Comparison of GRCop-84 to Other Cu Alloys with High Thermal Conductivities
Source abstract
Abstract
The mechanical properties of six highly conductive copper alloys, GRCop-84, AMZIRC, GlidCop Al-15, Cu-1Cr-0.1Zr, Cu-0.9Cr, and NARloy-Z were compared. Tests were done on as-received hard drawn material, and after a heat treatment designed to simulate a brazing operation at 935 °C. In the as-received condition AMZIRC, GlidCop Al-15, Cu-1Cr-0.1Zr, and Cu-0.9Cr had excellent strengths at temperatures below 500 °C. However, the brazing heat treatment substantially decreased the mechanical properties of AMZIRC, Cu-1Cr-0.1Zr, Cu-0.9Cr, and NARloy-Z. The properties of GlidCop Al-15 and GRCop-84 were not significantly affected by the heat treatment. Thus there appear to be advantages to GRCop-84 over AMZIRC, Cu-1Cr-0.1Zr, Cu-0.9Cr, and NARloy-Z if use or processing temperatures greater than 500 °C are expected. Ductility was the lowest in GlidCop Al-15 and Cu-0.9Cr; reduction in area was particularly low in GlidCop Al-15 above 500 °C, and as-received Cu-0.9Cr was brittle between 500 and 650 °C. Tensile creep tests were done at 500 and 650 °C; the creep properties of GRCop-84 were superior to those of brazed AMZIRC, Cu-1Cr-0.1Zr, Cu-0.9Cr, and NARloy-Z. In the brazed condition, GRCop-84 was superior to the other alloys due to its greater strength and creep resistance (compared to AMZIRC, Cu-1Cr-0.1Zr, Cu-0.9Cr, and NARloy-Z) and ductility (compared to GlidCop Al-15).
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Aluminum Alloy Microstructure Properties · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. D.T. Butler Jr. and M.J. Pindera, Analysis of Factors Affecting the Performance of RLV Thrust Cell Liners, NASA/CR—2004-213141, Aug 2004
2. J.J. Stephens and D.T. Schmale, “The Effect of High Temperature Braze Thermal Cycles on Mechanical Properties of a Dispersion Strengthened Copper Alloy,” SAND87-1296 UC-20, 1987, 1988, Second printing
3. M.V. Nathal, D.L. Ellis, W.S. Loewenthal, S.V. Raj, L.U. Thomas-Ogbuji, J. Ghosn, L.A. Greenbauer-Seng, J. Gayda, and C.A. Barrett, High Conductivity Materials for High Heat Flux Applications in Space Propulsion Systems, JANNAF 39th CS/27th APS/21st PSHS/3rd MSS Subcommittee Joint Meeting, Colorado Springs, CO, CD-ROM, Dec 2003, p 2003–0390cc
4. J.B. Conway, R.H. Stentz, and J.T. Berling, High Temperature, Low Cycle Fatigue of Copper-Base Alloys in Argon; Part I—Preliminary Results for 12 Alloys at 1000 °F (538 °C), NASA CR-121259, 1973
5. P.A. Wycliffe, “Literature Search on High Conductivity Copper Based Alloys,” Final Report IDWA No. 6458-2, Rockwell International Sci. Center, R5739TC/sn, 1984
6. D.D. Horn and H.F. Lewis, “Property Investigation of Copper Base Alloys at Ambient and Elevated Temperatures,” AEDC-TR-65-72, 1965, (Defense Document Center No. 467015), p 4, 11, 12, 35, 38
7. J.B. Conway, R.H. Stentz, and J.T. Berling, High-Temperature, Low-Cycle Fatigue of Copper-Base Alloys for Rocket Nozzles, Part II—Strainrange Partitioning and Low-Cycle Fatigue Results at 538 °C, NASA CR-135073, 1976
8. N.P. Hannum, H.J. Kasper, and A.J. Pavli, “Experimental and Theoretical Investigation of Fatigue Life in Reusable Rocket Thrust Chambers,” AIAA/SAE 12th Propulsion Conf., AIAA Paper No. 76-685, 197610.2514/6.1976-685 ↗
9. J.J. Esposito and R.F. Zabora, Thrust Chamber Life Prediction—Vol. I—Mechanical and Physical Properties of High Performance Rocket Nozzle Materials, NASA CR-134806, 1975
