, 23, p 151–163
10. M. Górny, Structure Formation of Ultra-Thin Wall Ductile Iron Castings. Akapit Ed., Cracow, 2010, p 89–93 (in Polish)
11. E. Fraś, M. Górny, and H.F. Lopez, Thin Wall Ductile and Austempered Iron Castings as Substitutes for Aluminum Alloy Castings, Int. Foundry Res., 2009, 61, p 2–10
12. R.E. Showman, R.C. Aufderheide, and N. Yeomans, Ironing Out Thin-Wall Casting Defects, Mod. Cast., 2006, 96, p 29–32
13. B. Lux and W. Kurz, Solidification of Metals, vol. 110, The Iron and Steel Institute, London, 1967, p 193
14. E. Fraś, M. Górny, and H.F. Lopez, Eutectic Transformation in Ductile Cast Iron. Part I—Theoretical Background, Metall. Foundry Eng., 2005, 31, p 113–136