Junction-free copper wires with submicron linewidth for large-area high-performance transparent electrodes
Source abstract
Abstract
Electrospinning and wet etching facilitate large-area fabrication of junction-free copper wires with the smallest linewidth of 550 nm.
Only a short abstract or summary was supplied by the source.
Source: crossref · Quality: short
Research context
OpenAlex topics: Nanomaterials and Printing Technologies · Advanced Sensor and Energy Harvesting Materials · Advanced Materials and Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Material Science and Engineering, Nanchang Hangkong University
696 Fenghe South Avenue
Nanchang 330063
China
Jiangxi Engineering Laboratory for Optoelectronics Testing Technology
Nanchang Hangkong University
Nanchang
Funding
Natural Science Foundation of Jiangxi Province · National Natural Science Foundation of China · Nanchang Hangkong University
References (45)
Show source-provided references
1. Kang · Adv. Mater. · 2010 · 22 · 437810.1002/adma.201001395 ↗
2. Wu · ACS Nano · 2010 · 4 · 4310.1021/nn900728d ↗
3. Gaetano · Adv. Funct. Mater. · 2018 · 28 · 170601010.1002/adfm.201706010 ↗
4. Wu · Nat. Nanotechnol. · 2013 · 8 · 42110.1038/nnano.2013.84 ↗
5. Cai · Acc. Chem. Res. · 2016 · 49 · 146910.1021/acs.accounts.6b00183 ↗
6. Hecht · Adv. Mater. · 2011 · 23 · 148210.1002/adma.201003188 ↗
7. Kim · Adv. Funct. Mater. · 2011 · 21 · 107610.1002/adfm.201002290 ↗
8. Lipomi · Nat. Nanotechnol. · 2011 · 6 · 78810.1038/nnano.2011.184 ↗
9. Bae · Nat. Nanotechnol. · 2010 · 5 · 57410.1038/nnano.2010.132 ↗
10. Zhao · ACS Appl. Mater. Interfaces · 2018 · 10 · 2751010.1021/acsami.8b08578 ↗
11. Lee · Nano Lett. · 2008 · 8 · 68910.1021/nl073296g ↗
12. Hsu · J. Am. Chem. Soc. · 2014 · 136 · 1059310.1021/ja505741e ↗
13. He · ACS Nano · 2014 · 8 · 478210.1021/nn500678b ↗
14. Wang · Chem. Soc. Rev. · 2018 · 47 · 461110.1039/C7CS00192D ↗
15. Ye · Adv. Mater. · 2014 · 26 · 667010.1002/adma.201402710 ↗
16. Catrysse · Nano Lett. · 2010 · 10 · 294410.1021/nl1011239 ↗
17. Wu · Nano Lett. · 2010 · 10 · 424210.1021/nl102725k ↗
18. Hu · ACS Nano · 2010 · 4 · 295510.1021/nn1005232 ↗
19. Tseng · Small · 2018 · 14 · 180054110.1002/smll.201800541 ↗
20. Garnett · Nat. Mater. · 2012 · 11 · 24110.1038/nmat3238 ↗
21. Zhang · Nanoscale · 2018 · 10 · 1298110.1039/C8NR01648H ↗
22. Song · ACS Nano · 2014 · 8 · 280410.1021/nn4065567 ↗
23. Lee · ACS Appl. Mater. Interfaces · 2017 · 9 · 3965010.1021/acsami.7b08626 ↗
24. Singh · J. Mater. Chem. C · 2017 · 5 · 419810.1039/C7TC01002H ↗
25. Im · Nanoscale · 2016 · 8 · 391610.1039/C5NR07657A ↗
26. Moon · Nanoscale · 2018 · 10 · 792710.1039/C8NR00002F ↗
27. Choi · Small · 2017 · 14 · 170256710.1002/smll.201702567 ↗
28. Hsu · Nat. Commun. · 2013 · 4 · 252210.1038/ncomms3522 ↗
29. Kim · Nano Lett. · 2018 · 18 · 386510.1021/acs.nanolett.8b01157 ↗
30. van de Groep · Nano Lett. · 2012 · 12 · 313810.1021/nl301045a ↗
31. Greiner · Angew. Chem., Int. Ed. · 2007 · 46 · 567010.1002/anie.200604646 ↗
32. Yang · ACS Appl. Mater. Interfaces · 2017 · 9 · 2646810.1021/acsami.7b08606 ↗
33. Wang · Org. Electron. · 2018 · 61 · 29610.1016/j.orgel.2018.06.007 ↗
34. Hong · ACS Appl. Mater. Interfaces · 2015 · 7 · 2739710.1021/acsami.5b09060 ↗
35. Bao · ACS Nano · 2015 · 9 · 250210.1021/nn504932e ↗
36. Wang · Small · 2017 · 13 · 160429110.1002/smll.201604291 ↗
37. Williams · J. Microelectromech. Syst. · 2003 · 12 · 76110.1109/JMEMS.2003.820936 ↗
38. Zhang · Opt. Mater. Express · 2018 · 8 · 90910.1364/OME.8.000909 ↗
39. Li · Nano Lett. · 2009 · 9 · 435910.1021/nl902623y ↗
40. Zhu · ACS Nano · 2011 · 5 · 647210.1021/nn201696g ↗
41. Deitzel · Polymer · 2001 · 42 · 26110.1016/S0032-3861(00)00250-0 ↗
42. De · ACS Nano · 2010 · 4 · 706410.1021/nn1025803 ↗
43. De · MRS Bull. · 2011 · 36 · 77410.1557/mrs.2011.236 ↗
44. Scardaci · Small · 2011 · 7 · 262110.1002/smll.201100647 ↗
45. Zhang · Opt. Express · 2017 · 25 · 1768310.1364/OE.25.017683 ↗