10. E.N.C. Dalder, W. Ludemann, and B. Schumacher, Thermal Stability of Four High-Strength, High-Conductivity Copper Sheet Alloys, UCRL-88919, and ASM’s Copper and Copper Alloys Conf., 1983, material also appears in UCRL-89034-Rev. 1, Conf-830466-Rev-1, DE83 013312 Accession No. 84N10288, DOE Workshop on Copper Alloys, 1983
11. J.J. Stephens, R.J. Bourcier, F.J. Vigil, and D.T. Schmale, “Mechanical Properties of Dispersion Strengthened Copper: A Comparison of Braze Cycle Annealed and Coarse Grain Microstructure,” Sandia Report SAND88-1351, 198810.2172/6775883 ↗
12. Metals Handbook, 9th ed., Vol. 2, Properties and Selection: Nonferrous Alloys and Pure Metals, ASM Handbook Committee, American Soc. for Metals, Metals Park, OH, 1979, p 309
13. J.B. Correia, H.A. Davies, and C.M. Sellars, “Strengthening in Rapidly Solidified Age Hardened Cu-Cr and Cu-Cr-Zr Alloys,” Acta Mater., 45, (1), 1997, p 177–19010.1016/S1359-6454(96)00142-5 ↗
14. T. Nguyentat, V.A. Gibson, and R.M. Horn, “NASA-Z A Liner Material for Rocket Combustion Chambers,” 27th Joint Prop. Conf., AIAA Paper No. 91-2487
15. D.L. Ellis, GRCop-84: A High-Temperature Copper Alloy for High-Heat-Flux Application, NASA/TM—2005-213566
16. K.J. Zeng, M. Hamalainen, and K. Lilius, “Phase Relationships in Cu-rich Corner of the Cu-Cr-Zr Phase Diagram,” Scripta Metallurgica et Materialia, 32, (12), 1995, p 2009–201410.1016/0956-716X(95)00084-9 ↗
17. Pratt and Whitney Aircraft Group: Thrust Chamber Material Technology Program, NASA CR-187207, 1989
18. S.J. Zinkle, Tensile Properties of High-Strength, High-Conductivity Copper Alloys at High Temperatures, Fusion Materials Semiann. Prog. Report for period ending June 30, 2000, DOE/ER-0313/28, Oak Ridge National Lab, Oak Ridge, TN, 2000, p 171–175
19. J.M. Kazaroff and G.A. Repas, Conventionally Cast and Forged Copper Alloy for High Heat Flux Thrust Chambers, NASA Technical Paper 2694, NASA Glenn Research Center, Cleveland OH, 1987
20. H.C. de Groh III, D.L. Ellis, and W.S. Loewenthal, Comparison of GRCop-84 to Other High Thermal Conductive Cu Alloys, NASA/TM—2007-214663, NASA Glenn Research Center, Cleveland, OH, 2007
21. D.L. Ellis and R.L. Dreshfield, Preliminary Evaluation of a Powder Metal Copper-8 Cr-4 Nb Alloy, Advanced Earth-to-Orbit Propulsion Technology 1992, NASA CP-3174, 1, NASA Marshall Space Flight Center, Huntsville, AL, May 1992, p 18–27
22. D.L. Ellis, R.L. Dreshfield, M.J. Verrilli, and D.G. Ulmer, Mechanical Properties of a Cu-8 Cr-4 Nb Alloy, Advanced Earth-to-Orbit Propulsion Technology 1994, NASA CP-3282, NASA Marshall Space Flight Center, Huntsville, AL, May 1994, p 32–41
23. D.L. Ellis and G.M. Michal, Mechanical and Thermal Properties of Two Cr-Cr-Nb Alloys and NARloy-Z, NASA CR-198529, NASA Glenn Research Center, Cleveland OH, Oct 1996
24. D.L. Ellis, W.S. Loewenthal, and H. Haller, Creep of Commercially Produced GRCop-84, NASA TM to be published, NASA Glenn Research Center, Cleveland, OH, 2007
25. A. Goldsmith, T.E. Waterman, and H.J. Hirschhorn, Handbook of Thermophysical Properties of Solid Materials, 1, Pergamon, New York, NY, 1961
26. D.L. Ellis and G.M. Michal, “Formation of Cr and Cr2Nb Precipitates in Rapidly Solidified Cu-Cr-Nb Ribbon,” Ultramicroscopy, 30, (1-2), June 1989, p 210-21610.1016/0304-3991(89)90189-7 ↗
27. J.D. Verhoeven, Fundamentals of Physical Metallurgy, Wiley & Sons pub., 1975, p 330, 459, 515–517
28. ASM Handbook, Vol. 8, Mechanical Testing and Evaluation, H. Kuhn and D. Medlin, Eds., ASM International, 2000, p 363–368
29. D.L. Ellis and D.J. Keller, Thermophysical Properties of GRCop-84, NASA/CR—2000-210055, NASA Glenn Research Center, Cleveland, OH, June 2000