Physical properties and anisotropic magnetism of EuBi2

We report the synthesis of EuBi 2 single crystals and their magnetic and electronic properties. Plate-like crystals were grown in excess bismuth, and X-ray diffraction data confirm the previously reported tetragonal space group, I 4 1 /amd (No. 141). A Néel temperature of T N = 18.6 K was determined from the specific heat data, and corresponding anomalies occur in the magnetization and resistivity. We only observe one magnetic transition in zero magnetic field. The magnetization data above 70 K are well described by a Curie-Weiss model with a Weiss temperature of Θ CW ≈ −35 K and an effective moment near that of the expected spin-only moment of Eu 2+ (S = 7/2). Isothermal magnetization measurements reveal field-induced transitions for H||[100], including a hysteretic spin-flop centered at 10.1 T and a change in slope at 12 T and 2 K. However, while the isothermal magnetization for H||[110] displays nonlinear behavior, discrete metamagnetic transitions are not observed for H||[110] or H||[001], indicating significant magnetic anisotropy. The magnetization does not saturate by 13.5 T for any orientation. EuBi 2 is metallic and our crystals possess an in-plane residual resistivity ratio of ⍴ 300 K /⍴ 2 K ≈ 40. Single crystal neutron diffraction data reveal a large magnetic unit cell and non-trivial antiferromagnetic ordering. These results demonstrate that strong antiferromagnetic coupling drives complex magnetism in EuBi 2 .